| 牌号简介 About |
|---|
| 任务2和任务3低粘度、高性能的铸造树脂与我们常用的光滑铸造系列通用铸造树脂相比，具有优越的物理性能和性能。真空脱气是不必要的，他们提供了一个方便的1a:1b体积（120a:100b重量）混合比。任务2和任务3之间的区别在于使用寿命和拆卸时间。任务2和任务3为白色。它们具有较高的拉伸和弯曲强度，以及较高的弯曲模量。这些塑料是为各种工业应用制定的，包括模式制作和原型模型制作。这些树脂的设计厚度为1.27厘米（1.27厘米）。task plastics价格适中，提供试用套件、1加仑、5加仑、55加仑桶和手提包。 TASK® 2 & TASK® 3 low viscosity, high performance casting resins offer superior physical and performance properties compared to our popular Smooth-Cast® Series of general purpose casting resins. Vacuum degassing is not necessary and they offer the convenience of a 1A:1B by volume (115A:100B by weight) mix ratio. The difference between TASK® 2 & TASK® 3 is the pot life and demold time. TASK® 2 & TASK® 3 are white. They have high tensile and flexural strength, as well as high flexural modulus. These plastics were formulated for a variety of industrial applications including pattern making and making prototype models. These resins are designed for casting in thicknesses up to 1/2" (1.27 cm). TASK® Plastics are moderately priced and are available in trial kits, one-gallon, five-gallon, 55-gallon drum and totes. |
产品描述 Product Description
用途：成型材料;
颜色：白色
加工条件：浇铸 casting
性能特点： 拉伸性能好; 低粘度; Low Viscosity,Good Tensile Strength
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.12 | g/cm³ | ASTM D1475 |
|
特定体积 Specific volume |
0.892 | cm³/g | ASTM D1475 |
|
收缩率 Shrinkage rate |
|||
|
MD MD |
0.25 | % | ASTM D2566 |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
混合比 Mixing ratio |
1A:1B by volume 120A:100B by weight | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D Shaw's D |
80 | ASTM D2240 | |
|
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
|
弯曲强度 bending strength |
MPa | ASTM D790 | |
|
压缩模量 Compression modulus |
MPa | ASTM D695 | |
|
压缩强度 compressive strength |
MPa | ASTM D695 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
储存稳定性 storage stability |
|||
|
23℃ 23℃ |
min | ASTM D2471 | |
|
热固性混合粘度 Thermosetting mixed viscosity |
cP | ASTM D2393 | |
|
脱模时间 stripping time 2 |
|||
|
23℃ 23℃ 2 |
min | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Cure Time |
|
【新闻资讯】查看全部 
车灯、LED灯选材有何讲究
2017-10-18 材料导读：PC具有优异的冲击性和透明性，力学性能的电绝缘性能好，使用温度广泛，尺寸稳定性高， 耐蠕变性好，是应用于车灯和LED灯中最常见的材料。在车灯中，PC主要应用前照灯 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付