牌号简介 About |
---|
MALEX 01FN002 - 1343是一种低粘度聚碳酸酯(PC)树脂,含有一种释放剂,以确保易于加工,用于注塑成型。该产品有米色(MALEX 01FN002 - 1343)可供选择,但也可根据要求提供其他颜色。MALEX 01FN002 - 1343结合了高机械、热学和电性能以及优异的耐化学性和尺寸稳定性应用。MALEX 01FN002 - 1343适用于电气部件的注塑成型和包括内饰在内的汽车应用。以及电气和机械系统,如:电器部件仪表板部件照明系统 MALEX 01FN002 - 1343 is a low viscosity polycarbonate (PC) resin and contains a release agent to ensure easy processing, intended for injection moulding. The product is available in beige (MALEX 01FN002 - 1343 ) but other colours can be provided on request They combine high mechanical, thermal and electrical properties with excellent chemical resistance and dimensional stability APPLICATIONS MALEX 01FN002 - 1343 is intended for the injection moulding of electrical components and automotive applications including interior, and electrical and mechanical systems, such as: Electrical appliance components Dashboard components Lighting system |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
24 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD MD |
0.50 到 0.70 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
0.35 | % | DIN 53495 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
2350 | MPa | ISO 527-1-2 |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 2 |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
ISO 180/1U | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
球压测试 Ball pressure test |
|||
125℃ 125℃ |
IEC 60695-10-2 | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
0.8 mm,在油中 0.8 mm in oil |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
50 Hz 50 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
50 Hz 50 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耐电弧性 Arc resistance |
sec | ASTM D495 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
3.00 mm 3.00 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
|||
1.0 mm 1.0 mm |
℃ | IEC 60695-2-12 | |
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.079 in/min |
【新闻资讯】查看全部
未来10年海洋塑料比鱼还多 我们能做点儿什么
2017-12-12 未来10年,海洋塑料比鱼还多,我们能做点儿什么? 海洋占全球面积的70%,80%的生命生活在其中,她为人类提供了60%的氧气,吸收了大量的二氧化碳和全球90%的多余热量;目前全球海洋经济规模已是第七大经济体,到2030年前,规模将比目前增长3倍,创造1310万个就业机会。 另一方面,全球平均每年产生4800亿个塑料瓶,并且还以每年3%-4%的速度增长,未来10年内,海洋中的塑料可能比鱼还要多;2030年前,全球人口将达到85亿,鱼类食品安全将成为更大挑战。< |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |