| 牌号简介 About |
|---|
| LL5400S是一种线性低密度聚乙烯，开发用于与聚乙烯混合的吹塑薄膜挤出。用该产品制备的薄膜具有良好的加工性能，具有良好的光学、机械性能和密封性。非常低的凝胶量。它含有抗氧化添加剂。用途：衬里；一般用途的低密度聚乙烯和高密度聚乙烯混合物和包装。其他应用：灌溉管道的混合物。工艺：薄膜挤出的推荐工艺条件约为170-210°C。最佳工艺条件将根据所用设备的类型而变化，不能作为性能保证。 LL5400S is a Linear Low Density Polyethylene developed for blown film extrusion in blends with polyethylenes. Films obtained with this product show a good processing performance balanced with good optical and mechanical properties as well as sealability. Very low gel amount. It contains antioxidant additives. Applications: Liners; LDPE and HDPE blends and packages for general use. Others applications: blends for irrigation pipes. Process: Recommended processing conditions for film extrusion about 170 - 210 °C. The optimum processing conditions will vary according to the type of equipment used and cannot be considered as performance guarantee. |
产品描述 Product Description
用途：薄膜;衬里;包装;吹膜;混合;管道系统;
加工条件：吹塑薄膜
性能特点： 低速凝固晶点; 抗氧化; 光学性能; 易加工; Excellent Processability,Optical performance,Low speed solidification point,Inoxidizability
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.918 | g/cm³ | ASTM D1505 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
1.0 | g/10min | ASTM D1238 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
ASTM D882 | ||
|
MD，断裂，38 µm，吹塑薄膜 MD, fracture, 38 µ m, blow molded film |
40.0 | MPa | ASTM D882 |
|
TD，断裂，38 µm，吹塑薄膜 TD, fracture, 38 µ m, blow molded film |
30.0 | MPa | ASTM D882 |
|
拉伸应变 Tensile strain |
ASTM D882 | ||
|
MD，断裂，38 µm，吹塑薄膜 MD, fracture, 38 µ m, blow molded film |
1100 | % | ASTM D882 |
|
TD，断裂，38 µm，吹塑薄膜 TD, fracture, 38 µ m, blow molded film |
% | ASTM D882 | |
|
弯曲模量 Bending modulus |
ASTM D790 | ||
|
1% 正割，MD，38 µm，吹塑薄膜 1% secant, MD, 38 µ m, blow molded film |
MPa | ASTM D790 | |
|
1% 正割，TD，38 µm，吹塑薄膜 1% secant, TD, 38 µ m, blow molded film |
MPa | ASTM D790 | |
|
落锤冲击 Drop hammer impact |
|||
|
38 µm，吹塑薄膜 38 µ m, blow molded film |
g | ASTM D1709 | |
|
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
|
MD：38 µm，吹塑薄膜 MD: 38 µ m, blow molded film |
g | ASTM D1922 | |
|
TD：38 µm，吹塑薄膜 TD: 38 µ m, blow molded film |
g | ASTM D1922 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
60°，38.0 µm，吹塑薄膜 60 °, 38.0 µ m, blow molded film |
ASTM D2457 | ||
|
雾度 Haze |
|||
|
38 µm，吹塑薄膜 38 µ m, blow molded film |
% | ASTM D1003 | |
| 备注 | |||
|---|---|---|---|
| 暂无数据 | |||
|
【新闻资讯】查看全部 
日本酸素增强乙硼烷产能
2021-12-19 搜料网资讯： 近日，日本酸素控股株式会社宣布，该公司决定到2023年提高其在日本的电子材料气体乙硼烷的产能，使工厂产能翻番，并在2023年前在韩国和中国工厂新建乙硼烷生产线。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付