| 牌号简介 About |
|---|
| SABIC® PP 571P是一种高流动性材料，通常用于板材和热成型等挤压应用。该等级结合了较高的MFI和较高的刚度。SABIC® PP 571P通常用于离线热成型工艺。更高的MFI被我们的客户视为优势，因为他们可以运行更快，并有更好的板厚控制。然后将这些进展外推到该过程的形成步骤。其他应用可以认为是泡罩包装是非常薄的包装是必需的。MFI越高，运行薄板越容易。该等级具有良好的光泽和表面硬度。典型的应用是卫生的，带或不带整体铰链的封闭。本文所述产品尤其未经测试，因此未经验证可用于医药/医疗应用。 SABIC® PP 571P is a higher flow material typically used in extrusion applications like sheet and thermoforming. This grade combines higher mfi and high stiffness. SABIC® PP 571P is typically used in off line thermoforming processes. The higher mfi is seen by our customers as advantages as they can run faster and have better wall thickness control of the sheet. These advances are then extrapolated to the forming step of the process. Other application that could be thought of are blister packaging were very thin packaging is required. The higher mfi makes it easier to run thinner sheet. This grade is characterized by excellent gloss and good surface hardness. Typical applications are sanitary, closures with and without integral hinges. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
产品描述 Product Description
用途：片材;包装;卫浴产品;热成型应用;外壳;
加工条件：片材挤出成型
性能特点： 机械强度好; 宽分子量分布; 硬度高; 均聚物; 流动性高; 表面光泽度好; Good Rigidity,Good surface appearance,High liquidity,Wide molecular weight distribution,Good Hardness,Homopolymer
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.905 | g/cm³ | ASTM D792, ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
230℃，2.16kg 230℃，2.16kg |
5.7 | g/10min | ASTM D1238，ISO 1133 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
23℃ 23℃ |
4.0 | kJ/m² | ISO 179/1eA |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
23℃ 23℃ |
25 | J/m | ASTM D256-A |
|
23℃ 23℃ |
3.0 | kJ/m² | ISO 180-1A |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
|
0.45 MPa，未退火 0.45 MPa, unannealed 4 |
℃ | ISO 75-2/Bf | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
1.8 MPa，未退火 1.8 MPa, unannealed 5 |
℃ | ISO 75-2/Af | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
-- -- |
℃ | ASTM D1525，ISO 306/A120 6 6 | |
|
B120 B120 |
℃ | ASTM D1525, ISO 306/B120 7 7 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D Shaw's D |
ISO 868 | ||
|
洛氏硬度 Rockwell hardness |
|||
|
R 级 R-level |
ASTM D785 | ||
|
拉伸模量 Tensile modulus |
|||
|
1% 正割 1% secant 1 |
MPa | ASTM D638 | |
|
-- -- |
MPa | ISO 527-2/1A/1 | |
|
拉伸强度 tensile strength |
|||
|
屈服 yield 2 |
MPa | ASTM D638 | |
|
屈服 yield |
MPa | ISO 527-2/1A/50 | |
|
拉伸应变 Tensile strain |
|||
|
屈服 yield 3 |
% | ASTM D638 | |
|
屈服 yield |
% | ISO 527-2/1A/50 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 0.039 in/min |
| 3 2.0 in/min |
| 4 testbar 80*10*4mm |
| 5 标准 B (120°C/h), 压 力1 (10N) |
| 6 标准 B (120°C/h), 载荷2 (50N) |
|
【新闻资讯】查看全部 
战狼一出谁与争锋！“搜料”向中国军人致敬！
2017-08-16 今天，八一建军节， 搜料向中国军人致敬！ 90年前，南昌城头一声枪响 一个年轻的政党 组建起一支真正属于人民的军队 星星之火，自此燎原。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付