MARPOL® EVA 802是一种8.7%醋酸乙烯共聚物薄膜树脂,具有优异的冲击强度和热密封性。 MARPOL® EVA 802 is an 8.7% vinyl acetate copolymer film resin with excellent impact strength and heat sealability. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.930 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.1kg 190℃,2.1kg |
2.0 | g/10min | ASTM D1238 |
醋酸乙烯含量 Vinyl acetate content |
8.7 | wt% | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
割线模量 Secant modulus |
ASTM D882 | ||
1% 正割,MD 1% secant, MD |
110 | MPa | ASTM D882 |
1% 正割,TD 1% secant, TD |
117 | MPa | ASTM D882 |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,断裂 MD, fracture |
MPa | ASTM D882 | |
TD,断裂 TD, fracture |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂 MD, fracture |
% | ASTM D882 | |
TD,断裂 TD, fracture |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
g | ASTM D1709-A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
MD MD |
g | ASTM D1922 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45° 45° |
ASTM D2457 | ||
雾度 Haze |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
前10月化学原料和制品业利润增长8.6%
2015-12-01 国家统计局11月27日发布的工业企业财务数据显示,1-10月份,规模以上工业企业利润总额同比下降2%,降幅比1-9月份扩大0.3个百分点。其中,化学原料和化学制品制造业增长8.6%。 规模以上工业企业中,1-10月份国有控股企业实现利润总额9080.6亿元,同比下降25%;集体企业实现利润总额395.3亿元,下降1.8%; 股份制企业实现利润总额32698.7亿元,下降1.5%;外商及港澳台商投资企业实现利润总额12082.9亿元,增长0.3%;私营企业实现利润总额 175 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |