牌号简介 About |
---|
天然化合物是一种高分子量的己烯共聚物,特别适合于管材的挤出。由于其他良好的机械性能及其特性,聚乙烯天然化合物Alcudia TR-135被设计用于生产管道。它具有足够的抗氧化包装,适合于挤压工艺。本产品为天然色,但使用干燥着色或色母粒技术,在加工温度下稳定的颜料可以很容易着色。阿尔库迪亚TR-135是一种中等密度聚乙烯级高分子量己烯共聚物,特别适用于薄膜挤出。该材料易于加工成具有优良机械性能、良好密封性能和高应力抗裂性的薄膜。它含有抗氧化添加剂。典型应用:运输袋。垃圾袋。防水板。推荐的熔化温度范围为190至220°C。应优化每个生产线的加工条件。 ALCUDIA® TR-135 natural compound is an hexene copolymer of high molecular weight especially apt for the extrusion of pipe. Because other good mechanical properties and their characteristics, the polyethylene natural compound ALCUDIA® TR-135, is designed to produce pipe. It has the antioxidant package enough for the extrusion process. This product is supplied in natural colour but they can be easily coloured with pigments steady at processing temperature, using dry-colouring or masterbatch techniques. ALCUDIA® TR-135 is a medium density polyethylene grade, high molecular weight hexene copolymer, especially intended for film extrusion. This material offers easy processability into films with excellent mechanical properties, good sealing characteristics and high stress crack resistance. It contains antioxidant additives. TYPICAL APPLICATIONS Carrier bags. Refuse sacks. Waterproof sheets. Recommended melt temperature range from 190 to 220°C. Processing conditions should be optimised for each production line. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.938 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
190℃,2.16kg 190℃,2.16kg |
0.12 | g/10min | ISO 1133 |
190℃,21.6kg 190℃,21.6kg |
12 | g/10min | ISO 1133 |
190℃,5.0kg 190℃,5.0kg |
0.60 | g/10min | ISO 1133 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
10%乳化剂,F50 10% emulsifier, F50 |
> 4000 | hr | ASTM D1693 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
µm | ||
拉伸强度 tensile strength |
ISO 527-3 | ||
断裂 fracture |
MPa | ASTM D638 | |
屈服 yield |
MPa | ASTM D638 | |
MD,屈服,1500 µm,吹塑薄膜 MD, yield, 1500 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,屈服,1500 µm,吹塑薄膜 TD, yield, 1500 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,1500 µm,吹塑薄膜 MD, 1500 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,1500 µm,吹塑薄膜 TD, 1500 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
断裂 fracture |
% | ASTM D638 | |
屈服 yield |
% | ASTM D638 | |
MD,断裂,1500 µm,铸造薄膜 MD, fracture, 1500 µ m, cast thin film |
% | ISO 527-3 | |
TD,断裂,1500 µm,铸造薄膜 TD, fracture, 1500 µ m, cast thin film |
% | ISO 527-3 | |
落锤冲击 Drop hammer impact |
|||
20 µm,吹塑薄膜 20 µ m, blow molded film |
g | ISO 7765-1 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ISO 6383-2 | ||
MD:20 µm,吹塑薄膜 MD: 20 µ m, blow molded film |
N | ISO 6383-2 | |
TD:20 µm,吹塑薄膜 TD: 20 µ m, blow molded film |
N | ISO 6383-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 2 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 速率 A (50°C/h) |
【新闻资讯】查看全部
齐鲁石化紧盯市场行情,加快推进树脂新产品研发生产
2020-12-24 搜料网资讯: 12月初,齐鲁石化研发的高光泽聚丙烯新产品在国内知名家电企业实现批量使用。该产品光泽度高、刚韧性能强,成功应用于家电、童车、高端日用品等领域,有效替代进 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |