牌号简介 About |
---|
Valox 815树脂15%Gr PBT+PET,表面光洁度极佳。典型应用是热风枪外壳组件、工业胶枪、电器外壳和手柄。Valox 815树脂Valox 815是一种15%玻璃增强PBT+PET混合物,具有良好的表面光洁度。应用:热风枪外壳组件,工业胶枪,电器外壳和手柄。Valox 815树脂15%Gr PBTP,表面光洁度极佳。典型应用是热风枪外壳组件、工业胶枪、电器外壳和手柄。 15% GR PBT+ PET, excellent surface finish. Typical applications are hot air gun housing assemblies, industrial glue guns, appliance housings and handles. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.43 | g/cm³ | ASTM D792 |
特定体积 Specific volume |
0.704 | cm³/g | ASTM D792 |
收缩率 Shrinkage rate |
Internal Method | ||
TD TD 3 |
0.50 to 0.80 | % | 内部方法 |
TD TD 4 |
0.80 to 1.1 | % | 内部方法 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.060 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D4812 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
ASTM E831 | ||
-40 到 40℃ -40 to 40 ℃ |
cm/cm/℃ | ASTM E831 | |
60 到 138℃ 60 to 138 ℃ |
cm/cm/℃ | ASTM E831 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
ASTM D149 | ||
1.6 mm,在油中 1.6 mm in oil |
kV/mm | ASTM D149 | |
3.2 mm,在空气中 3.2 mm in air |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
100 Hz 100 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
100 Hz 100 Hz |
ASTM D150 | ||
耐电弧性 Arc resistance 7 |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
高电压电弧起痕速率 High voltage arc marking rate |
|||
HVTR HVTR |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.50 mm 1.50 mm |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 5 |
|||
断裂 fracture 5 |
MPa | ASTM D638 | |
弯曲模量 Bending modulus 7 |
|||
50 mm跨距 50 mm span 7 |
MPa | ASTM D790 | |
弯曲强度 bending strength 6 |
|||
断裂,50 mm跨度 Fracture, 50 mm span 6 |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
特殊值 Special value |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
MD MD 2 |
% | 内部方法 | |
MD MD 3 |
% | 内部方法 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 1.5 to 3.2 mm |
3 3.2 to 4.6 mm |
4 Tensile Bar |
5 3.2-4.6 mm |
6 0,20 in/min |
7 类型 1, 0,20 in/min |
8 类型 1, 2,0 in/min |
9 0,051 in/min |
10 0,079 in/min |
11 Yield |
12 Break |
13 2 mm/min |
14 80*10*4 sp=62mm |
15 80*10*4 |
16 120*10*4 mm |
17 80*10*4 mm |
18 标准 B (120°C/h), 载荷2 (50N) |
19 速率 A (50°C/h), 载荷2 (50N) |
20 Short-Time |
21 钨电极 |
【新闻资讯】查看全部
安庆石化聚丙烯装置核心装置进入安装阶段
2022-07-26 7月19日,炼化工程集团第五建设公司承建的安庆石化炼油化工结构调整项目30万吨/年聚丙烯装置挤出造粒装置主减速器成功吊装就位,标志着该装置核心装置安装正式开工。 30万吨/年聚 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |