| 牌号简介 About |
|---|
| 一种双组分、充铜、导电和导热的环氧树脂，用于电子产品中的粘合剂粘合。它可用于印刷电路板层的互连、接地和EMI射频屏蔽。可实现相对低温下的快速固化。 High flow grade. