牌号简介 About |
---|
聚丙烯均聚物,50%玻璃纤维化学耦合增强,热稳定,热性能和机械性能在较宽的温度间隔内显著,线性热膨胀系数低(30°C至70°C),中等流动性,用于注射成型的化合物具有较高的硬度和机械性能。在温度上紧密,在自然状态下可用,并根据样品着色。 Polypropylene homopolymer 50% reinforced with glass fiber chemically coupled; heat stabilized; thermal and mechanical properties conspicuous in a wide temperature interval; low coefficient of linear thermal dilatation (from 30°C to 70°C) Medium flowabilty, compound indicated for injection molding of particulars with high stiffness and mechanical tightness in temperature, availble in natural version and colored as per sample. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.34 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
6.0 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD TD |
0.75 | % | ISO 294-4 |
MD MD |
0.15 | % | ISO 294-4 |
吸水率 Water absorption rate 2 |
|||
23℃,24hr 23℃,24hr 2 |
0.020 | % | ISO 62 |
灰份含量 Ash Content |
% | ISO 3451 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-40℃ -40℃ |
kJ/m² | ISO 180-1A | |
-20℃ -20℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
加速烘箱老化 Accelerate oven aging |
|||
150℃ 150℃ |
day | ISO 4577 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
球压测试 Ball pressure test |
|||
145℃ 145℃ |
IEC 335 | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ISO 11359-2 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.50 mm 1.50 mm |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,15 秒 Shore D, 15 seconds |
ISO 868 | ||
拉伸强度 tensile strength |
ISO 527-2/20 | ||
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2/20 | |
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2/20 | |
拉伸应变 Tensile strain |
ISO 527-2/20 | ||
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2/20 | |
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2/20 | |
弯曲模量 Bending modulus 3 |
|||
23℃ 23℃ 3 |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ISO 178 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 50%RH |
3 0.079 in/min |
【新闻资讯】查看全部
杜邦新型塑料强度堪比合金钢
2016-01-06 由美国杜邦公司的工程技术人员研制的名为“戴尔瑞ST”的新塑料日前经测试,被证实是现今强度最大的塑料,将用于工程行业。 这种塑料是一种把硫基单位结合进聚合物长链中的一种新型材料。它具有合金钢般的高强度,并有惊人的耐高温特性和耐酸性。高强度耐磨工程塑料与金属材料相比有许多优点:容易加工;具有突出耐磨、耐腐蚀性;质量轻,密度比铝轻一半,比钢轻3/4,是良好的工程机械更新换代产品。这种塑料不仅可用于制造耐磨损零部件,还可填充到玻璃、不锈钢等材料中,制成特别需要高温消毒的器具如医疗器 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |