牌号简介 About |
---|
TAISOX 2114是一种线性低密度聚乙烯材料,。 该产品在亚太地区、北美洲或欧洲有供货,加工方式为:吹塑薄膜。 TAISOX 2114的主要特性有: Antiblock 软件 滑动 耐冲击 良好的密封性能 良好的抗撕裂强度 TAISOX 2114的典型应用领域为:电影 TAISOX® 2114 is a Linear Low Density Polyethylene material. It is available in Asia Pacific, Europe, or North America for blown film. Important attributes of TAISOX® 2114 are: Antiblock Good Sealability Good Tear Strength High Strength Impact Resistant Typical application of TAISOX® 2114: Film |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.918 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.0 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
38 | µm | |
割线模量 Secant modulus |
ASTM D882 | ||
1% 正割,MD:38 µm,吹塑薄膜 1% secant, MD: 38 µ m, blow molded film |
157 | MPa | ASTM D882 |
1% 正割,TD:38 µm,吹塑薄膜 1% secant, TD: 38 µ m, blow molded film |
196 | MPa | ASTM D882 |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,38 µm,吹塑薄膜 MD, yield, 38 µ m, blow molded film |
MPa | ASTM D882 | |
TD,屈服,38 µm,吹塑薄膜 TD, yield, 38 µ m, blow molded film |
MPa | ASTM D882 | |
MD,断裂,38 µm,吹塑薄膜 MD, fracture, 38 µ m, blow molded film |
MPa | ASTM D882 | |
TD,断裂,38 µm,吹塑薄膜 TD, fracture, 38 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,38 µm,吹塑薄膜 MD, fracture, 38 µ m, blow molded film |
% | ASTM D882 | |
TD,断裂,38 µm,吹塑薄膜 TD, fracture, 38 µ m, blow molded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
38 µm,吹塑薄膜 38 µ m, blow molded film |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:38 µm,吹塑薄膜 MD: 38 µ m, blow molded film |
g | ASTM D1922 | |
TD:38 µm,吹塑薄膜 TD: 38 µ m, blow molded film |
g | ASTM D1922 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融温度 Melting temperature |
℃ | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,38 µm,吹塑薄膜 45 °, 38 µ m, blow molded film |
ASTM D2457 | ||
透明度 transparency |
ASTM D1746 | ||
雾度 Haze |
|||
38 µm,吹塑薄膜 38 µ m, blow molded film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
“2035年实现100%可再生能源供电”,德国激进步伐背后的隐忧
2022-03-02 欧洲火车头德国正率先加速能源转型。 2月28日德国经济部推出一份草案,计划加速风能和太阳能基础设施的扩张,将100%可再生能源供电目标提前至2035年实现。按照计划,陆上风力发电 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |