牌号简介 About |
---|
KH52T是一种聚丙烯复合材料,由于使用了优质的基础树脂,具有优异的防霉性能,具有平衡的强度和冲击强度。该树脂的突出特点是高流动性、优越的加工性和高耐热变色性和耐光性,具有优良的外部饰面和高抗真菌性能。KH52T在韩国和日本已经通过了抗真菌测试,广泛应用于需要抗真菌特性的电子零件和厨房用具。 Description Anti-fungus compound PP KH52T features superior anti-fungus:a compound PP product possessing balanced strength and impact strength due to use of high-quality base resins. Outstanding features of these resins are high flowability, superior processability and high resistance to thermal discoloration and to light. Another advantage is that they afford excellent external finishes and high anti-fungus properties. Hanwha Total's anti-fungus compound resins have passed anti-fungus tests in Korea and Japan, and are widely used for electronic parts and kitchen utensils requiring anti-fungus characteristics. Characteristics With excellent anti-fungus properties, these products suppress colon bacillus and staphylococcus. High resistance to thermal discoloration and can be used under high-temperature conditions. Applications extrusion molded anti-fungus chopping boards Dishwasher tubs and parts, drinking water containers, and filter parts for water purifiers |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.15 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
12 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
1.1 到 1.5 | % | 内部方法 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
39 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
145 | ℃ | ASTM D648 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸强度 tensile strength 2 |
|||
屈服 yield 2 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 2 |
|||
断裂 fracture 2 |
% | ASTM D638 | |
弯曲模量 Bending modulus 3 |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 0.20 in/min |
【新闻资讯】查看全部
海通石化:我国乙烯原料轻质化进程加快
2018-03-23 乙烷制乙烯发展潜力大。乙烯生产路线主要包括石脑油蒸汽热裂解、轻烃(乙烷、丙烷等)脱氢、(煤)甲醇制烯烃和乙醇脱水制乙烯等,其中乙烷制乙烯路线具备经济性强、投资小、盈利稳定性较高等优势。目前,轻烃(乙烷和丙烷等)路线在国内乙烯生产中占比仅16%,乙烷供给是制约我国原料轻质化发展的主要瓶颈。我们认为随着国内项目及配套储运设施建设的推进,以及VLEC运输能力的提升,乙烷脱氢制乙烯装置比例有望快速提升,发展 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |