牌号简介 About |
---|
尼龙是第一种工程树脂。它已被应用于从电子、海洋和汽车工业到用于制造地毯的纤维。尼龙具有优异的耐磨性和低摩擦性能。它具有很好的温度、化学和冲击性能。然而,尼龙的一个缺点是容易吸收水分,因此尺寸稳定性差。Tecamid具有优良的性能平衡,使其成为汽车零件、工业阀门、铁路连接绝缘体和其他工业用途(其设计要求包括高强度、韧性和重量减轻)中金属替换的理想材料。6/6型尼龙。热稳定尼龙。增强了承受热暴露负面影响的能力,并提高了Tecamid 6/6的整体工作温度。Tecamid 6/6型6/6通用标准级尼龙。天然和黑色挤压。(也可定制耐候黑色等级。)Tecamid 6/12 6/12型尼龙。与尼龙6/6相比,这种尼龙的吸湿率更低,因此尺寸稳定性更好。Tecamid ST 6/6型尼龙。超硬尼龙。在Tecamid 6/6上增加了抗冲击性和韧性。Tecamid 6/6型尼龙。热稳定尼龙。增强了承受热暴露负面影响的能力,并提高了Tecamid 6/6的整体工作温度。 Nylon was the first engineering resin. It has been used in applications ranging from electronic, marine, and automotive industries to fibers used to make carpet. Nylon has outstanding wear resistance and low frictional properties. It has very good temperature, chemical, and impact properties. However, nylon's one weakness is a propensity to absorb moisture and thus have poor dimensional stability. TECAMID® has an excellent balance of properties which make it an ideal material for metal replacement in applications such as automotive parts, industrial valves, railway tie insulators, and other industry uses whose design requirements include high strength, toughness, and weight reduction. Type 6/6 nylon. Heat Stabilized nylon. Increased ability to withstand the negative effects of heat exposure and increased overall service temperature over Tecamid® 6/6. TECAMID™ 6/6 Type 6/6 general purpose standard grade nylon. Extruded in natural and black. (Weather Resistant Black Grade is also available as a custom.) TECAMID™ 6/12 Type 6/12 nylon. This nylon has lower moisture absorpton rates than nylon 6/6, hence superior dimensional stability. TECAMID™ ST Type 6/6 nylon. Super Tough nylon. Increased impact resistance and toughness over Tecamid™ 6/6. TECAMID™ HS Type 6/6 nylon. Heat Stabilized nylon. Increased ability to withstand the negative effects of heat exposure and increased overall service temperature over Tecamid™ 6/6. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.15 | g/cm³ | ASTM D792 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.28 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
2410 | MPa | ASTM D638 |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
68.9 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
25 | % | ASTM D638 |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ||
熔融温度 Melting temperature |
℃ | ASTM D2133 | |
使用温度 Operating temperature |
|||
长期 long-term |
℃ | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
0.75 mm 0.75 mm |
UL 94 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
全球最大尼龙66原液着色纤维生产基地在河南诞生
2021-09-29 搜料网资讯: 9月23日,在神马股份帘子布发展公司尼龙66原丝生产现场,本应该是白色的尼龙66纤维,变成了一缕缕黑丝,正在卷绕机上有序生产。据了解,这种黑色纤维不仅颜值高、性 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |