技术参数
冲击性能
IMPACT
VALOX™ FR Resin 855
VALOX™ 420SE0M resin
单位
UNIT
测试方法
TEST METHOD
仪表控制抗冲击总能量 23℃
Instrument control anti impact total energy 23 ℃
cm-kgf
ASTM D 3763
悬臂梁冲击强度，80*10*4(无缺口-30℃)
Impact strength of cantilever beam, 80 * 10 * 4
kJ/m²
ISO 180/1U
悬臂梁冲击强度，80*10*4(无缺口23℃)
Impact strength of cantilever beam, 80 * 10 * 4
kJ/m²
ISO 180/1U
悬臂梁冲击强度，80*10*4(缺口-30℃)
Impact strength of cantilever beam, 80 * 10 * 4
kJ/m²
ISO 180/1A
悬臂梁冲击强度，80*10*4(缺口23℃)
Impact strength of cantilever beam, 80 * 10 * 4
kJ/m²
ISO 180/1A
悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam
J/m
ASTM D4812
悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam
kJ/m²
ISO 180/1U
悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam
J/m
ASTM D4812
悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam
kJ/m²
ISO 180/1U
悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch
J/m
ASTM D256
悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch
kJ/m²
ISO 180-1A
悬臂梁缺口冲击强度(0℃)
Impact strength of cantilever beam notch
J/m
ASTM D256
悬臂梁缺口冲击强度(0℃)
Impact strength of cantilever beam notch
kJ/m²
ISO 180-1A
悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch
J/m
ASTM D256
悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch
J/m
ASTM D4812
悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch
kJ/m²
ISO 180-1A
简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength
kJ/m²
ISO 179/1eU
简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength
kJ/m²
ISO 179/2U
简支梁无缺口冲击强度(-30℃，80*10*4)
Charpy Unnotch Impact strength
kJ/m²
ISO 179/1eU
简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength
kJ/m²
ISO 179/1eU
简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength
kJ/m²
ISO 179/2U
简支梁无缺口冲击强度(23℃，80*10*4)
Charpy Unnotch Impact strength
kJ/m²
ISO 179/1eU
简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength
kJ/m²
ISO 179/1eA
简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength
kJ/m²
ISO 179/2C
简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength
kJ/m²
ISO 179/1eA
简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength
kJ/m²
ISO 179/2C
简支梁缺口冲击强度(80*10*4)
Charpy Notched Impact Strength
装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments
J
ASTM D3763
热性能
THERMAL
VALOX™ FR Resin 855
VALOX™ 420SE0M resin
单位
UNIT
测试方法
TEST METHOD
导热系数
Thermal conductivity coefficient
W/m/K
ISO 8302
导热系数
Thermal conductivity coefficient
W/m/℃
ISO 8302
热变形温度(0.45 MPa)
Hot deformation temperature
℃
ASTM D 648
热变形温度(0.45 MPa，未退火，100 mm跨距)
Hot deformation temperature
℃
ISO 75-2/Be
热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature
℃
ASTM D648
热变形温度(0.45 MPa，未退火，4.0 mm，64 mm跨距)
Hot deformation temperature
℃
ISO 75-2/Bf
热变形温度(0.45 MPa，未退火，64 mm跨距)
Hot deformation temperature
℃
ISO 75/Be
热变形温度(1.8 MPa，未退火，100 mm跨距)
Hot deformation temperature
℃
ISO 75-2/Ae
热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature
℃
ASTM D648
热变形温度(1.8 MPa，未退火，4.0 mm，64 mm跨距)
Hot deformation temperature
℃
ISO 75-2/Af
热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature
℃
ISO 75/Ae
热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature
℃
ISO 75/Af
热变形温度(1.8MPa)
Hot deformation temperature
℃
ASTM D 648
热变形温度(未退火，3.2 mm)
Hot deformation temperature
球压测试(123~127℃)
Ball pressure test
IEC 60695-10-2
球压测试(125℃±2℃)
