牌号简介 About |
---|
Styrolux® S是一种新开发的透明苯乙烯-丁二烯共聚物(SBC),专门设计用于与苯乙烯-T混合,以实现高性能薄膜挤出和收缩薄膜应用。由于Styrolux® S与Styrolux T混合,它增加了膜的刚度,提高了膜卷的存储稳定性(减少了自然收缩)。特点:高清晰度,高硬度,用于Styrolux T收缩套的混合组件,标签膜。 Styrolux® S is a new developmental, clear styrene-butadiene copolymer (SBC) designed specifically for blending with Styrolux® T in order to enable high performance film extrusion and shrink film applications. As Styrolux® S is blended with Styrolux® T it increases the stiffness of the film and improves the storage stability of film reels (reduced natural shrinkage). FEATURES Excellent clarity High stiffmess APPLICATIONS Blend component for Styrolux T Shrink sleeve applications Label film |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔体质量流动速率 Melt Flow Rate |
|||
200℃,5.0kg 200℃,5.0kg |
10 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
200℃,5 kg 200℃,5 kg |
11.0 | cm³/10min | ISO 1133 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
0.070 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
83 | ISO 868 | |
邵氏 D Shaw's D |
74 | ASTM D2240 | |
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
屈服,23℃ Yield, 23 ℃ |
% | ASTM D638 | |
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2 | |
标称拉伸断裂应变 Nominal tensile fracture strain |
|||
23℃ 23℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 2 | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
B50 B50 |
℃ | ISO 306 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
透光率 Transmittance |
|||
550 nm 550 nm |
% | ASTM D1003 | |
雾度 Haze |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 标准 B (120°C/h), 压 力1 (10N) |
【新闻资讯】查看全部
美媒:全球塑料垃圾美国造得最多
2020-11-25 搜料网资讯: 全球塑料污染日益严重,据德国《焦点周刊》21日报道,在过去几年,从北极一直到河流和深海,我们在全球各地收集的样本中都发现塑料微粒。如今连世界之巅珠穆朗玛 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |