牌号简介 About |
---|
Noryl WCD933树脂柔性和非卤化阻燃挤出等级,用于评估HD 21.14软电缆绝缘等应用。阻燃性能满足EN 50265-2-1要求。93邵尔A硬度。通常在标准挤压设备上进行的加工。用0.12 mm x 20股铜导线在2.0 mm导线上进行的导线试验。 Flexible and non-halogenated flame retardant extrusion grade intended for evaluation in applications such as insulation of HD 21.14 flexible cables. Flame retardant performance capable of meeting EN 50265-2-1 requirement. 93 Shore A hardness. Processing typically conducted on standard extrusion equipment. Wire tests conducted on 2.0 mm wire with 0.12 mm x 20 stranded copper conductor. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.33 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
250℃,10.0kg 250℃,10.0kg |
8.5 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,30 秒 Shore A, 30 seconds |
93 | ASTM D2240 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
9.00 | MPa | ISO 527-2/50 |
断裂 fracture |
15.0 | MPa | UL 1581 |
断裂 fracture 2 |
MPa | ASTM D638 | |
断裂,80℃ Fracture, 80 ℃ 3 |
MPa | UL 1581 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/50 | |
断裂 fracture |
% | UL 1581 | |
断裂 fracture 2 |
% | ASTM D638 | |
断裂,80℃ Fracture, 80 ℃ 3 |
% | UL 1581 | |
弯曲模量 Bending modulus 4 |
MPa | ISO 178 | |
100 mm跨距 100 mm span 4 |
MPa | ASTM D790 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
Heat Deformation(100℃) Heat Deformation(100℃) 5 |
% | UL 1581 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
|||
2 mm,在油中 2 mm in oil |
kV/mm | IEC 60243-1 | |
介电常数 Dielectric constant |
|||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
1 MHz 1 MHz |
ASTM D150 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
灼热丝可燃性指数 Glowing wire flammability index |
|||
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 | |
烟雾密度 Smoke density |
ASTM E662 | ||
Flame,0.5 mm plaque,Ds,max Flame,0.5 mm plaque,Ds,max |
ASTM E662 | ||
Non-Flame,0.5 mm plaque,Ds,max Non-Flame,0.5 mm plaque,Ds,max |
ASTM E662 | ||
Vertical Flame Test Vertical Flame Test |
EN 50265-2-1 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 1, 2,0 in/min |
3 After 7 days |
4 0,49 in/min |
5 250 g |
【新闻资讯】查看全部
2021年3月份规模以上工业增加值增长14.1%
2021-04-16 搜料网资讯: 3月份,规模以上工业增加值同比实际增长14.1 %(以下增加值增速均为扣除价格因素的实际增长率)。从环比看,3月份,规模以上工业增加值比上月增长0.60%。一季度,规模 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |