| 牌号简介 About |
|---|
| 产品说明：SABLC低密度聚乙烯HP4027J是一种低密度聚乙烯级产品，采用助滑剂和防堵塞添加剂配制而成，密度增加。它通常表现出良好的下拉能力和更高的输出。薄膜具有良好的光学性能、低摩擦、低阻塞和高刚性。典型应用：纺织包装用薄膜、高清晰度洗衣袋、面包袋、高速自动包装线用通用薄膜。该等级通常适用于需要更高刚度和向下测量的地方。本产品不适用于医疗和制药应用。 PRODUCT DESCRIPTION: SABlC® LDPE HP4027J is a Low Density Polyethylene grade formulated with slip agent and anti-block additives, with increased density. It typically exhibits excellent draw down ability with higher output. Films typically exhibit good optics, low friction, low blocking and high rigidity. TYPICAL APPLICATIONS: Thin film for textile packaging, high clarity laundry bags, bread bags, general purpose film for high speed automatic packaging lines. This grade is typically suitable where higher stiffness and down gauging are required. This product is not intended for use in medical and pharmaceutical applications. |
产品描述 Product Description
用途：薄膜;包装;袋子;洗衣袋;
加工条件：吹塑薄膜
性能特点： 抗结块性; 机械强度好; 高光滑性; 易剥离; 低摩擦系数; 食品接触; 光学性能; 低密度; Good Rigidity,Smoothness,Good dissection,Optical performance,Low coefficient of friction,High anti-blocking,Food contact compliance,Low density
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.927 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
4.0 | g/10min | ISO 1133 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
|||
|
0.05 mm 0.05 mm |
300 | MPa | ISO 527-2 |
|
摩擦系数 friction coefficient |
< 20 | % | ISO 8295 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
50 | µm | |
|
薄膜厚度 film thickness |
|||
|
拉伸强度 tensile strength |
ISO 527-3 | ||
|
屈服，0.05 mm Yield, 0.05 mm |
MPa | ISO 527-2 | |
|
MD，断裂，50 µm，吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
MPa | ISO 527-3 | |
|
TD，断裂，50 µm，吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
MPa | ISO 527-3 | |
|
拉伸应变 Tensile strain |
ISO 527-3 | ||
|
MD，断裂，50 µm，吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
% | ISO 527-3 | |
|
TD，断裂，50 µm，吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
% | ISO 527-3 | |
|
落锤冲击 Drop hammer impact |
|||
|
50 µm，吹塑薄膜 50 µ m, blow molded film |
g | ASTM D1709 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
维卡软化温度 Vicat Softening Temp |
|||
|
A50 A50 |
℃ | ISO 306/A50 | |
|
熔融温度 Melting temperature |
|||
|
DSC DSC |
℃ | ISO 3146 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
ASTM D2457 | ||
|
20°，50 µm，吹塑薄膜 20 °, 50 µ m, blow molded film |
ASTM D2457 | ||
|
60°，50.0 µm，吹塑薄膜 60 °, 50.0 µ m, blow molded film |
ASTM D2457 | ||
|
雾度 Haze |
|||
|
50 µm，吹塑薄膜 50 µ m, blow molded film |
% | ASTM D1003 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Blow（up Ratio） Blow（up Ratio） |
|||
| 备注 |
|---|
| 1 Natural Silica |
| 2 Erucamide |
| 3 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部 
中国回收企业方案斥资5200万美元建造美国工厂
2018-04-10 一家中国公司计划投资5200万美元在美国南卡罗来纳州建造一座无菌纸盒回收工厂，预计将在当地创造200个就业机会。 据政府官员介绍，漳州三利达环保科技有限公司将从美国进口材料，通过其下属公司美国利美公司南卡 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付