牌号简介 About |
---|
BMC 3001H成型化合物是一种矿物填充的玻璃纤维增强醇酸化合物,适用于压缩和转移成型。由于其流动性好,在冷激成型中也得到了广泛的应用。这是一种通用材料,具有良好的抗蠕变和电性能。典型应用包括刷握、调压器外壳和继电器底座。BMC 3001H模塑料是以各种工业颜色的挤压形式生产的。它可用于长度不超过12英寸的原木,或作为特定重量的预切段塞,直径为3/4“至2 7/8”。在这个范围内,较小的直径作为多个挤压件提供,重量公差为正负5%,最大为正负15克。 BMC 3001H molding compound is a mineral filled, glass-fiber reinforced alkyd compound suitable for compression and transfer molding. Because of its soft flow, it is also used extensively in cold spur molding. This is a general-purpose material with good creep resistance and electrical properties. Typical applications include brush holders, voltage regulator housings and relay bases. BMC 3001H molding compound is produced in extruded form in a range of industrial colors. It is available in logs up to 12 inches in length or as precut slugs, of specific weight, in diameters from ¾ " to 2 7/8 ". Within this range smaller diameters are supplied as multiple extrusions and weight tolerances are plus or minus 5% up to a maximum of of plus 15 grams. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
2.14 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD:模压成型 MD: Compression molding |
0.30 to 0.50 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.19 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
模压成型 Compression Molding |
160 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,模压成型 1.8 MPa, unannealed, molded |
260 | ℃ | ASTM D648 |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电强度 Dielectric strength 2 |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
60 Hz 60 Hz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
60 Hz 60 Hz |
ASTM D150 | ||
耐电弧性 Arc resistance |
sec | ASTM D495 | |
相比漏电起痕指数 Compared to the leakage tracing index |
V | UL 746 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
3.20 mm 3.20 mm |
UL 94 | ||
6.40 mm 6.40 mm |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
弯曲强度 bending strength |
|||
模压成型 Compression Molding |
MPa | ASTM D790 | |
压缩强度 compressive strength |
MPa | ASTM D695 | |
巴氏硬度 Babbitt hardness 2 |
ASTM D2583 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 方法A(短时间) |
【新闻资讯】查看全部
美国专家:再生行业曙光在前
2016-02-05 美国废弃物再生行业研究院(Institute of Scrap Recycling Industries Inc.)首席经济学家认为,备受油价等因素困扰的塑料再生行业的情况将会有所好转。 该机构总监Joe Pickard在美国新奥尔良召开的2016塑料再生会议上说,但要准确预测境况何时将会好转则是另外一回事。 他对再生业务的周期性质非常了解。油价降低给再生塑料行业带来了压力,因为再生树脂的价格通常按照原生树脂的折扣价出售。但这并不是导致行业如今举步维艰的唯一 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |