PP均聚，PROTEQ™ H16ST8对比PP均聚，PROTEQ™ H24ST8物性表,价格行情_搜料

牌号信息	PROTEQ™ H16ST8 物性表 PP均聚 & 澳大利亚凯诺斯指导价格：暂无塑料库存：缺货	PROTEQ™ H24ST8 物性表 PP均聚 & 澳大利亚凯诺斯指导价格：暂无塑料库存：缺货
牌号简介	PROTEQ™ H16ST8是一种中等熔融流动汽车聚丙烯均聚物，含有40%滑石填料，具有改善的热老化性能。ProteqH16ST8的设计符合汽车耐久性规范的严格要求，结合了易加工性、高刚性和耐热性。典型应用是加热器外壳、继电器盖和座椅部件。 PROTEQ™ H16ST8 is a medium melt flow automotive polypropylene homopolymer containing 40% talc filler which features improved heat ageing performance. PROTEQ™H16ST8 has been designed to meet the stringent requirements of automotive durability specifications, combining easy processing with a high rigidity and heat resistance. Typical applications are heater cases, relay covers and seating components.	PROTEQ™ H24ST8是一种高流量40%滑石填充热稳定级聚丙烯均聚物。它已经稳定下来以满足汽车热老化的要求。 PROTEQ™ H24ST8 is a high flow 40% Talc filled heat stabilised grade of polypropylene homopolymer. It has been stabilised to meet automotive heat aging requirements

产品描述
厂家：	澳大利亚凯诺斯 Qenos	澳大利亚凯诺斯 Qenos
类别：	PP均聚 PP homopolymerization	PP均聚 PP homopolymerization
填料：	滑石粉 40	滑石粉 40
用途：	汽车领域的应用	汽车领域的应用
性能特点：	机械强度好,易加工,耐老化,耐高温,流动性中等,热稳定性好,均聚物,防火阻燃等级HB Good Rigidity,Excellent Processability,Good heat aging resistance,High Heat Resistance,Moderate liquidity,Heat Stabilized,Homopolymer,HB	耐老化,流动性高,热稳定性好,均聚物,防火阻燃等级HB Good heat aging resistance,High liquidity,Heat Stabilized,Homopolymer,HB
加工条件：

技术参数

物理性能
PHYSICAL PROTEQ™ H16ST8 PROTEQ™ H24ST8 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

收缩率(MD：3.0 mm)
Shrinkage rate % ASTM D955

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

冲击性能
IMPACT PROTEQ™ H16ST8 PROTEQ™ H24ST8 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(3.2 mm)
Notched impact strength of cantilever beam J/m ASTM D256

悬臂梁缺口冲击强度(3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

热性能
THERMAL PROTEQ™ H16ST8 PROTEQ™ H24ST8 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ASTM D696

阻燃性能
FLAMMABILITY PROTEQ™ H16ST8 PROTEQ™ H24ST8 单位
UNIT 测试方法
TEST METHOD

1.60 mm
1.60 mm UL 94

灼热丝起燃温度(1.6 mm)
Igniting temperature of the hot wire ℃ AS/NZS 60695

机械性能
MECHANICAL PROTEQ™ H16ST8 PROTEQ™ H24ST8 单位
UNIT 测试方法
TEST METHOD

弯曲强度(3.20 mm)
bending strength MPa ASTM D790

弯曲模量(3.20 mm)
Bending modulus MPa ASTM D790

拉伸应变(断裂，3.20 mm)
Tensile strain % ASTM D638

拉伸强度(3.20 mm)
tensile strength MPa ASTM D638

邵氏硬度(邵氏 D)
Shore hardness ISO 868

邵氏硬度(邵氏 D，15 秒)
Shore hardness ISO 868

加工方式

注射 PROTEQ™ H16ST8 PROTEQ™ H24ST8 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

注射速度 PROTEQ™ H16ST8 PROTEQ™ H24ST8 单位测试方法

背压 MPa

螺杆转速 rpm

锁模力 kN/cm²

备注

1 一般属性：这些不能被视为规格。

2 0.20 in/min

3 0.051 in/min

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 0.39 in/min