| 牌号简介 About |
|---|
| 符合ISO 1043-1的材料规范：聚丙烯，纤维含量为60%，长玻璃纤维增强。纤维与聚丙烯基体发生化学耦合。球是圆柱形的，通常也包括10 mm长的嵌入纤维。Celstran成型件具有高强度、高刚度、高热变形等优异的力学性能。由于部件中内置了纤维骨架，因此在高温和低温下缺口冲击强度会增加。长纤维增强能显著降低蠕变。模制品的各向同性收缩使翘曲最小化。通过注射成型，可以制造出具有高再现性的复杂零件。应用领域：汽车功能/结构件 Material code according to ISO 1043-1: PP Polypropylene with 60 weight percent fiber content, long glass fibers reinforced. The fibers are chemically coupled to the polypropylene matrix. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long. Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly. The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding. Application field: Functional/structural parts for automotive |
产品描述 Product Description
用途：汽车领域的应用;
加工条件：注射成型 Injection Molding
性能特点： 化学耦合; 机械强度好; 耐低温冲击; 各向同性好; 低翘曲性; 韧性好; Good Rigidity,Low warping,Good flexibility,Chemical coupling,low-temperature impact resistance,Good Isotropy
填料：玻璃纤维 60
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.43 | g/cm³ | ISO 1183 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
15000 | MPa | ISO 527-2/1A |
|
拉伸强度 tensile strength |
|||
|
断裂 fracture |
145 | MPa | ISO 527-2/1A/5 |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
1.5 | % | ISO 527-2/1A/5 |
|
弯曲模量 Bending modulus |
|||
|
23℃ 23℃ |
16000 | MPa | |
|
80℃ 80℃ |
MPa | ||
|
弯曲强度 bending strength |
|||
|
23℃ 23℃ |
MPa | ||
|
80℃ 80℃ |
MPa | ||
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
-30℃ -30℃ |
kJ/m² | ||
|
23℃ 23℃ |
kJ/m² | ||
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
|
-30℃ -30℃ |
kJ/m² | ||
|
23℃ 23℃ |
kJ/m² | ||
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
熔融温度 Melting temperature 2 |
℃ | ISO 11357-3 | |
| 备注 |
|---|
| 2. 10°C/min |
|
【新闻资讯】查看全部
索尔维宣布PA66不可抗力
2018-01-15 索尔维于2018年1月9日告知其PA66合同客户，受西班牙和法国近期的聚合问题影响，宣布不可抗力。 在12月份重启西班牙产能42万吨的布兰(Blane)聚合工厂后出现了一些相当严重的问题，同时在瓦朗斯和法国圣芳斯也出现了部分问题，这些事件的发生违背了合同承诺内容，因此宣布不可抗力不可避免。持续时间或分配水平暂未告知。 随着此次不可抗力的宣布，欧洲供求问题已十分严重。这不仅会影响到欧洲，还可能影响到亚洲，因为索尔维部分产品也出口至亚洲。 我们将 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |