牌号简介 About |
---|
SAMAT 5003N(+)是以磷和氮为阻燃剂的无卤环保聚丙烯(PP)。混凝相和气相对阻燃效果的协同作用提高了阻燃效率,催化机理加速了体系的熔化和下降。可燃性可达到UL94-V2(0.75毫米、1.5毫米和3.0毫米),并在70°C下通过168h(UL746C)和GWIT 750°C和GWFI 960°的浸水试验。具有成品密度低、烟度低、对模具腐蚀小的特点。5003N(+)通过UL测试,符合RoHS、SVHC、PFOS和PFOA、16P、无卤和PAHS的要求。 5003N is halogen-free flame retardant environmental polypropylene with phosphorus and nitrogen as the flame retardant elements. Through synergistic effect of solidifying phase and gas-phase mechanism improve flame retardant performance, and accelerating melting and dripping by catalytic mechanism to play flame retardant perforamnce. 5003N flammability can reach UL94 V-2(1.5mm and 3.0mm), glow-wire test meets GWIT:750/3.0 and GWFI:850/3.0. 5003N has passed UL certification and meet the requirements of RoHS, SVHC, 17P, Halogen-free, PAHs...etc. 5003N has the characteristics of low density of finished products, low smoke, less corrosion to the mould etc. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.950 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
12 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
1.4 到 1.8 | % | ASTM D955 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
28.0 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
150 | % | ASTM D638 |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
|||
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
3 mm 3 mm |
℃ | IEC 60695-2-13 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Flammability after water-boiling testing at 70°C for 168 hours |
【新闻资讯】查看全部
新版外资准入负面清单发布:取消乘用车制造外资股比限制
2021-12-28 搜料网资讯: 经党中央、国务院同意,国家发展改革委、商务部于2021年12月27日发布第47号令和第48号令,分别发布了《外商投资准入特别管理措施(负面清单)(2021年版)》和《自由贸 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |