PC+ABS，CYCOLOY™ FR Resin CM6140对比PC+ABS，CYCOLOY™ FR Resin NX07353物性表,价格行情_搜料

牌号信息	CYCOLOY™ FR Resin CM6140 物性表 PC+ABS & 沙特沙伯基础指导价格：暂无塑料库存：缺货	CYCOLOY™ FR Resin NX07353 物性表 PC+ABS & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	Cycoloy CM6140聚碳酸酯/丙烯腈-丁二烯-苯乙烯（PC/ABS）树脂是一种矿物填充级低翘曲，可注塑成型。这种无氯化、无溴阻燃PC/ABS具有UL V0和5VB的阻燃等级。Cycoloy CM6140树脂是各种薄壁应用（包括外壳）的理想选择。 CYCOLOY CM6140 Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) resin is a mineral filled grade, low warpage that can be injection molded. This non-chlorinated, non-brominated flame retardant PC/ABS has a UL V0 & 5VB flame rating. CYCOLOY CM6140 resin is an excellent candidate for a wide variety of thin wall applications including enclosures.	Cycoloy C7230P树脂是一种矿物填充的阻燃PC/ABS。良好的刚度，平衡的流动和冲击性能，使其成为各种应用的理想选择。 CYCOLOY C7230P resin is a mineral filled, flame retardant PC/ABS. Good stiffness combined with balanced flow and impact performance, makes it a good candidate for various applications.

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PC+ABS PC+ABS	PC+ABS PC+ABS
填料：	矿物	矿物
用途：	电器用具,电子显示器,电气/电子应用领域,液体处理,药物
性能特点：	机械强度好,冲击性能好,易流动,无卤,阻燃,耐热性好 Good Rigidity,High impact resistance,Good liquidity,Halogen free,Flame Characteristics,Heat Resistance, Good	机械强度好,冲击性能好,易流动,阻燃 Good Rigidity,High impact resistance,Good liquidity,Flame Characteristics
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL CYCOLOY™ FR Resin CM6140 CYCOLOY™ FR Resin NX07353 单位
UNIT 测试方法
TEST METHOD

吸水率(24hr)
Water absorption rate % ASTM D570

吸水率(24hr，50% RH)
Water absorption rate % ASTM D570

吸水率(平衡，23℃，50% RH)
Water absorption rate %

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate %

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度(--)
Density g/cm³ ASTM D792

密度(--)
Density g/cm³ ISO 1183

收缩率(MD：3.2 mm)
Shrinkage rate %

收缩率(MD：3.2 mm)
Shrinkage rate % 内部方法

收缩率(TD：3.2 mm)
Shrinkage rate %

熔体体积流动速率(220℃，5 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体体积流动速率(260℃，2.16 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(260℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL CYCOLOY™ FR Resin CM6140 CYCOLOY™ FR Resin NX07353 单位
UNIT 测试方法
TEST METHOD

弯曲强度(--)
bending strength MPa ISO 178

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/5

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/5

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT CYCOLOY™ FR Resin CM6140 CYCOLOY™ FR Resin NX07353 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL CYCOLOY™ FR Resin CM6140 CYCOLOY™ FR Resin NX07353 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，6.4 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，4.0 mm，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

热变形温度(1.8 MPa，未退火，6.4 mm)
Hot deformation temperature ℃ ASTM D648

球压测试(73~77℃)
Ball pressure test IEC 60695-10-2

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：-40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度(--)
Vicat Softening Temp ℃ ASTM D1525 10

维卡软化温度(--)
Vicat Softening Temp ℃ ASTM D1525 12

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

电气性能
ELECTRICAL CYCOLOY™ FR Resin CM6140 CYCOLOY™ FR Resin NX07353 单位
UNIT 测试方法
TEST METHOD

体积电阻率
Volume resistivity ohms·cm ASTM D257

表面电阻率
Surface resistivity ohms ASTM D257

阻燃性能
FLAMMABILITY CYCOLOY™ FR Resin CM6140 CYCOLOY™ FR Resin NX07353 单位
UNIT 测试方法
TEST METHOD

灼热丝可燃性指数(0.80 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

灼热丝起燃温度(1 mm)
Igniting temperature of the hot wire ℃

灼热丝起燃温度(3 mm)
Igniting temperature of the hot wire ℃

阻燃等级(0.60 mm)
Flame retardant level

阻燃等级(0.80 mm)
Flame retardant level

阻燃等级(1.20 mm)
Flame retardant level

阻燃等级(1.50 mm)
Flame retardant level

阻燃等级(2.00 mm)
Flame retardant level

加工方式

注射 CYCOLOY™ FR Resin CM6140 CYCOLOY™ FR Resin NX07353 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议注射量 %

建议的最大水分含量 %

排气孔深度 mm

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

注射说明 CYCOLOY™ FR Resin CM6140 CYCOLOY™ FR Resin NX07353 单位测试方法

备注

3. 5.0 mm/min

4. 类型 1, 50 mm/min

5. 类型 1, 5.0 mm/min

6. 1.3 mm/min

7. 2.0 mm/min

8. at Yield

9. 80*10*3 sp=62mm

10. 80*10*3 mm

11. 80*10*4 mm

12. 速率 A (50°C/h), 载荷2 (50N)

3. 5.0 mm/min

4. 类型 1, 50 mm/min

5. 1.3 mm/min

6. 2.0 mm/min

7. at Yield

8. 80*10*4 sp=62mm

9. 80*10*4 mm

10. 速率 A (50°C/h), 载荷2 (50N)


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
加工方式
注射
注射说明
备注