牌号简介 About |
---|
无增强聚酰胺PA66,中等粘度,热稳定,注塑成型,快速结晶,短周期。 TECHNYL® A 222 Black is an unfilled polyamide 66, heat stabilized, medium viscosity, for injection moulding, fast crystallization, for short cycles. This grade offers a good combination between primary properties of the unreinforced polyamide 66 and processing properties leading to increased productivity. These performances are associated with excellent dimensional stability and good rigidity of moulded parts. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.14 | g/cm³ | ISO 1183/A |
吸水率 Water absorption rate |
|||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
2.9 | % | ISO 62 |
23℃,24hr 23℃,24hr |
1.1 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
3700 | MPa | ISO 527-2/1A |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
80.0 | MPa | ISO 527-2/1A |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
ISO 179/1eU | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
kJ/m² | ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/Af | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/Bf | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
2 mm 2 mm |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
IEC 60112 | ||
解决方案 A Solution A |
V | IEC 60112 | |
解决方案 B Solution B |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.60 mm 1.60 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
|||
1.6 mm 1.6 mm |
℃ | IEC 60695-2-12 | |
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
拜耳660亿美元收购获孟山都股东批准 还需反垄断审查
2016-12-15 美国种子公司巨头孟山都(Monsanto)当地时间12月13日发布官网声明,股东们已经批准德国拜耳(Bayer)公司并购孟山都。 这次股东特别大会以99%的赞同票达成以每股128美元,共计660亿美元的价格将孟山都并入拜耳的决议。交易的截止窗口是2017年年底。 但拜耳和孟山都能否成功“合体”为全球最大的种子和农用化学品公司,还需要过美国政府这一关。美国司法部联邦贸易委员会将基于反垄断法,对该并购案的合法性进行裁决。 孟山都首席执行官Hugh |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |