XH-03A氯化聚乙烯(CPE)复合65°C重阻燃橡胶护套产品特点:我公司可通过多次试验和试验生产XH-03A CPE护套材料。经连续固化后,该橡胶电缆护套的各项性能均能达到并超过GB7594.5标准。主要用途:该产品可用于制造重型电缆护套,其导线允许工作温度可长期保持在65。它具有优良的韧性、耐油性、耐热性、耐臭氧性和优良的阻燃性,也能完全替代CR橡胶化合物。制造的电缆,特别适合长期恶劣的工作条件。我公司生产的红、黄矿质电缆护套材料符合GB12972-91标准。 XH-03A CHLORINATED POLYETHYLENE (CPE) COMPOUND FOR 65°C HEAVY FLAME-RESISTANT RUBBER JACKET PRODUCT FEATURES: Our company can manufacture XH-03A CPE jacket material through many experiments and tests. After continuous curing, all properties of this rubber cable jacket can meet and surpass the Standard No. GB7594.5. MAIN APPLICATION: This product can be used to manufacture heavy cable jacket which its conductor allowable work-temperature can stay at 65 for a long trem. It has excellent tenacity, oil-resistance, heat-resistance, ozone resistance and fine flame resistance, it also can subsititute CR rubber compound completely. The manufactured cable, particularly suitable for the long-term poor working conditions. Our red and yellow mineral cable jacket material can satisfy the Standard No. GB12972-91. |
技术参数 Technical Data | |||
---|---|---|---|
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
|||
断裂 fracture 2 |
> 11.0 | MPa | |
拉伸应变 Tensile strain |
|||
断裂 fracture 2 |
> 300 | % | |
断裂 fracture 3 |
> 250 | % | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度的变化率 The rate of change in tensile strength |
|||
75℃,240 hr,in Air oven 75℃,240 hr,in Air oven |
-15 到 15 | % | |
100℃,24 hr,在IRM 902油中 100 ℃, 24 hours, in IRM 902 oil |
-40 到 40 | % | |
断裂时拉伸应力变化 Changes in tensile stress during fracture |
|||
75℃,240 hr,in Air oven 75℃,240 hr,in Air oven |
% | ||
100℃,24 hr,在IRM 902油中 100 ℃, 24 hours, in IRM 902 oil |
% | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
极限氧指数 Extreme oxygen index |
% |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Before ageing test |
3 After Oven ageing test |
【新闻资讯】查看全部
中国建材集团自主研发的T800级碳纤维完成千吨级量产
2018-01-17 目前,中国建材集团自主研发的T800级碳纤维已经实现千吨级量产,T1000级碳纤维在百吨线上试验成功,下一步要实现千吨级量产。 中国建材集团党委书记、董事长宋志平介绍,碳纤维是一种含碳量在90%以上的高强度/高模量的新型纤维材料,是国家安全、武器装备亟须的关键战略物资,是国外长期技术封锁和产品垄断的敏感材料,同时又兼备纺织纤维的柔软可加工性,是新一代增强纤维。 十多年来,中国建材集团将碳纤维的发展纳入集团培育新材料的战略规划中,持续提供资金、技术、管理、人才 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |