PA6+PO，Edgetek™ ET6500-5006 natural对比PA6+PO，INNOMID® CS 6-9000物性表,价格行情_搜料

牌号信息	Edgetek™ ET6500-5006 natural 物性表 PA6+PO & 美国普立万指导价格：暂无塑料库存：缺货	INNOMID® CS 6-9000 物性表 PA6+PO & 匈牙利Inno-Comp 指导价格：暂无塑料库存：缺货
牌号简介	Edgetek工程热塑性化合物产品组合涵盖广泛的标准和定制高性能材料。该产品组合包括用于高温工作环境的高温材料、用于承载和高强度应用的高模量/结构材料以及阻燃产品。这些化合物是基于选择的工程热塑性树脂，与增强添加剂，如碳纤维，玻璃纤维和玻璃珠复合。 The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for elevated service temperature environments, high-modulus / structural materials for load-bearing and high-strength applications and flame-retardant products. These compounds are based on select engineering thermoplastic resins that are compounded with reinforcing additives such as carbon fiber, glass fiber and glass beads.	Innomid CS 6-9000是一种未填充的聚酰胺（PA-6）化合物。该等级有自然色和定制色两种形式。推荐应用Innomid CS 6-9000用于生产注塑产品，要求的性能是高强度和刚度。 INNOMID ® CS 6-9000 is an unfilled polyamide (PA-6) compound. This grade is available in nature and custom coloured form. Recommended application INNOMID ® CS 6-9000 is recommended for producing injection moulded products, where the required properties are high strength and stiffness.

产品描述
厂家：	美国普立万 Polyone	匈牙利Inno-Comp
类别：	PA6+PO PA6 Alloy	PA6+PO PA6 Alloy
填料：	碳纤维
用途：	通用
性能特点：		机械强度好 Good Rigidity
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Edgetek™ ET6500-5006 natural INNOMID® CS 6-9000 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage rate % ISO 294-4

收缩率(TD)
Shrinkage rate % ISO 294-4

熔体体积流动速率(275℃，5 kg)
Melt Volume Rate cm³/10min ISO 1133

机械性能
MECHANICAL Edgetek™ ET6500-5006 natural INNOMID® CS 6-9000 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ISO 527-2/1A/50

拉伸应变(屈服，23℃，4 mm，注塑成型)
Tensile strain % ISO 527-2

拉伸应变(断裂)
Tensile strain % ISO 527-2/1A/50

拉伸强度(屈服)
tensile strength MPa ISO 527-2/1A/50

拉伸强度(屈服，23℃，4.00 mm，注塑成型)
tensile strength MPa ISO 527-2/50

拉伸模量
Tensile modulus MPa ISO 527-2/2

拉伸模量(23℃，4 mm，注塑成型)
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT Edgetek™ ET6500-5006 natural INNOMID® CS 6-9000 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL Edgetek™ ET6500-5006 natural INNOMID® CS 6-9000 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

电气性能
ELECTRICAL Edgetek™ ET6500-5006 natural INNOMID® CS 6-9000 单位
UNIT 测试方法
TEST METHOD

体积电阻率
Volume resistivity ohms·cm DIN 53482

相比漏电起痕指数(解决方案 A)
Compared to the leakage tracing index V IEC 60112

加工方式

注射 Edgetek™ ET6500-5006 natural INNOMID® CS 6-9000 单位测试方法

加工熔体温度 °C

干燥温度 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注射速度 Edgetek™ ET6500-5006 natural INNOMID® CS 6-9000 单位测试方法

备注

1 一般属性：这些不能被视为规格。

2 类型1A, 0.079 in/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
加工方式
注射
注射速度
备注
返回顶部

PA6+PO，Edgetek™ ET6500-5006 natural对比PA6+PO，INNOMID® CS 6-9000对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别