PA66，Durethan® AKV30XTS3 901510对比PA66，Durethan® AKV30GH2.0 900051 SR1物性表,价格行情_搜料

牌号信息	Durethan® AKV30XTS3 901510 物性表 PA66 & 德国恩骅力指导价格：暂无塑料库存：缺货	Durethan® AKV30GH2.0 900051 SR1 物性表 PA66 & 德国恩骅力指导价格：暂无塑料库存：缺货
牌号简介	PA 66，30%玻璃纤维，注塑成型，热老化稳定，高温稳定 Durethan® AKV30XTS3 901510 (Dry) PA 66, 30 % glass fibers, injection molding, heat-aging stabilized, high temperature stabilized Durethan® AKV30XTS3 901510 PA 66, 30 % glass fibers, injection molding, heat-aging stabilized, high temperature stabilized Durethan® AKV30XTS3 901510 PA 66, 30 % glass fibers, injection molding, heat-aging stabilized, high temperature stabilized	PA 66，30%玻璃纤维，注塑成型，热老化稳定，改善表面光洁度 Durethan® AKV30GH2.0 900051 SR1 (Dry) PA 66, 30 % glass fibers, injection molding, heat-aging stabilized, improved surface finish Durethan® AKV30GH2.0 900051 SR1 PA 66, 30 % glass fibers, injection molding, heat-aging stabilized, improved surface finish Durethan® AKV30GH2.0 900051 SR1 PA 66, 30 % glass fibers, injection molding, heat-aging stabilized, improved surface finish

产品描述
厂家：	德国恩骅力 Envalior	德国恩骅力 Envalior
类别：	PA66 PA66	PA66 PA66
填料：	玻璃纤维 30	玻璃纤维 30
用途：
性能特点：	热稳定性好 Heat Stabilized	表面光泽度好,热稳定性好 Good surface appearance,Heat Stabilized
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Durethan® AKV30XTS3 901510 Durethan® AKV30GH2.0 900051 SR1 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate %

吸水率(饱和，23℃)
Water absorption rate %

密度
Density g/cm³

收缩率(MD：120℃，2.0 mm)
Shrinkage rate %

收缩率(MD：120℃，3.0 mm)
Shrinkage rate %

收缩率(MD：290℃，2.0 mm)
Shrinkage rate %

收缩率(MD：290℃，3.0 mm)
Shrinkage rate %

收缩率(TD：120℃，2.0 mm)
Shrinkage rate %

收缩率(TD：120℃，3.0 mm)
Shrinkage rate %

收缩率(TD：290℃，2.0 mm)
Shrinkage rate %

收缩率(TD：290℃，3.0 mm)
Shrinkage rate %

表观密度
Apparent density g/cm³

机械性能
MECHANICAL Durethan® AKV30XTS3 901510 Durethan® AKV30GH2.0 900051 SR1 单位
UNIT 测试方法
TEST METHOD

弯曲应变
Bending strain %

弯曲强度(23℃)
bending strength MPa

弯曲强度(3.50% 应变，23℃)
bending strength MPa

弯曲模量(23℃)
Bending modulus MPa

拉伸应变(断裂，23℃)
Tensile strain %

拉伸强度(断裂，23℃)
tensile strength MPa

拉伸模量(23℃)
Tensile modulus MPa

球压硬度
Ball hardness MPa

冲击性能
IMPACT Durethan® AKV30XTS3 901510 Durethan® AKV30GH2.0 900051 SR1 单位
UNIT 测试方法
TEST METHOD

多轴向仪器化冲击力峰值(-30℃)
Multi axial instrumented peak impact force N

多轴向仪器化冲击力峰值(23℃)
Multi axial instrumented peak impact force N

多轴向仪器化冲击能量(-30℃，冲击总贯穿能量)
Multi axial instrumented impact energy J

多轴向仪器化冲击能量(23℃，冲击总贯穿能量)
Multi axial instrumented impact energy J

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam kJ/m²

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m²

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m²

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m²

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m²

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m²

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(-40℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m²

热性能
THERMAL Durethan® AKV30XTS3 901510 Durethan® AKV30GH2.0 900051 SR1 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃

热变形温度(8.0 MPa，未退火)
Hot deformation temperature ℃

熔融温度
Melting temperature ℃

线性热膨胀系数(MD：23~55℃)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(TD：23~55℃)
Linear coefficient of thermal expansion 1/℃

维卡软化温度
Vicat Softening Temp ℃

补充信息
Durethan® AKV30XTS3 901510 Durethan® AKV30GH2.0 900051 SR1 单位
UNIT 测试方法
TEST METHOD

ISO Shortname
ISO Shortname

电气性能
ELECTRICAL Durethan® AKV30XTS3 901510 Durethan® AKV30GH2.0 900051 SR1 单位
UNIT 测试方法
TEST METHOD

介电强度(23 ℃，1 mm)
Dielectric strength kV/mm

体积电阻率(23℃)
Volume resistivity ohms·cm

相对电容率(23℃，1 MHz)
Relative permittivity

相对电容率(23℃，100 Hz)
Relative permittivity

相比漏电起痕指数(解决方案 A)
Compared to the leakage tracing index V

耗散因数(23℃，1 MHz)
Dissipation factor

耗散因数(23℃，100 Hz)
Dissipation factor

表面电阻率
Surface resistivity ohms

阻燃性能
FLAMMABILITY Durethan® AKV30XTS3 901510 Durethan® AKV30GH2.0 900051 SR1 单位
UNIT 测试方法
TEST METHOD

US FMVSS302
US FMVSS302

极限氧指数
Extreme oxygen index %

灼热丝可燃性指数(2.0 mm)
Glowing wire flammability index ℃

阻燃等级(1.50 mm)
Flame retardant level

加工方式

注射 Durethan® AKV30XTS3 901510 Durethan® AKV30GH2.0 900051 SR1 单位测试方法

Admissible Residence Time at Tmax min

Residual Moisture Content % Karl Fisher

加工熔体温度 °C

干燥时间 - Dry Air Dryer hr

干燥温度 - Dry Air Dryer °C

模具温度 °C

备注

2. 60x60x2mm, 4 hr

3. 60x60x2mm, 80°C MT, 500 bar

4. 60x60x2mm, 80°C MT, 600 bar

5. 2.0 mm/min

6. 2 mm/min

7. 10°C/min

2. 150x105x3mm, 4 hr

3. 150x105x3mm, 80°C MT, 500 bar

4. 2.0 mm/min

5. 2 mm/min

6. 10°C/min

7. 程序 A


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
补充信息
电气性能
阻燃性能
加工方式
注射
备注
返回顶部