PP均聚，Polifil® BS BS-7010对比PP均聚，Petrotene® PP A3 E8 CNZ0018 PH346 MSP物性表,价格行情_搜料

牌号信息	Polifil® BS BS-7010 物性表 PP均聚 & 美国TPG 指导价格：暂无塑料库存：缺货	Petrotene® PP A3 E8 CNZ0018 PH346 MSP 物性表 PP均聚 & 巴西Petropol 指导价格：暂无塑料库存：缺货
牌号简介	Polifil® BS系列化合物是用硫酸钡增强的均聚聚丙烯树脂。它们具有增加的比重、高弯曲模量、高偏转温度、良好的耐化学性、摩擦性和X射线不透明度。这些化合物可用于化妆品、塑模、隔音部件和医疗器械。适用标准加工技术。使用此信息作为指南，帮助您选择适合您应用的树脂。TPG将为您的应用定制化合物并微调我们的配方。 Polifil ® BS series compounds are homopolymer polypropylene resins reinforced with barium sulfate. They possess increased specific gravity, high flex modulus, high deflection temperature, good chemical resistance, frictional resistance, and x-ray opacity. These compounds are utilized in cosmetic application, molded weights, soundproofing components, and medical devices. Standard processing techniques are applicable. Use this information as a guide to aid you in selecting the proper resin for your application. TPG will custom compound and fine-tune our formulations for your application.	灰色增强聚丙烯均聚物用8%的弹性体共混材料注塑成型，具有良好的力学性能和尺寸稳定性。 Polypropylene homopolymer in gray color reinforced with 8% of elastomer blend material to injection molding, good set of mechanical properties and dimensional stability.

产品描述
厂家：	美国TPG	巴西Petropol
类别：	PP均聚 PP homopolymerization	PP均聚 PP homopolymerization
填料：
用途：	医疗器械,砝码和天平,化妆品
性能特点：	高灵活性,高密度,耐化学性,均聚物 High Flexibility,High density,Solvent resistance,Homopolymer	尺寸稳定性好,均聚物,防火阻燃等级HB Good Dimensional Stability,Homopolymer,HB
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Polifil® BS BS-7010 Petrotene® PP A3 E8 CNZ0018 PH346 MSP 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡)
Water absorption rate % ASTM D570

密度
Density g/cm³ ASTM D792

收缩率(MD)
Shrinkage rate % ASTM D955

收缩率(MD：2.49 mm)
Shrinkage rate % ASTM D955

灰份含量
Ash Content % ASTM D2584

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL Polifil® BS BS-7010 Petrotene® PP A3 E8 CNZ0018 PH346 MSP 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ASTM D790

弯曲强度(屈服，23℃)
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量(1% 正割，23℃)
Bending modulus MPa

弯曲模量(正切，23℃)
Bending modulus MPa

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂，23℃)
Tensile strain % ASTM D638

拉伸强度
tensile strength MPa ASTM D638

拉伸强度(23℃)
tensile strength MPa ASTM D638

冲击性能
IMPACT Polifil® BS BS-7010 Petrotene® PP A3 E8 CNZ0018 PH346 MSP 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

热性能
THERMAL Polifil® BS BS-7010 Petrotene® PP A3 E8 CNZ0018 PH346 MSP 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525 4

电气性能
ELECTRICAL Polifil® BS BS-7010 Petrotene® PP A3 E8 CNZ0018 PH346 MSP 单位
UNIT 测试方法
TEST METHOD

介电强度
Dielectric strength kV/mm ASTM D149

体积电阻率
Volume resistivity ohms·cm ASTM D257

耗散因数(1 kHz)
Dissipation factor ASTM D150

阻燃性能
FLAMMABILITY Polifil® BS BS-7010 Petrotene® PP A3 E8 CNZ0018 PH346 MSP 单位
UNIT 测试方法
TEST METHOD

阻燃等级
Flame retardant level UL 94

加工方式

注射 Polifil® BS BS-7010 Petrotene® PP A3 E8 CNZ0018 PH346 MSP 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注射速度

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 2°C/min

4 标准 B (120°C/h), 压力1 (10N)


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
加工方式
注射
备注