PA6，Durethan® BKV140H2.0 900051对比PA6，Durethan® BKV140 000000物性表,价格行情_搜料

牌号信息	Durethan® BKV140H2.0 900051 物性表 PA6 & 德国恩骅力指导价格：暂无塑料库存：缺货	Durethan® BKV140 000000 物性表 PA6 & 德国恩骅力指导价格：暂无塑料库存：缺货
牌号简介	PA 6-共聚物，40%玻璃纤维，注塑成型，提高冲击强度，热老化稳定 Durethan® BKV140H2.0 900051 (Dry) PA 6-Copolymer, 40 % glass fibers, injection molding, improved impact strength, heat-aging stabilized Durethan® BKV140H2.0 900051 PA 6-Copolymer, 40 % glass fibers, injection molding, improved impact strength, heat-aging stabilized Durethan® BKV140H2.0 900051 PA 6-Copolymer, 40 % glass fibers, injection molding, improved impact strength, heat-aging stabilized	PA 6-共聚物，40%玻璃纤维，注塑成型，提高冲击强度 Durethan® BKV140 000000 (Dry) PA 6-Copolymer, 40 % glass fibers, injection molding, improved impact strength Durethan® BKV140 000000 PA 6-Copolymer, 40 % glass fibers, injection molding, improved impact strength Durethan® BKV140 000000 PA 6-Copolymer, 40 % glass fibers, injection molding, improved impact strength

产品描述
厂家：	德国恩骅力 Envalior	德国恩骅力 Envalior
类别：	PA6 PA6	PA6 PA6
填料：	玻璃纤维 40	玻璃纤维 40
用途：
性能特点：	热稳定性好,共聚物,冲击性能好 Heat Stabilized,Copolymer,High impact resistance	冲击性能好,共聚物 High impact resistance,Copolymer
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Durethan® BKV140H2.0 900051 Durethan® BKV140 000000 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate %

吸水率(饱和，23℃)
Water absorption rate %

密度
Density g/cm³

密度(--)
Density g/cm³

密度(23℃)
Density g/cm³

收缩率(MD：120℃，3.0 mm)
Shrinkage rate %

收缩率(MD：290℃，3.0 mm)
Shrinkage rate %

收缩率(TD：120℃，3.0 mm)
Shrinkage rate %

收缩率(TD：290℃，3.0 mm)
Shrinkage rate %

表观密度
Apparent density g/cm³

机械性能
MECHANICAL Durethan® BKV140H2.0 900051 Durethan® BKV140 000000 单位
UNIT 测试方法
TEST METHOD

弯曲应变
Bending strain %

弯曲强度(23℃)
bending strength MPa

弯曲强度(3.50% 应变，23℃)
bending strength MPa

弯曲模量(23℃)
Bending modulus MPa

拉伸应变(断裂，23℃)
Tensile strain %

拉伸强度(断裂，23℃)
tensile strength MPa

拉伸模量(23℃)
Tensile modulus MPa

拉伸蠕变模量(1 hr)
Tensile creep modulus MPa

拉伸蠕变模量(1000 hr)
Tensile creep modulus MPa

球压硬度
Ball hardness MPa

冲击性能
IMPACT Durethan® BKV140H2.0 900051 Durethan® BKV140 000000 单位
UNIT 测试方法
TEST METHOD

多轴向仪器化冲击力峰值(-30℃)
Multi axial instrumented peak impact force N

多轴向仪器化冲击力峰值(23℃)
Multi axial instrumented peak impact force N

多轴向仪器化冲击能量(-30℃，冲击总贯穿能量)
Multi axial instrumented impact energy J

多轴向仪器化冲击能量(23℃，冲击总贯穿能量)
Multi axial instrumented impact energy J

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam kJ/m²

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m²

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m²

悬臂梁缺口冲击强度(-40℃，3.2mm)
Impact strength of cantilever beam notch J/m

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m²

悬臂梁缺口冲击强度(23℃，3.2mm)
Impact strength of cantilever beam notch J/m

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m²

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m²

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m²

热性能
THERMAL Durethan® BKV140H2.0 900051 Durethan® BKV140 000000 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃

热变形温度(0.45 MPa，未退火，4.0 mm)
Hot deformation temperature ℃

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃

热变形温度(1.8 MPa，未退火，3.99 mm)
Hot deformation temperature ℃

热变形温度(8.0 MPa，未退火)
Hot deformation temperature ℃

熔融温度
Melting temperature ℃

线性热膨胀系数(MD：23~55℃)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(TD：23~55℃)
Linear coefficient of thermal expansion 1/℃

维卡软化温度
Vicat Softening Temp ℃

维卡软化温度(--)
Vicat Softening Temp ℃

电气性能
ELECTRICAL Durethan® BKV140H2.0 900051 Durethan® BKV140 000000 单位
UNIT 测试方法
TEST METHOD

介电常数(23 ℃，1 MHz)
Dielectric constant

介电常数(23 ℃，100 Hz)
Dielectric constant

介电常数(23 ℃，50 Hz)
Dielectric constant

介电强度(23 ℃，1 mm)
Dielectric strength kV/mm

介电强度(23 ℃，3 mm)
Dielectric strength kV/mm

体积电阻率(23℃)
Volume resistivity ohms·cm

相对电容率(23℃，1 MHz)
Relative permittivity

相对电容率(23℃，100 Hz)
Relative permittivity

相比漏电起痕指数(CTI)
Compared to the leakage tracing index V

相比漏电起痕指数(解决方案 A)
Compared to the leakage tracing index V

相比漏电起痕指数(解决方案 B)
Compared to the leakage tracing index V

耐电弧性
Arc resistance sec

耗散因数(23℃，1 MHz)
Dissipation factor

耗散因数(23℃，100 Hz)
Dissipation factor

耗散因数(23℃，50 Hz)
Dissipation factor

表面电阻率
Surface resistivity ohms

阻燃性能
FLAMMABILITY Durethan® BKV140H2.0 900051 Durethan® BKV140 000000 单位
UNIT 测试方法
TEST METHOD

US FMVSS302
US FMVSS302

极限氧指数
Extreme oxygen index %

灼热丝可燃性指数(2.0 mm)
Glowing wire flammability index ℃

阻燃等级(0.75 mm)
Flame retardant level

阻燃等级(1.50 mm)
Flame retardant level

补充信息
Durethan® BKV140H2.0 900051 Durethan® BKV140 000000 单位
UNIT 测试方法
TEST METHOD

ISO Shortname
ISO Shortname

加工方式

注射 Durethan® BKV140H2.0 900051 Durethan® BKV140 000000 单位测试方法

Residual Moisture Content % Karl Fisher

加工熔体温度 °C

干燥时间 - Dry Air Dryer hr

干燥温度 - Dry Air Dryer °C

模具温度 °C

备注

3. 150x105x3mm, 4 hr

4. 150x105x3mm, 80°C MT, 500 bar

5. 2.0 mm/min

6. 2 mm/min

7. 10°C/min

8. 程序 A

3. 150x105x3mm, 4 hr

4. 150x105x3mm, 80°C MT, 400 bar

5. 1.0 mm/min

6. 2.0 mm/min

7. 2 mm/min

8. 10°C/min

9. Tinfoil Electrodes

10. Tungsten Electrodes

11. 程序 A


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
补充信息
加工方式
注射
备注
返回顶部

PA6，Durethan® BKV140H2.0 900051对比PA6，Durethan® BKV140 000000对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别