牌号简介 About |
---|
KOPPS® S13A65BL是一种聚苯硫醚(PPS)产品,含有的填充物为65% 填料。 它,在亚太地区、北美洲、拉丁美洲或欧洲有供货。 特性包括: 阻燃/额定火焰 通过 ROHS 认证 耐热 良好的尺寸稳定性 高流动性 KOPPS® S13A65BL is a Polyphenylene Sulfide (PPS) product filled with 65% filler. It is available in Asia Pacific, Europe, Latin America, or North America. Characteristics include: Flame Rated RoHS Compliant Good Dimensional Stability Heat Resistant High Flow |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.95 | g/cm³ | ASTM D792 , ISO 1183 |
收缩率 Shrinkage rate |
|||
MD MD |
0.20 | % | ASTM D955 |
TD TD |
1.0 | % | ISO 294-4 |
MD MD |
0.23 | % | ISO 294-4 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.020 | % | ISO 62 |
平衡,23℃,60% RH Equilibrium, 23 ℃, 60% RH |
% | ASTM D570 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,6.35 mm 1.8 MPa, unannealed, 6.35 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 , ASTM D3418 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
1 MHz 1 MHz |
ASTM D150 | ||
耐电弧性 Arc resistance |
sec | ASTM D495 | |
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
0.80 mm 0.80 mm |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
R 级 R-level |
ISO 2039-2 | ||
拉伸强度 tensile strength |
|||
23℃ 23℃ |
MPa | ASTM D638 | |
23℃ 23℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
23℃ 23℃ |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
23℃ 23℃ |
MPa | ISO 178 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
原材料涨价背后:中小企业直呼“不敢接单” 上市公司表示“优化库存
2021-10-12 搜料网资讯: 电影名:《涨价》 ;导演:袁材料;领衔主演:木头、钢材、海绵、纸箱等;上映档期:2021年10月份。 如上是河北省定州市一家家装公司负责人在国庆假期期间发布的朋 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |