| 牌号简介 About |
|---|
| Eastar™ EN001共聚酯是一种热塑性聚酯共聚物。Eastar™ EN001共聚酯的结晶速度相对较慢。这扩大了挤压和成型工艺的操作窗口，有助于在加工更厚的板材时保持良好的清晰度。Eastar™ EN001共聚酯也可用于注塑应用。它是热成型的首选通用可结晶聚酯。本产品已通过绿色卫士室内空气质量认证。Greenguard室内空气质量认证标志是通过Greenguard环境研究所（GEI）许可使用的注册认证标志。GEI是一个行业独立的非盈利组织，负责监督Greenguard认证计划。Greenguard认证计划是一个行业独立的第三方测试计划，用于室内环境的低排放产品和材料。欲了解更多关于GEI的信息，并获得Eastman共聚酯的可打印证书，请访问www.greenguard.org。在制造商类别下选择Eastman Chemical Company，然后单击搜索以显示我们的产品列表。 Eastar™ EN001 Copolyester is a thermoplastic polyester copolymer and is suitable for food packaging applications. Eastar™ EN001 Copolyester has a relatively slow crystallization rate. This broadens the operating window for extrusion and forming processes and helps maintain good clarity when processing much thicker sheet. Eastar™ EN001 copolyester can also be used for injection molding applications. It is the preferred general-purpose crystallizable PET for thermoforming. Eastar™ EN001 copolyester is regulated for use in food packaging applications in accordance with US FDA Regulation 21 CFR 177.1315. It is lawful for use under US Department of Agriculture Food Safety Inspection Service regulations as a packaging material for meat or poultry food products prepared under federal inspection. This product has been GREENGUARD INDOOR AIR QUALITY CERTIFIED The GREENGUARD INDOOR AIR QUALITY CERTIFIED Mark is a registered certification mark used under license through the GREENGUARD Environmental Institute (GEI). GEI is an industry-independent, non-profit organization that oversees the GREENGUARD Certification Program. The GREENGUARD Certification Program is an industry independent, third-party testing program for low-emitting products and materials for indoor environments. For more information about GEI and to obtain printable certificates for Eastman™ Copolyesters, visit www.greenguard.org. Choose Eastman Chemical Company under the Manufacturer category and click search to display a list of our products. |
产品描述 Product Description
用途：家用货品;玩具;食品包装;文具;体育用品;
加工条件：热成型 Thermo forming
性能特点： 共聚物; 食品接触; Food contact compliance,Copolymer
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.33 | g/cm³ | ASTM D792 |
|
密度 Density |
1.33 | g/cm³ | ISO 1183/D |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
|
-40℃ -40℃ |
27 | J/m | ASTM D256 |
|
23℃ 23℃ |
40 | J/m | ASTM D256 |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
|
-40℃ -40℃ |
3.1 | kJ/m² | ISO 180-1A |
|
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D4218 | ||
|
-40℃ -40℃ |
ASTM D4218 | ||
|
-30℃ -30℃ |
ASTM D4218 | ||
|
-20℃ -20℃ |
ASTM D4218 | ||
|
23℃ 23℃ |
ASTM D4218 | ||
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
ISO 180/1U | ||
|
-40℃ -40℃ |
kJ/m² | ISO 180/1U | |
|
-30℃ -30℃ 2 |
kJ/m² | ISO 180/1U | |
|
-20℃ -20℃ |
ISO 180/1U | ||
|
23℃ 23℃ |
ISO 180/1U | ||
|
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
ASTM D3763 | ||
|
-40℃，2.50 mm，Energy at Peak Load -40℃，2.50 mm，Energy at Peak Load |
J | ASTM D3763 | |
|
-40℃，3.20 mm，Energy at Peak Load -40℃，3.20 mm，Energy at Peak Load |
J | ASTM D3763 | |
|
23℃，2.50 mm，Energy at Peak Load 23℃，2.50 mm，Energy at Peak Load |
J | ASTM D3763 | |
|
23℃，3.20 mm，Energy at Peak Load 23℃，3.20 mm，Energy at Peak Load |
J | ASTM D3763 | |
|
多轴向仪器化冲击能量 Multi axial instrumented impact energy |
ISO 6603-2 | ||
|
-40℃，2.50 mm，Energy to Peak Force -40℃，2.50 mm，Energy to Peak Force |
J | ISO 6603-2 | |
|
-40℃，3.20 mm，Energy to Peak Force -40℃，3.20 mm，Energy to Peak Force |
J | ISO 6603-2 | |
|
23℃，2.50 mm，Energy to Peak Force 23℃，2.50 mm，Energy to Peak Force |
J | ISO 6603-2 | |
|
23℃，3.20 mm，Energy to Peak Force 23℃，3.20 mm，Energy to Peak Force |
J | ISO 6603-2 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
透光率 Transmittance |
|||
|
总计 total |
% | ASTM D1003 | |
|
雾度 Haze |
% | ASTM D1003 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
|||
|
23℃ 23℃ |
MPa | ISO 527-2 | |
|
23℃ 23℃ |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength |
|||
|
断裂，23℃ Fracture, 23 ℃ |
MPa | ISO 527-2 | |
|
断裂，23℃ Fracture, 23 ℃ |
MPa | ASTM D638 | |
|
屈服，23℃ Yield, 23 ℃ |
MPa | ASTM D638 | |
|
屈服，23℃ Yield, 23 ℃ |
MPa | ISO 527-2 | |
|
拉伸应变 Tensile strain |
|||
|
断裂，23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
|
断裂，23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
|||
|
23℃ 23℃ |
MPa | ISO 178 | |
|
23℃ 23℃ |
MPa | ASTM D790 | |
|
弯曲强度 bending strength |
|||
|
屈服，23℃ Yield, 23 ℃ |
MPa | ASTM D790 | |
|
23℃ 23℃ |
MPa | ISO 178 | |
|
洛氏硬度 Rockwell hardness |
|||
|
R 级 R-level |
ASTM D785 | ||
|
R 级 R-level |
ISO 2039-2 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 90%C, 10%NB |
|
【新闻资讯】查看全部
完成塑料循环经济已渐成为开展趋势 2018-02-08 伴随着环境污染的不断加剧，关于“可持续塑料包装”的探讨其实从没有停止，一些大型的企业已经开始在行动，而实现塑料循环经济已渐成为发展趋势。 而亚马逊在运输塑料包装上面也做出了较大的调整：准备尽可能的采用Bubble Mailer(气泡袋)以及紧凑的纸箱来对包装进行发货。可口可乐公司在1月22日宣布，会将将重塑可持续包装全球战略，到2030年，让公司所有包装实现100%等量回收和再利用。为此，可口可乐未来将在环境保护和包装创新两个大方向上持续投入，使包装废弃物问题成为过去。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付