PP均聚，ALTECH® NXT PP-H A 2330/456 LE GF20 GB10 CP对比PP均聚，SAXALEN™ PPH325GK20物性表,价格行情_搜料

牌号信息	ALTECH® NXT PP-H A 2330/456 LE GF20 GB10 CP 物性表 PP均聚 & 德国爱彼斯指导价格：暂无塑料库存：缺货	SAXALEN™ PPH325GK20 物性表 PP均聚 & 奥地利SAX 指导价格：暂无塑料库存：缺货
牌号简介	ALTECH® NXT PP-H A 2330/456 LE GF20 GB10 CP是一种聚丙烯均聚物(PP Homopoly)产品,含有的填充物为20% 玻璃纤维增强材料和 10% 玻璃珠。它可以通过注射成型进行加工,在北美洲、欧洲或亚太地区有供货。典型应用领域为:汽车行业。特性包括: 阻燃/额定火焰通过 ROHS 认证低排放量高刚度化学耦合 ALTECH® NXT PP-H A 2330/456 LE GF20 GB10 CP is a Polypropylene Homopolymer (PP Homopolymer) product filled with 10% glass bead and 20% glass fiber. It can be processed by injection molding and is available in Asia Pacific, Europe, or North America. Typical application: Automotive. Characteristics include: Flame Rated RoHS Compliant Chemically Coupled Heat Stabilizer High Stiffness	SAXALEN™ PPH325GK20是一种20%玻璃纤维和玻璃珠填充聚丙烯均聚物，用于注塑成型。这种类型具有增加的刚度和优化的翘曲等级。 SAXALEN PPH325GK20 is a 20% glass-fiber and glass-beads filled Polypropylene - Homopolymer intended for injection molding. This type has a increased stiffness and a optimized warpage grade.

产品描述
厂家：	德国爱彼斯 ALBIS	奥地利SAX
类别：	PP均聚 PP homopolymerization	PP均聚 PP homopolymerization
填料：	玻璃纤维/玻璃珠 20:10	玻璃纤维/玻璃珠 20
用途：	汽车领域的应用
性能特点：	机械强度好,低VOC,化学耦合,热稳定性好,均聚物 Good Rigidity,Low odor,Chemical coupling,Heat Stabilized,Homopolymer	机械强度好,低翘曲性 Good Rigidity,Low warping
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL ALTECH® NXT PP-H A 2330/456 LE GF20 GB10 CP SAXALEN™ PPH325GK20 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³

密度
Density g/cm³ ISO 1183

收缩率(MD：24 hrs)
Shrinkage rate %

收缩率(TD：24 hrs)
Shrinkage rate %

熔体质量流动速率
Melt Flow Rate g/10min ISO 1033

螺旋流动长度(1.00 mm)
Spiral flow length n

螺旋流动长度(2.00 mm)
Spiral flow length n

机械性能
MECHANICAL ALTECH® NXT PP-H A 2330/456 LE GF20 GB10 CP SAXALEN™ PPH325GK20 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲强度(23℃)
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(23℃)
Bending modulus MPa ISO 178

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸应变(断裂，23℃)
Tensile strain % ISO 527-2

拉伸强度(23℃)
tensile strength MPa ISO 527-2

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸模量
Tensile modulus MPa ISO 527-2

拉伸模量(23℃)
Tensile modulus MPa ISO 527-2

冲击性能
IMPACT ALTECH® NXT PP-H A 2330/456 LE GF20 GB10 CP SAXALEN™ PPH325GK20 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(--)
Charpy Unnotch Impact strength kJ/m²

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(-40℃)
Charpy Unnotch Impact strength kJ/m²

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度(--)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(-40℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL ALTECH® NXT PP-H A 2330/456 LE GF20 GB10 CP SAXALEN™ PPH325GK20 单位
UNIT 测试方法
TEST METHOD

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(1.8 MPa，退火)
Hot deformation temperature ℃ ISO 75-2/Af

熔融温度(DSC)
Melting temperature ℃ ISO 11357

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

阻燃性能
FLAMMABILITY ALTECH® NXT PP-H A 2330/456 LE GF20 GB10 CP SAXALEN™ PPH325GK20 单位
UNIT 测试方法
TEST METHOD

阻燃等级(1.50 mm)
Flame retardant level UL 94

加工方式

注射 ALTECH® NXT PP-H A 2330/456 LE GF20 GB10 CP SAXALEN™ PPH325GK20 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

模具温度 °C

注塑温度模具温度 °C

注塑温度螺筒后部温度 °C

备注

1 一般属性：这些不能被视为规格。

2 0.079 in/min

3 80*10*4mm


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
阻燃性能
加工方式
注射
备注
返回顶部