牌号简介 About |
---|
采用Unipol II工艺技术生产CONTINUUM™ DGDD-2480 NT双峰聚乙烯树脂。该产品可用于需要长期流体静强度和优异的抗缓慢裂纹扩展和快速裂纹扩展能力的管道应用。合适的应用包括天然气分配管道、工业管道、采矿、污水和市政供水管道。符合工业标准ASTM D 3350:电池分类自然-PE445574A黑色-PE445574C(见注释A)塑料管道协会(PPI):TR-4黑色管道-连续DGDD-2480 BK(见注释A)ASTM PE4710管道等级-1600psi HDB和1000psi HDS@73°F,以及1000psi HDB@140°F NSF国际:标准14和61黑色管道-DGDD-2480 BK(见注释A)有关完整的详细信息,请参考法规。注:(a)用炭黑母料DFNF-0092(6.5%)在适当条件下挤出的天然树脂。 CONTINUUM™ DGDD-2480 NT Bimodal Polyethylene Resin is produced using UNIPOL™ II process technology. This product may be utilized for pipe applications where long term hydrostatic strength combined with outstanding resistance to slow crack growth and rapid crack propagation are desired. Suitable applications include natural gas distribution pipes, industrial piping, mining, sewage, and municipal water service lines. Industrial Standards Compliance ASTM D 3350: cell classification Natural - PE445574A Black - PE445574C (See NOTES A) Plastics Pipe Institute (PPI): TR-4 Black Pipe - CONTINUUM DGDD-2480 BK (See NOTES A) ASTM PE4710 pipe grade - 1600psi HDB and 1000psi HDS @ 73°F, and 1000psi HDB @ 140°F NSF International: Standard 14 and 61 Black Pipe - DGDD-2480 BK (See NOTES A) Consult the regulations for complete details. NOTES: (A) Natural resin extruded under proper conditions with carbon black masterbatch DFNF-0092 (6.5%). |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
- - |
ASTM D1505 | ||
2 |
0.949 | g/cm³ | ASTM D1505 |
黑色 black 3 |
0.959 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
190℃,2.16kg 190℃,2.16kg |
0.080 | g/10min | ASTM D1238 |
190℃,21.6kg 190℃,21.6kg |
8.5 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 4 |
|||
屈服 yield 4 |
> 24.1 | MPa | ASTM D638 |
拉伸应变 Tensile strain 4 |
|||
断裂 fracture 4 |
% | ASTM D638 | |
弯曲模量 Bending modulus 5 , 4 |
MPa | ASTM D790B | |
抗快速裂缝扩展 Resistance to rapid crack propagation |
|||
Tc Tc 8 |
℃ | ISO 13477 | |
Pc Pc |
|||
Full Scale:0℃ Full Scale:0℃ 6 |
bar | ISO 13478 | |
S-4:0℃ S-4:0℃ 7 |
bar | ISO 13477 | |
裂纹缓慢扩展 PENT Slow crack propagation PENT 4 |
|||
@ 2.4 MPa,80℃ @ 2.4 MPa,80℃ 4 |
hr | ASTM F1473 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 4 |
|||
23℃ 23℃ 4 |
J/m | ASTM D256-A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature 4 |
℃ | ASTM D746A | |
热稳定性 thermal stability |
℃ | ASTM D3350 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 天然树脂 |
3 在使用炭黑母料 DFNF-0092 (6.5%) 的正常条件下挤压天然树脂。 |
4 根据 ASTM D 4703 程序 C 准备压缩模塑配件。属性将随着模塑条件和老化时间的变化而变化。 |
5 方法 I (三点负荷) |
6 Calculated value, determined by the equation in ISO 4437 based on S-4 test data. Pipe diameter of 10 inch IPS (25.4 cm) and Standard Diameter Ratio (SDR) 11. |
7 Pipe diameter of 10 inch IPS (25.4 cm) and Standard Diameter Ratio (SDR) 11. |
8 在使用炭黑母料 DFNF-0092 (6.5%) 的正常条件下挤压天然树脂。 管道直径为 10 英寸 IPS (25.4 cm),标准直径比 (SDR) 为 11。 |
【新闻资讯】查看全部
跨行业CEO联盟支持欧盟计划到2030年将碳排放量减少55%
2021-07-11 搜料网资讯: 随着欧盟委员会准备提交其Fit for 55立法方案,欧洲CEO联盟发布政策建议,支持逐步推动实现气候中和。该联盟在巴黎会议后宣布,应对气候变化需要公共部门和行业之间的 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |