| 牌号简介 About |
|---|
| SABIC高密度聚乙烯B5823 SABIC® HDPE B5823通常用于高达5升的消费者包装的吹塑，结合了高硬度和良好的ESCR水平。该等级通常用于包装大多数家用和工业化学品，如洗涤剂、清洁剂、洗发水和化妆品，以及食品包装。本产品不适用于任何医药/医疗应用，也不得用于任何医药/医疗应用。SABIC HDPE B5823 SABIC® HDPE B5823适用于高达5 L的吹塑消费包装，结合了高硬度和良好的ESCR水平。该等级适用于大多数清洁剂、清洁剂、洗发水和化妆品的包装。本文所述产品尤其未经测试，因此未经验证可用于医药/医疗应用。 SABIC® HDPE B5823 SABIC® HDPE B5823 is typically used for blow moulding of consumer packaging up to 5 l, combining high stiffness and a good ESCR level. This grade is typically used for packaging the majority of household and industrial chemicals, such as detergents, cleaners, shampoos and cosmetics, as well as food packaging. This product is not intended for and must not be used in any pharmaceutical/medical applications. SABIC® HDPE B5823 SABIC® HDPE B5823 is developed for blow moulding consumer packaging up to 5 l, combining high stiffness and a good ESCR level. This grade is suitable for packaging the majority of detergents, cleaners, shampoos and cosmetics. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
产品描述 Product Description
用途：包装;片材;食品包装;瓶子;化妆品包装;管道系统;
加工条件：管路挤出成型
性能特点： 机械强度好; 高密度; 抗应力开裂; Good Rigidity,High density,High ESCR
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.958 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
|
190℃，2.16kg 190℃，2.16kg |
0.16 | g/10min | |
|
190℃，21.6kg 190℃，21.6kg |
23 | g/10min | |
|
190℃，5.0kg 190℃，5.0kg |
0.89 | g/10min | |
|
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
|
10%非离子洗涤剂，模压成型，F50 10% non-ionic detergent, molded, F50 |
45.0 | hr | ASTM D1693B |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/A | ||
|
-30℃，模压成型 -30 ℃, molded |
kJ/m² | ||
|
23℃，模压成型 23 ℃, molded |
kJ/m² | ||
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
|
熔融温度 Melting temperature |
|||
|
DSC DSC |
℃ | ISO 11357-3 | |
|
Enthalpy Change Enthalpy Change |
J/g | ISO 11357-3 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D，模压成型 Shaw's D, molded |
ISO 868 | ||
|
拉伸模量 Tensile modulus |
|||
|
2 mm，模压成型 2 mm, molded into shape |
MPa | ISO 527-2/1BA/50 | |
|
拉伸强度 tensile strength |
ISO 527-2/1BA/50 | ||
|
屈服，2 mm，模压成型 Yield, 2 mm, molded |
MPa | ||
|
断裂，2 mm，模压成型 Fracture, 2 mm, molded |
MPa | ||
|
拉伸应变 Tensile strain |
|||
|
断裂，2 mm，模压成型 Fracture, 2 mm, molded |
% | ISO 527-2/1BA/50 | |
|
弯曲模量 Bending modulus |
|||
|
2 mm，模压成型 2 mm, molded into shape |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
|||
|
2 mm，模压成型 2 mm, molded into shape |
MPa | ISO 178 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 3 MPa |
|
【新闻资讯】查看全部 
朗盛聚氨酯业务部门将增强新型材料研讨
2017-10-17 为加强对新型材料的科学研究，特种化学品公司朗盛科技的聚氨酯业务部门决定加入美国马萨诸塞州大学马萨诸塞州聚合物研究中心(CUMIRP)。CUMIRP是大学研究和教育与聚合物材料工程相结合之地，共同利用资源促进合作。朗盛将加 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |