牌号简介 About |
---|
作为电子包装的一种低应力替代品,Nusil Technology的硅树脂允许设计师从一系列独特的硅树脂中选择不同级别的包装。我们有广泛的封装材料、粘合剂和润滑脂可供选择。这些包括用于热界面材料(TIM)或EMI和RFI屏蔽应用的热传导和导电硅酮。电子用硅酮的好处:宽工作温度范围为-115°C至250°C,低吸水率,<0.4%典型耐腐蚀性,高介电强度>500 V/mil(0.001英寸)或20 kV/mm填料,可提供低模量(通常小于5.5 MPa/800 psi)的热传导性能稳定。e暴露于高温下时的化学和机械性能,如凝胶、弹性体、薄膜粘合剂、片材和润滑脂,一般用途:灌封和封装材料评论:1.43折射率 As a low stress alternative for electronic packaging, NuSil Technology's silicones allow the designer to choose from a unique line of silicones for various levels of packaging. We have an extensive line of encapsulants, adhesives, and greases to choose from. These include thermally and electrically conductive silicones for Thermal Interface Materials (TIM) or for EMI and RFI shielding applications. Benefits of Silicone for Electronics: Wide Operating Temperature Range of -115 °C to 250 °C Low moisture absorption, < 0.4% Typical Corrosion Resistance High Dielectric Strength > 500 V/mil (0.001 inch) or 20 kV/mm Fillers can be added to provide thermal and electrical conductive properties Low Modulus (Typically less than 5.5 MPa/800 psi) Stable chemical and mechanical properties when exposed to high temperatures Low Shrinkage Available as gels, elastomers, film adhesives sheeting, and greases General Purpose: Potting and Encapsulating Materials Comments: 1.43 Refractive Index |
技术参数 Technical Data | |||
---|---|---|---|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
1.0E+15 | ohms·cm | ASTM D257 |
介电强度 Dielectric strength |
22 | kV/mm | ASTM D149 |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
1.430 | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Cure System Cure System |
Platinum | ||
离子含量 Ion content |
|||
Cl Cl |
< 5 | ppm | |
K K |
ppm | ||
Na Na |
ppm | ||
工作温度 working temperature |
℃ | ||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
颜色 colour |
|||
密度 Density |
g/cm³ | ||
粘度 viscosity 2 |
Pa·s | ||
固化时间 Curing time |
|||
65℃ 65℃ |
hr | ||
Cured Properties Cured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
|||
搭接剪切强度 lap shear strength 3 |
MPa | ||
拉伸强度 tensile strength |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ||
热固组件 Thermosetting components |
|||
部件 A Component A |
|||
部件 B Component B |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Part A |
3 Primed with CF1-135 |
【新闻资讯】查看全部
阻燃还减薄!SABIC共聚树脂助力Realme新款手机
2021-07-01 搜料网资讯: 国际电工委员会(the Int er nationalElectrotechni cal Commission)颁布实施全新的消费电子产品IEC 62368-1 安全标准,促使许多制造商寻求性能更高的阻燃(FR)材料。 中国领先智能 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |