PC，LEXAN™ Copolymer FST3002对比PC，LEXAN™ FST3002 resin物性表,价格行情_搜料

牌号信息	LEXAN™ Copolymer FST3002 物性表 PC & 沙特沙伯基础指导价格：暂无塑料库存：缺货	LEXAN™ FST3002 resin 物性表 PC & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	LEXAN FST3002树脂是MVR为8的无卤阻燃PC共聚树脂，适用于注塑成型。该树脂符合EN45545 R6 HL2标准，是列车内部应用（R6类）的理想选择。提供不透明色 LEXAN FST3002 resin is a halogen-free flame retardant PC Copolymer Resin with MVR of 8, suitable for injection molding. This resin is EN45545 R6 HL2 compliant and an ideal candidate for train interior applications (category R6). Available in opaque colors	LEXAN™ FST3002 resin是一种无卤阻燃PC共聚物树脂，MVR为8，适用于注塑成型。该树脂符合EN45545 R6 HL2标准，是列车内部应用（R6类）的理想选择。提供不透明色 LEXAN FST3002 resin is a halogen-free flame retardant PC Copolymer Resin with MVR of 8, suitable for injection molding. This resin is EN45545 R6 HL2 compliant and an ideal candidate for train interior applications (category R6). Available in opaque colors

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PC Polycarbonate	PC Polycarbonate
填料：
用途：	电气/电子应用领域,Rail Applications
性能特点：	无卤,阻燃,共聚物 Halogen free,Flame Characteristics,Copolymer	无卤,阻燃,共聚物 Halogen free,Flame Characteristics,Copolymer
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LEXAN™ Copolymer FST3002 LEXAN™ FST3002 resin 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ASTM D792, ISO 1183

收缩率(MD)
Shrinkage rate %

收缩率(TD)
Shrinkage rate %

熔体体积流动速率(300℃，1.2 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(300℃，1.20kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL LEXAN™ Copolymer FST3002 LEXAN™ FST3002 resin 单位
UNIT 测试方法
TEST METHOD

弯曲强度(--)
bending strength MPa ISO 178

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT LEXAN™ Copolymer FST3002 LEXAN™ FST3002 resin 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m²

装有测量仪表的落镖冲击(--)
Dart impact equipped with measuring instruments J ISO 6603-2

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LEXAN™ Copolymer FST3002 LEXAN™ FST3002 resin 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，4.0 mm，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(0.45 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，4.0 mm，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃

维卡软化温度(--)
Vicat Softening Temp ℃ ASTM D1525 10

维卡软化温度(--)
Vicat Softening Temp ℃ ISO 306/A120

维卡软化温度(B50)
Vicat Softening Temp ℃ ASTM D1525, ISO 306/B50, ISO 306/B120 20

阻燃性能
FLAMMABILITY LEXAN™ Copolymer FST3002 LEXAN™ FST3002 resin 单位
UNIT 测试方法
TEST METHOD

Fire Safety Hazard Level(Requirement set R6)
Fire Safety Hazard Level（Requirement set R6） EN 45545-2

Smoke Toxicity - CITG(8 min)(3.00 mm)
Smoke Toxicity - CITG（8 min）（3.00 mm） ISO 5659-2

Smoke Toxicity - CITG(8 min)，50 kW/m²(3.00 mm)
Smoke Toxicity - CITG（8 min），50 kW/m²（3.00 mm） ISO 5659-2

放热(MAHRE，3.00 mm)
exothermic kW/m² ISO 5660-1

散热量，MAHRE - 50 kW/m²(3.00 mm)
Heat dissipation, MAHRE -50 kW/m ² kW/m² ISO 5660-1

烟雾密度(DS-4，50 kW/m²：3.00 mm)
Smoke density

烟雾密度(DS-4：3.00 mm)
Smoke density

烟雾密度(VOF4，50 kW/m²：3.00 mm)
Smoke density

烟雾密度(VOF4：3.00 mm)
Smoke density

加工方式

注射 LEXAN™ Copolymer FST3002 LEXAN™ FST3002 resin 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料斗温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

备注

2. 50 mm/min

3. 类型 1, 50 mm/min

4. 1.3 mm/min

5. 2.0 mm/min

6. at Yield

7. 80*10*3 sp=62mm

8. 80*10*3 mm

9. 80*10*4 mm

10. 速率 A (50°C/h), 载荷2 (50N)

11. 50 kW/m²

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 类型 1, 2.0 in/min

4 0.051 in/min

5 0.079 in/min

6 Yield

7 80*10*3 sp=62mm

8 80*10*4 sp=62mm

9 80*10*3

10 80*10*4

11 80*10*4 mm

12 标准 B (120°C/h), 载荷2 (50N)


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
阻燃性能
加工方式
注射
备注