Ball pressure test
IEC 60695-10-2
相对温度指数(冲击机械性能)
Relative temperature index
℃
UL 746
相对温度指数(冲击机械性能)
Relative temperature index
℃
UL 746B
相对温度指数(电气性能)
Relative temperature index
℃
UL 746
相对温度指数(电气性能)
Relative temperature index
℃
UL 746B
相对温度指数(非机械冲击性能)
Relative temperature index
℃
UL 746B
线性热膨胀系数(MD：-20~150℃)
Linear coefficient of thermal expansion
1/℃
ASTM E831
线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion
1/℃
ASTM E831
线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion
1/℃
ISO 11359-2
线性热膨胀系数(MD：23~150℃)
Linear coefficient of thermal expansion
1/℃
ISO 11359-2
线性热膨胀系数(MD：23~80℃)
Linear coefficient of thermal expansion
1/℃
ISO 11359-2
线性热膨胀系数(TD：-20：150℃)
Linear coefficient of thermal expansion
1/℃
ASTM E831
线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion
1/℃
ASTM E831
线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion
1/℃
ISO 11359-2
线性热膨胀系数(TD：-40℃)
Linear coefficient of thermal expansion
1/℃
ISO 11359-2
线性热膨胀系数(TD：23~150℃)
Linear coefficient of thermal expansion
1/℃
ISO 11359-2
线性热膨胀系数(TD：23~80℃)
Linear coefficient of thermal expansion
1/℃
ISO 11359-2
维卡软化温度(--)
Vicat Softening Temp
℃
ASTM D1525 13
维卡软化温度(--)
Vicat Softening Temp
℃
ASTM D1525 14
维卡软化温度(A50)
Vicat Softening Temp
℃
ISO 306
维卡软化温度(B120)
Vicat Softening Temp
℃
ISO 306
维卡软化温度(B50)
Vicat Softening Temp
℃
ASTM D1525
维卡软化温度(B50)
Vicat Softening Temp
℃
ISO 306
电气性能
ELECTRICAL
VALOX™ FR Resin 855
VALOX™ 420SE0M resin
单位
UNIT
测试方法
TEST METHOD
介电常数(1 MHz)
Dielectric constant
ASTM D150
介电常数(100 Hz)
Dielectric constant
ASTM D150
介电常数(50 Hz)
Dielectric constant
IEC 60250
介电常数(60 Hz)
Dielectric constant
IEC 60250
介电强度(0.8 mm，在油中)
Dielectric strength
kV/mm
ASTM D149
介电强度(0.8 mm，在油中)
Dielectric strength
kV/mm
IEC 60243-1
介电强度(1 mm)
Dielectric strength
kV/mm
IEC 60243-1
介电强度(1.6 mm，在油中)
Dielectric strength
kV/mm
ASTM D149
介电强度(1.6 mm，在油中)
Dielectric strength
kV/mm
IEC 60243-1
介电强度(3.2 mm，在油中)
Dielectric strength
kV/mm
ASTM D149
介电强度(3.2 mm，在油中)
Dielectric strength
kV/mm
IEC 60243-1
介电强度(3.2 mm，在空气中)
Dielectric strength
kV/mm
ASTM D149
体积电阻率
Volume resistivity
ohms·cm
ASTM D257
热丝引燃{PLC}
Hot wire ignition {PLC}
PLC Code
UL 746A
热丝引燃(HWI)
Hot wire ignition
UL 746
电阻率(体积)
resistivity
Ohm-cm
IEC 60093
电阻率(表面)
resistivity
Ohm
IEC 60093
相对电容率(1 MHz)
Relative permittivity
ASTM D150
相对电容率(1 MHz)
Relative permittivity
IEC 60250
相对电容率(100 Hz)
Relative permittivity
ASTM D150
相对电容率(100 Hz)
Relative permittivity
IEC 60250
相对电容率(50-60 Hz)
Relative permittivity
IEC 60250
相比漏电起痕指数
Compared to the leakage tracing index
PLC Code
UL 746A
相比漏电起痕指数
Compared to the leakage tracing index
UL 746
相比漏电起痕指数(CTI)
Compared to the leakage tracing index
V
相比漏电起痕指数(CTI)
Compared to the leakage tracing index
V
IEC 60112
相比漏电起痕指数(解决方案 B)
Compared to the leakage tracing index
V
耐电弧性
Arc resistance
ASTM D495
耐电弧性(钨丝)
Arc resistance
PLC Code
ASTM D495
耗散因数(1 MHz)
Dissipation factor
ASTM D150
耗散因数(1 MHz)
Dissipation factor
IEC 60250
耗散因数(1 MHz)
Dissipation factor
ASTM D150
耗散因数(1 MHz)
Dissipation factor
IEC 60250
耗散因数(100 Hz)
Dissipation factor
ASTM D150
耗散因数(100 Hz)
Dissipation factor
IEC 60250
耗散因数(100 Hz)
Dissipation factor
ASTM D150
耗散因数(100 Hz)
Dissipation factor
IEC 60250
耗散因数(50 Hz)
Dissipation factor
IEC 60250
耗散因数(50-60 Hz)
Dissipation factor
