| 牌号简介 About |
|---|
| SABIC® LLDPE PCG61是一种己烯线性低密度聚乙烯，通常用于医疗保健。用这种树脂制成的薄膜具有良好的机械、光学和热粘性能。SABIC® LLDPE PCG61的典型应用是要求具有良好冲击强度、抗撕裂性、光学性能和热粘性能的药膜、袋和袋。符合法规SABIC® LLDPE PCG6118NE符合欧洲药典（EP）和美国药典（USPVI）的相关专著。 SABIC® LLDPE PCG61 is a hexene-linear low density polyethylene typically used for healthcare applications. Films made from this resin exhibit good mechanical, optical and hottack properties. Application Typical application for SABIC® LLDPE PCG61 are pharmaceutical films, bags and pouches requiring good impact strength, tear resistance, optical performance and hottack properties. Compliance to Regulations SABIC® LLDPE PCG6118NE complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI). |
产品描述 Product Description
用途：医疗/护理用品;薄膜;药物;袋子;
性能特点： 机械强度好-撕裂; 抗氧化; 己烯共聚单体; 冲击性能好; 光学性能; 低密度; High impact resistance,Optical performance,Inoxidizability,Low density,Good tear strength,Hexene copolymers
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.918 | g/cm³ | ISO 1183/A |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
0.90 | g/10min | ISO 1133 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
50 | µm | |
|
拉伸模量 Tensile modulus |
ISO 527-3 | ||
|
MD，50 µm，吹塑薄膜 MD, 50 µ m, blow molded film |
190 | MPa | |
|
TD，50 µm，吹塑薄膜 TD, 50 µ m, blow molded film |
230 | MPa | |
|
拉伸强度 tensile strength |
ISO 527-3 | ||
|
MD，屈服，50 µm，吹塑薄膜 MD, yield, 50 µ m, blow molded film |
MPa | ||
|
TD，屈服，50 µm，吹塑薄膜 TD, yield, 50 µ m, blow molded film |
MPa | ||
|
MD，断裂，50 µm，吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
MPa | ||
|
TD，断裂，50 µm，吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
MPa | ||
|
拉伸应变 Tensile strain |
ISO 527-3 | ||
|
MD，断裂，50 µm，吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
% | ||
|
TD，断裂，50 µm，吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
% | ||
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁冲击强度 Izod notched impact strength |
|||
|
50µm,吹塑成型 50 µ m, blow molded |
J/cm | ASTM D4272 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
|
熔融温度 Melting temperature |
|||
|
DSC DSC |
℃ | 内部方法 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
45°，吹塑薄膜 45 °, blow molded film |
ASTM D2457 | ||
|
雾度 Haze |
|||
|
吹塑薄膜 Blown film |
% | ASTM D1003A | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
抗穿刺性 Puncture resistance |
|||
|
吹塑薄膜，50.0 µm Blow molded film, 50.0 µ m |
J/m | 内部方法 | |
|
撕裂强度 tear strength 1 |
ISO 6383-2 | ||
|
MD，50 µm MD，50 µm |
kN/m | ||
|
TD，50 µm TD，50 µm |
kN/m | ||
|
memo_intro memo_intro |
|||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Blown Film |
|
【新闻资讯】查看全部 
保时捷公布新计划 或将单独研发高性能电动车用动力电池
2021-04-07 搜料网资讯： 从外媒获悉，保时捷已经与电池初创企业Custom Cells合作，一同建立了合资企业Cellforce来研发与生产保时捷的高性能动力电池。 保时捷的研发总监称，电动化车型的需求量逐 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付