牌号简介 About |
---|
HANWHA EVA 1815采用高压高压釜工艺生产,适用于各种电线电缆化合物(如半导电化合物、阻燃化合物)的基树脂。EVA 1815以其优良的加工性能、填料的可装载性和高质量保证而闻名。 HANWHA EVA 1815 is manufactured by high pressure autoclave process and designed for base resin of variety of wire & cable compounds such as semi-conductive compound, flame retardant compound. EVA 1815 is well known for its excellent processability, filler loadability and high quality assurance. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.936 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
6.0 | g/10min | ASTM D1238 |
醋酸乙烯含量 Vinyl acetate content |
15.0 | wt% | 内部方法 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
< -76.0 | ℃ | ASTM D746 |
维卡软化温度 Vicat Softening Temp |
66.0 | ℃ | ASTM D1525 |
熔融温度 Melting temperature |
℃ | ASTM D3417 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
加工温度 Processing temperature |
|||
Kneader Kneader |
℃ | ||
Roll Mill Roll Mill |
℃ | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,1 秒 Shore A, 1 second |
ASTM D2240 | ||
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
拙劣打造塑料产业互联网平台型总部经济
2017-06-16 作为中国合成革产业基地,高明区昨日举行“众塑联”产业平台发起人签约仪式,来自蓝源资本、万方、高明塑协等27家企业参与抱团发展。 这是高明区推进塑料行业供给侧结构性改革的一次探索。高明区将借助蓝源资本的顶层设计,联合高明塑料企业集群,全面整合全国塑料行业资源,打造中国塑料产业互联网平台型总部经济。 强强联合打造“众塑联”产业平台 金融资本顶层设计,产业资本合伙参与,人力资本持股执行……昨日上午,作为“众塑联”产业平台发起人,27家企业负责人齐聚 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |