PC，LEXAN™ Copolymer 943X对比PC，LEXAN™ EXL9330P resin物性表,价格行情_搜料

牌号信息	LEXAN™ Copolymer 943X 物性表 PC & 沙特沙伯基础指导价格：暂无塑料库存：缺货	LEXAN™ EXL9330P resin 物性表 PC & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	LEXAN943X是一款紫外线稳定介质流动冲击改性注塑（IM）级产品。该树脂提供基于无溴、无氯阻燃系统的UL94 V0@1.5毫米阻燃性能、低温延展性和良好的加工性能，与标准PC相比，具有更短的IM循环时间。Lexan 943x树脂是一种可用于各种不透明颜色的产品，可能是一种很好的候选材料。R用途广泛。 LEXAN 943X is a UV stabilized medium flow impact modified injection molding (IM) grade. This resin offers UL94 V0 @ 1.5mm flame retardancy based on non-bromine, non-chlorine FR systems, low temperature ductility characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC. LEXAN 943X resin is a product available in a wide range of opaque colors and may be an excellent candidate for a wide range of applications.	不透明PC硅氧烷共聚物，加工性能优异。大多数颜色的无氯化、无溴阻燃产品。紫外线稳定。额定值F1/V-0/5VA。 Opaque PC-Siloxane copolymer with excellent processability. Non-chlorinated, non-brominated flame retardant product in most colors. UV-stabilized. UL rated f1/V-0/5VA.

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PC Polycarbonate	PC Polycarbonate
填料：
用途：	电子显示器,电气/电子应用领域,电器用具	电气/电子应用领域,电子显示器
性能特点：	耐候抗UV,易加工,冲击性能好,机械强度好-延展,成型周期快,无卤,阻燃,流动性中等 Weather resistance is good,Excellent Processability,High impact resistance,Ductility,Quick molding cycle,Halogen free,Flame Characteristics,Moderate liquidity	耐候抗UV,易加工,无卤,阻燃,共聚物,防火阻燃等级V-1,防火阻燃等级V-0,防火阻燃等级5VA耐候性 Weather resistance is good,Excellent Processability,Halogen free,Flame Characteristics,Copolymer,V-1,V-0,5VA
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LEXAN™ Copolymer 943X LEXAN™ EXL9330P resin 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate %

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate %

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度(--)
Density g/cm³ ASTM D792

密度(--)
Density g/cm³ ISO 1183

收缩率(MD：3.2 mm)
Shrinkage rate %

收缩率(MD：3.2 mm)
Shrinkage rate % 内部方法

收缩率(TD：3.2 mm)
Shrinkage rate %

收缩率(TD：3.2 mm)
Shrinkage rate % 内部方法

熔体体积流动速率(300℃，1.2 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(300℃，1.20kg)
Melt Flow Rate g/10min ASTM D1238

耐候性
Weathering resistance UL 746C

机械性能
MECHANICAL LEXAN™ Copolymer 943X LEXAN™ EXL9330P resin 单位
UNIT 测试方法
TEST METHOD

弯曲强度(--)
bending strength MPa ISO 178

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-1-2

球压硬度(H358/30)
Ball hardness MPa ISO 2039-1

冲击性能
IMPACT LEXAN™ Copolymer 943X LEXAN™ EXL9330P resin 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam ISO 180/1U

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam J/m 内部方法

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam ISO 180/1U

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-4A

悬臂梁缺口冲击强度(-50℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-4A

悬臂梁缺口冲击强度(23℃，6.4mm)
Impact strength of cantilever beam notch J/m ASTM D256

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength ISO 179/1eU

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LEXAN™ Copolymer 943X LEXAN™ EXL9330P resin 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，100 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Be

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，100 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Ae

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，6.4 mm)
Hot deformation temperature ℃ ASTM D648

球压测试(123~127℃)
Ball pressure test IEC 60695-10-2

球压测试(125℃)
Ball pressure test IEC 60695-10-2

相对温度指数(冲击机械性能)
Relative temperature index ℃ UL 746

相对温度指数(电气性能)
Relative temperature index ℃ UL 746

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(MD：23~80℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：23~80℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度(B120)
Vicat Softening Temp ℃ ASTM D1525 13 , ISO 306/B120 13

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

电气性能
ELECTRICAL LEXAN™ Copolymer 943X LEXAN™ EXL9330P resin 单位
UNIT 测试方法
TEST METHOD

介电常数(1 MHz)
Dielectric constant

介电常数(50 kHz)
Dielectric constant

介电常数(60 Hz)
Dielectric constant

介电强度(3.2 mm，在油中)
Dielectric strength kV/mm ASTM D149

介电强度(3.2 mm，在油中)
Dielectric strength kV/mm IEC 60243-1

体积电阻率
Volume resistivity ohms·cm IEC 60093

热丝引燃(HWI)
Hot wire ignition UL 746

相比漏电起痕指数
Compared to the leakage tracing index V IEC 60112

相比漏电起痕指数
Compared to the leakage tracing index UL 746

耗散因数(1 MHz)
Dissipation factor

耗散因数(1 MHz)
Dissipation factor ASTM D150 , IEC 60250

耗散因数(50 Hz)
Dissipation factor

耗散因数(50 Hz)
Dissipation factor ASTM D150

耗散因数(50 Hz)
Dissipation factor IEC 60250

耗散因数(60 Hz)
Dissipation factor

耗散因数(60 Hz)
Dissipation factor ASTM D150

耗散因数(60 Hz)
Dissipation factor IEC 60250

表面电阻率
Surface resistivity ohms IEC 60093

高电弧燃烧指数(HAI)
High Arc Burning Index (HAI) UL 746

阻燃性能
FLAMMABILITY LEXAN™ Copolymer 943X LEXAN™ EXL9330P resin 单位
UNIT 测试方法
TEST METHOD

极限氧指数
Extreme oxygen index % ISO 4589-2

灼热丝可燃性指数(1.0 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

灼热丝起燃温度(1 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-13

阻燃等级(0.80 mm)
Flame retardant level UL 94

阻燃等级(1.50 mm)
Flame retardant level

阻燃等级(1.50 mm)
Flame retardant level UL 94

阻燃等级(3.00 mm)
Flame retardant level

阻燃等级(3.00 mm)
Flame retardant level UL 94

加工方式

注射 LEXAN™ Copolymer 943X LEXAN™ EXL9330P resin 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥时间，最大 hr

干燥温度 °C

建议注射量 %

建议的最大水分含量 %

排气孔深度 mm

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

注射说明 LEXAN™ Copolymer 943X LEXAN™ EXL9330P resin 单位测试方法

建议注射量 LEXAN™ Copolymer 943X LEXAN™ EXL9330P resin 单位测试方法

加工熔体温度 °C

射嘴温度 °C

排气孔深度 mm

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

3. 50 mm/min

4. 类型 1, 50 mm/min

5. 1.3 mm/min

6. 2.0 mm/min

7. at Yield

8. 80*10*3 sp=62mm

9. 80*10*3 mm

10. 速率 A (50°C/h), 载荷2 (50N)

11. Surface

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 类型 1, 2.0 in/min

4 0.051 in/min

5 0.079 in/min

6 Yield

7 80*10*3 sp=62mm

8 80*10*3

9 63.5*12.7*3.2

10 Double-Gated

11 120*10*4 mm

12 标准 B (120°C/h), 载荷2 (50N)


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
加工方式
注射
注射说明
建议注射量
备注