| 牌号简介 About |
|---|
| 符合ISO 1043-1的材料规范：PA66热稳定尼龙66，由50%重量的长玻璃纤维加固。球是圆柱形的，通常还有11毫米长的嵌入纤维。Celstran成型件具有高强度、高刚度、高热变形等优异的力学性能。由于部件中内置了纤维骨架，因此在高温和低温下缺口冲击强度会增加。长纤维增强能显著降低蠕变。模制品的各向同性收缩使翘曲最小化。通过注射成型，可以制造出具有高再现性的复杂零件。可代替压铸金属，重量轻，无腐蚀问题，无后处理。 Material code according to ISO 1043-1: PA66 Heat stabilized Nylon 66 reinforced by 50 weight percent long glass fibers. The pellets are cylindrical and normally as well as the embedded fibers 11 mm long. Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly. The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding. Can be used for substituting die cast metal with the advantage of Weight reduction, no corrosion problems, no post treatment. |
产品描述 Product Description
性能特点： 热稳定性好; 机械强度好; 耐低温冲击; 韧性好; Good Rigidity,Good flexibility,low-temperature impact resistance,Heat Stabilized
填料：玻璃纤维 50
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.57 | g/cm³ | ISO 1183 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
|||
|
-- -- |
16800 | MPa | ISO 527-2/1A/1 |
|
80℃ 80℃ |
10000 | MPa | ISO 527-2/1A |
|
拉伸强度 tensile strength |
|||
|
断裂 fracture |
220 | MPa | ISO 527-2/1A/5 |
|
80℃ 80℃ |
140 | MPa | ISO 527-2/1A |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ISO 527-2/1A/5 | |
|
断裂，80℃ Fracture, 80 ℃ |
% | ISO 527-2/1A | |
|
弯曲模量 Bending modulus |
ISO 178 | ||
|
23℃ 23℃ |
MPa | ISO 178 | |
|
80℃ 80℃ |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
ISO 178 | ||
|
23℃ 23℃ |
MPa | ISO 178 | |
|
80℃ 80℃ |
MPa | ISO 178 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
|
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
|
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
|
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
ISO 180/1U | ||
|
-30℃ -30℃ |
kJ/m² | ISO 180/1U | |
|
23℃ 23℃ |
kJ/m² | ISO 180/1U | |
|
多轴向仪器化冲击能量 Multi axial instrumented impact energy |
|||
|
-30℃ -30℃ |
J | ISO 6603-2 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
8.0 MPa，未退火 8.0 MPa, unannealed |
℃ | ISO 75-2/C | |
|
熔融温度 Melting temperature 2 |
℃ | ISO 11357-3 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 10°C/min |
|
【新闻资讯】查看全部 
万华化学：3月份中国地区纯MDI挂牌价上调
2022-02-28 万华化学公告，自2022年3月份开始，万华化学集团股份有限公司中国地区聚合MDI挂牌价22800元/吨（同2月份相比没有变动）；纯MDI挂牌价26800元/吨（比2月份价格上调3000元/吨）。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付