热固性复合材料，Gordon Composites™ GC-67-UB对比热固性复合材料，Gordon Composites™ GC-70-ULS物性表,价格行情_搜料

牌号信息	Gordon Composites™ GC-67-UB 物性表热固性复合材料 & 美国普立万指导价格：暂无塑料库存：缺货	Gordon Composites™ GC-70-ULS 物性表热固性复合材料 & 美国普立万指导价格：暂无塑料库存：缺货
牌号简介	一种连续单向E玻璃纤维/环氧树脂棒材料，在所有厚度范围内提供高强度和刚度。GC-67-UB采用专有的脉冲成形工艺制造，在浸渍和固化过程中，所有玻璃纤维都经过预拉伸和对齐。 A continuous unidirectional "E" fiberglass/epoxy bar material that provides high strength and stiffness at all thickness ranges. GC-67-UB is manufactured with a proprietary pulforming process in which all glass fibers are pretensioned and aligned during the impregnation and curing process.	连续单向E玻璃纤维与50/50编织玻璃纤维嵌体结合，沿纵向（0）轴具有高强度和刚度，并提供横向强度（与纵向轴成90度）。GC-70-ULS采用专有的脉冲成形工艺制造，在浸渍和固化过程中，所有玻璃纤维均进行预拉伸和对齐。 A continuous unidirectional "E" fiberglass combined with a 50/50 woven fiberglass inlay that has high strength and stiffness along the longitudinal (0) axis and provides cross strength (90 degrees to the longitudinal axis). GC-70-ULS is manufactured with a proprietary pulforming process in which all glass fibers are pretensioned and aligned during the impregnation and curing process.

产品描述
厂家：	美国普立万 Polyone	美国普立万 Polyone
类别：	热固性复合材料热固性复合材料	热固性复合材料热固性复合材料
填料：	玻璃纤维	玻璃纤维
用途：	汽车领域的应用,弹簧,船舶应用,体育用品,金属取代,构件,工业应用	船舶应用,金属取代,工业应用,弹簧,体育用品,构件
性能特点：
加工条件：	机器加工	机器加工

技术参数

物理性能
PHYSICAL Gordon Composites™ GC-67-UB Gordon Composites™ GC-70-ULS 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D1505

机械性能
MECHANICAL Gordon Composites™ GC-67-UB Gordon Composites™ GC-70-ULS 单位
UNIT 测试方法
TEST METHOD

剪切强度(--)
shear strength MPa ASTM D5379

剪切强度(--)
shear strength MPa ASTM D5397

剪切模量(--)
shear modulus MPa

压缩强度
compressive strength MPa ASTM D3410

压缩强度(--)
compressive strength MPa

压缩模量
Compression modulus MPa ASTM D3410

压缩模量(--)
Compression modulus MPa

弯曲强度
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

拉伸应变(断裂)
Tensile strain % ASTM D3039

拉伸强度
tensile strength MPa ASTM D3039

拉伸强度(--)
tensile strength MPa

拉伸模量
Tensile modulus MPa ASTM D3039

拉伸模量(--)
Tensile modulus MPa

泊松比
Poisson's ratio ASTM D3410

热性能
THERMAL Gordon Composites™ GC-67-UB Gordon Composites™ GC-70-ULS 单位
UNIT 测试方法
TEST METHOD

玻璃化转变温度
Glass transition temperature ℃ ASTM D3418

备注

2. Width: .400 to 8.75 Thickness: .130 to .550 Length: 6 to 264

3. 0 degree orientation

4. 90 degree orientation

5. Strength Values developed from ASTM D790 are dependent on thickness. As thickness increased flex strength decreased. The test data above is based on a test thickness of .060

6. Inter-laminar, 2,3 direction

7. In-plane, 1,2 direction

8. nu12 (0/90), valid both tensile and compression

2. Width: .1.50 to 18.00 Thickness: .040 to .080 Length: 6 to 120

3. 0 degree orientation

4. Strength Values developed from ASTM D790 are dependent on thickness. As thickness increased flex strength decreased. The test data above is based on a test thickness of .060