PBT，Ultradur® B 2300 G6 HR Unc.对比PBT，POCAN® B 3235 XF 000000物性表,价格行情_搜料

牌号信息	Ultradur® B 2300 G6 HR Unc. 物性表 PBT & 德国巴斯夫指导价格：暂无塑料库存：缺货	POCAN® B 3235 XF 000000 物性表 PBT & 德国恩骅力指导价格：暂无塑料库存：缺货
牌号简介	Ultradur® B 2300 G6 HR Unc.是一种抗水解，30%玻璃纤维增强PBT，显示优越的流动特性。设计用于提高汽车连接器的闩锁强度。应用程序Ultradur® B 2300 G6 HR Unc.是为薄壁汽车连接器开发的，设计用于满足USCAR三级要求。 Ultradur B 2300 G6 HR Unc. is a hydrolysis resistant, 30% fiberglass reinforced PBT, exhibiting superior flow characteristics. Designed for improved latch strength in automotive connectors. Applications Ultradur B 2300 G6 HR Unc. was developed for thin walled automotive connectors designed to meet USCAR Class III requirements.	Pocan B 3235 xF 000000 PBT，30%玻璃纤维，注塑成型，提高流动性 POCAN® B3235XF 000000 PBT, 30 % glass fibers, injection molding, improved flowability POCAN® B3235XF 000000 PBT, 30 % glass fibers, injection molding, improved flowability POCAN® B3235XF 000000 PBT, 30 % glass fibers, injection molding, improved flowability

产品描述
厂家：	德国巴斯夫 BASF	德国恩骅力 Envalior
类别：	PBT polybutylene terephthalate	PBT polybutylene terephthalate
填料：	玻璃纤维 30	玻璃纤维 30
用途：	连接器,汽车领域的应用
性能特点：	耐水解,易流动 Hydrolysis stability,Good liquidity	易流动,防火阻燃等级HB Good liquidity,HB
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Ultradur® B 2300 G6 HR Unc. POCAN® B 3235 XF 000000 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ISO 1183

收缩率(MD：150℃，2.0 mm，48 hrs)
Shrinkage rate % ISO 294-4

收缩率(MD：260℃，2.0 mm)
Shrinkage rate % ISO 294-4

收缩率(TD：150℃ ，2.0 mm，48 hrs)
Shrinkage rate % ISO 294-4

收缩率(TD：260℃，2.0 mm)
Shrinkage rate % ISO 294-4

熔体体积流动速率(260℃，2.16 kg)
Melt Volume Rate cm³/10min ISO 1133

粘度值(降低的粘度)
Viscosity value ml/g ISO 1628

表观密度
Apparent density g/cm³ ISO 60

机械性能
MECHANICAL Ultradur® B 2300 G6 HR Unc. POCAN® B 3235 XF 000000 单位
UNIT 测试方法
TEST METHOD

弯曲应变
Bending strain %

弯曲强度(23℃)
bending strength MPa ISO 178

弯曲模量(23℃)
Bending modulus MPa ISO 178

弯曲模量(23℃)
Bending modulus MPa ISO 178-A

拉伸应变(断裂，23℃)
Tensile strain % ISO 527-2

拉伸应变(断裂，23℃)
Tensile strain % ISO 527-2/5

拉伸强度(断裂，23℃)
tensile strength MPa ISO 527-2

拉伸强度(断裂，23℃)
tensile strength MPa ISO 527-2/5

拉伸模量(23℃)
Tensile modulus MPa ISO 527-1-2

球压硬度
Ball hardness MPa ISO 2039-1

冲击性能
IMPACT Ultradur® B 2300 G6 HR Unc. POCAN® B 3235 XF 000000 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL Ultradur® B 2300 G6 HR Unc. POCAN® B 3235 XF 000000 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(8.0 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/C

熔融温度
Melting temperature ℃ ISO 11357-3

熔融温度(DSC)
Melting temperature ℃ ISO 3146

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(MD：23~55℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(TD：23~55℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

电气性能
ELECTRICAL Ultradur® B 2300 G6 HR Unc. POCAN® B 3235 XF 000000 单位
UNIT 测试方法
TEST METHOD

相比漏电起痕指数
Compared to the leakage tracing index V IEC 60112

相比漏电起痕指数(解决方案 A)
Compared to the leakage tracing index V IEC 60112

阻燃性能
FLAMMABILITY Ultradur® B 2300 G6 HR Unc. POCAN® B 3235 XF 000000 单位
UNIT 测试方法
TEST METHOD

灼热丝可燃性指数(2.0 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

灼热丝起燃温度(2 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-13

阻燃等级
Flame retardant level ISO 3795

阻燃等级(0.75 mm)
Flame retardant level UL 94

阻燃等级(1.60 mm)
Flame retardant level UL 94

补充信息
Ultradur® B 2300 G6 HR Unc. POCAN® B 3235 XF 000000 单位
UNIT 测试方法
TEST METHOD

ISO Shortname
ISO Shortname ISO 7792

加工方式

注射 Ultradur® B 2300 G6 HR Unc. POCAN® B 3235 XF 000000 单位测试方法

Residual Moisture Content %

加工熔体温度 °C

干燥时间 hr

干燥时间 - 除湿干燥剂 hr

干燥温度 °C

干燥温度 - 除湿干燥剂 °C

建议的最大水分含量 %

模具温度 °C

注塑压力 MPa

注射速度

背压 MPa

备注

1 一般属性：这些不能被视为规格。

2 60x60x2; MT 80°C; 600 Bar

3 60x60x2mm, 80°C MT, 600 bar

4 60x60x2mm

5 60x60x2

6 0.079 in/min

7 Pull Rate: 2 mm/min; 50% RH

8 2 mm/min

9 10°C/min

10 US-FMVSS302


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
补充信息
加工方式
注射
备注
返回顶部