IEC 60250
耗散因数(60 Hz)
Dissipation factor
IEC 60250
表面电阻率
Surface resistivity
ohms
IEC 60093
高电压弧起痕速率{PLC}
High voltage arc marking rate {PLC}
PLC Code
UL 746A
高电压电弧起痕速率(HVTR)
High voltage arc marking rate
UL 746
高电弧燃烧指数(HAI)
High Arc Burning Index (HAI)
UL 746
高电流电弧引燃(表面{PLC})
High current arc ignition (surface {PLC})
PLC Code
UL 746A
阻燃性能
FLAMMABILITY
VALOX™ FR Resin 855
VALOX™ 420SE0M resin
单位
UNIT
测试方法
TEST METHOD
极限氧指数
Extreme oxygen index
%
ISO 4589-2
极限氧指数(LOI)
Extreme oxygen index
%
ISO 4589
灼热丝可燃性指数(1.0 mm)
Glowing wire flammability index
℃
IEC 60695-2-12
灼热丝可燃性指数(960℃，通过)
Glowing wire flammability index
mm
IEC 60695-2-12
紫外线(水暴露/浸没)
ultraviolet radiation
-
UL 746C
阻燃等级(0.40 mm)
Flame retardant level
UL 94
阻燃等级(0.71 mm)
Flame retardant level
UL 94
阻燃等级(1.50 mm)
Flame retardant level
UL 94
阻燃等级(2.00 mm)
Flame retardant level
UL 94
补充信息
VALOX™ FR Resin 855
VALOX™ 420SE0M resin
单位
UNIT
测试方法
TEST METHOD
填充物
Filler
%
ASTM D229
机械性能
MECHANICAL
VALOX™ FR Resin 855
VALOX™ 420SE0M resin
单位
UNIT
测试方法
TEST METHOD
弯曲应变(at Break)
Bending strain
%
ISO 178
弯曲强度
bending strength
MPa
ISO 178
弯曲强度(--)
bending strength
MPa
ISO 178
弯曲强度(屈服，50 mm跨度)
bending strength
MPa
ASTM D790
弯曲强度(断裂，50 mm跨度)
bending strength
MPa
ASTM D790
弯曲模量(--)
Bending modulus
MPa
ISO 178
弯曲模量(2 mm/mim)
Bending modulus
MPa
ISO 178
弯曲模量(50 mm跨距)
Bending modulus
MPa
ASTM D790
拉伸应变(屈服)
Tensile strain
%
ASTM D638
拉伸应变(屈服)
Tensile strain
%
ISO 527-2/5
拉伸应变(屈服，1.3 mm/min，50 mm跨度)
Tensile strain
%
ISO 527
拉伸应变(断裂)
Tensile strain
%
ASTM D638
拉伸应变(断裂)
Tensile strain
%
ISO 527-2/5
拉伸应变(断裂，1.3 mm/min，50 mm跨度)
Tensile strain
%
ISO 527
拉伸强度(5 mm/min)
tensile strength
拉伸强度(屈服)
tensile strength
MPa
ASTM D638
拉伸强度(屈服)
tensile strength
MPa
ISO 527
拉伸强度(屈服)
tensile strength
MPa
ISO 527-2/5
拉伸强度(断裂)
tensile strength
MPa
ASTM D638
拉伸强度(断裂)
tensile strength
MPa
ISO 527
拉伸强度(断裂)
tensile strength
MPa
ISO 527-2/5
拉伸模量(--)
Tensile modulus
MPa
ASTM D638
拉伸模量(--)
Tensile modulus
MPa
ISO 527-1-2
拉伸模量(1 mm/min)
Tensile modulus
MPa
ISO 527
泰伯磨损(CS-17，1kg)
Taber wear and tear
mg/1000cy
内部方法
泰伯耐磨性(1000 周期，1000 g，CS-17 转轮)
Taber abraser
mg
内部方法
洛氏硬度
Rockwell hardness
ASTM D785
洛氏硬度
Rockwell hardness
ISO 2039-2
洛氏硬度(R 级)
Rockwell hardness
ISO 2039-2
球压硬度(H358/30)
Ball hardness
MPa
ISO 2039-1
物理性能
PHYSICAL
VALOX™ FR Resin 855
VALOX™ 420SE0M resin
单位
UNIT
测试方法
TEST METHOD
吸水率(23℃，50% RH)
Water absorption rate
%
ISO 62
吸水率(平衡，23℃，50% RH)
Water absorption rate
%
吸水率(饱和，23℃)
Water absorption rate
%
吸水率(饱和，23℃)
Water absorption rate
%
ISO 62
密度
Density
g/cm³
ASTM D792
密度
Density
g/cm³
ISO 1183
拉伸杆收缩模具(TD)
Stretching rod shrinkage mold
%
SABIC Method
拉伸杆收缩模具(流动)
Stretching rod shrinkage mold
%
SABIC Method
收缩率(MD)
Shrinkage rate
%
收缩率(MD：3.2 mm)
Shrinkage rate
%
收缩率(MD：3.2 mm)
Shrinkage rate
%
内部方法
收缩率(TD)
Shrinkage rate
%
收缩率(TD：3.2 mm)
Shrinkage rate
%
内部方法
比积
Specific product
cm³/g
ASTM D 792
熔体体积流动速率(250℃，5 kg)
Melt Volume Rate
cm³/10min
熔体体积流动速率(250℃，5 kg)
Melt Volume Rate
cm³/10min
ISO 1133
熔体体积流动速率(265℃，1.2 kg)
Melt Volume Rate
cm³/10min
熔体体积流动速率(265℃，5 kg)
Melt Volume Rate
cm³/10min
熔体表观粘度(260℃，1500 sec^-1)
Apparent viscosity of melt
Pa·s
ISO 11443
熔体质量流动速率(250℃，5.0kg)
Melt Flow Rate
g/10min
ASTM D1238
熔体质量流动速率(266℃，5.0kg)
Melt Flow Rate
g/10min
ASTM D1238
高亮区别
隐藏相同