牌号信息	Fortron® 1131L4 ITT 物性表 PPS & 美国塞拉尼斯指导价格：暂无塑料库存：缺货	Fortron® 1130L4 物性表 PPS & 美国塞拉尼斯指导价格：暂无塑料库存： 96800kg
牌号简介	Fortron® 1131L4 ITT是一种聚苯硫醚(PPS)产品,含有的填充物为30% 玻璃纤维增强材料。它,在北美洲、拉丁美洲、欧洲或非洲和中东有供货。主要特性为:阻燃/额定火焰。 Fortron® 1131L4 ITT is a Polyphenylene Sulfide (PPS) product filled with 30% glass fiber. It is available in Africa & Middle East, Europe, Latin America, or North America. Primary characteristic: flame rated.	Fortron® 1130L4是一种30%的玻璃纤维增强聚苯硫醚，具有优异的耐热性和耐化学性。它本身具有阻燃性，硬度高，强度和刚度平衡良好。特别适用于需要较长流动长度的薄壁零件。由于填料含量低，该等级在二次操作中也表现出良好的可焊性。 Fortron 1130L4 is a 30% glass-reinforced PPS that has excellent heat and chemical resistance. It is inherently flame-retardant and exhibits high hardness and a good balance of strength and stiffness. Especially used for thin walled parts requiring long flow lengths. This grade also exhibits excellent weldability in secondary operations due to its low filler content.

产品描述
厂家：	美国塞拉尼斯 Celanese	美国塞拉尼斯 Celanese
类别：	PPS PPS	PPS PPS
填料：	玻璃纤维 30	玻璃纤维 30
用途：		薄壁部件
性能特点：	防火阻燃等级V-0 V-0	机械强度好,硬度高,阻燃,耐高温,耐化学性,焊接,防火阻燃等级V-0 Good Rigidity,Good Hardness,Flame Characteristics,High Heat Resistance,Solvent resistance,Welding,V-0
加工条件：

技术参数

物理性能
PHYSICAL Fortron® 1131L4 ITT Fortron® 1130L4 单位
UNIT 测试方法
TEST METHOD

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage rate % ASTM D955

收缩率(MD)
Shrinkage rate % ISO 294-4

收缩率(TD)
Shrinkage rate % ASTM D955

收缩率(TD)
Shrinkage rate % ISO 294-4

特定体积
Specific volume cm³/g ASTM D792

冲击性能
IMPACT Fortron® 1131L4 ITT Fortron® 1130L4 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL Fortron® 1131L4 ITT Fortron® 1130L4 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(8.0 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/C

熔融温度
Melting temperature ℃ ISO 11357-3

玻璃化转变温度
Glass transition temperature ℃ ISO 11357-2

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

电气性能
ELECTRICAL Fortron® 1131L4 ITT Fortron® 1130L4 单位
UNIT 测试方法
TEST METHOD

介电常数(1 kHz)
Dielectric constant ASTM D150

介电常数(1 MHz)
Dielectric constant ASTM D150

体积电阻率
Volume resistivity ohms·cm ASTM D257

体积电阻率
Volume resistivity ohms·cm IEC 60093

相比漏电起痕指数
Compared to the leakage tracing index V ASTM D3638

耐电弧性
Arc resistance sec ASTM D495

耗散因数(1 kHz)
Dissipation factor ASTM D150

耗散因数(1 MHz)
Dissipation factor ASTM D150

表面电阻率
Surface resistivity ohms IEC 60093

阻燃性能
FLAMMABILITY Fortron® 1131L4 ITT Fortron® 1130L4 单位
UNIT 测试方法
TEST METHOD

阻燃等级(0.38 mm)
Flame retardant level UL 94

阻燃等级(0.80 mm)
Flame retardant level UL 94

阻燃等级(1.50 mm)
Flame retardant level UL 94

机械性能
MECHANICAL Fortron® 1131L4 ITT Fortron® 1130L4 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲模量(23℃)
Bending modulus MPa ISO 178

拉伸应变(断裂)
Tensile strain % ISO 527-2/1A/5

拉伸应变(断裂，23℃)
Tensile strain % ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/1A/5

拉伸强度(断裂，23℃)
tensile strength MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-2/1A/1

洛氏硬度(M 级)
Rockwell hardness ASTM D785

洛氏硬度(M 级)
Rockwell hardness ISO 2039-2

补充信息
Fortron® 1131L4 ITT Fortron® 1130L4 单位
UNIT 测试方法
TEST METHOD

Specimen Thickness(Shrinkage)
Specimen Thickness（Shrinkage） mm Internal Method

加工方式

注射 Fortron® 1131L4 ITT Fortron® 1130L4 单位测试方法

保压 MPa

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料斗温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

注射速度

背压 MPa

备注

1 一般属性：这些不能被视为规格。

2 Break

3 10°C/min

1 一般属性：这些不能被视为规格。

2 Break

3 10°C/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
电气性能
阻燃性能
机械性能
补充信息
加工方式
注射
备注
返回顶部

PPS，Fortron® 1131L4 ITT对比PPS，Fortron® 1130L4对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别