牌号简介 About |
---|
LNP™ STAT-KON™ KD000 compound 是一种基于缩醛树脂的化合物,含有专有填料。这种材料的另一个特点是:导电。再订购名称: KD000 LNP STAT-KON KD000 is a compound based on Acetal resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.45 | g/cm³ | ASTM D792 |
密度 Density |
1.45 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
|||
MD:60℃ MD:60℃ |
1.2 to 1.3 | % | 内部方法 |
MD:100℃ MD:100℃ |
1.5 to 1.6 | % | 内部方法 |
MD:24 hrs MD:24 hrs |
1.5 to 3.5 | % | ASTM D955 |
收缩率 Shrinkage rate |
|||
TD:60℃ TD:60℃ |
% | 内部方法 | |
TD:100℃ TD:100℃ |
% | 内部方法 | |
TD:24 hrs TD:24 hrs |
% | ASTM D955 | |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD:24 hrs TD:24 hrs |
% | ISO 294-4 | |
MD:24 hrs MD:24 hrs |
% | ISO 294-4 | |
吸水率 Water absorption rate |
|||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
24hr,50% RH 24hr,50% RH |
% | ASTM D570 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2 | |
屈服 yield |
MPa | ISO 527-2 | |
屈服 yield |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2 | |
断裂 fracture |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2 | |
屈服 yield |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D4812 | |
23℃ 23℃ 3 |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 3 |
|||
23℃ 23℃ 3 |
kJ/m² | ISO 180/1U | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Energy at Peak Load 23℃,Energy at Peak Load |
J | ASTM D3763 | |
多轴向仪器化冲击能量 Multi axial instrumented impact energy |
J | ISO 6603-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 4 |
℃ | ISO 75-2/Af | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ISO 11359-2 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ISO 11359-2 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM E831 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
0.70 mm 0.70 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 80*10*4 |
4 80*10*4 mm |
【新闻资讯】查看全部
ARBURG阿博格即将出席Chinaplas2021国际橡塑展
2021-03-25 搜料网资讯: 粤港澳大湾区是中国塑料制品至关重要的生产基地,全球领先的橡塑科技大展 -CHINAPLAS 国际橡塑展将落户大湾区的核心引擎 - 深圳,于2021年4月13 - 16日在深圳国际会展中心 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |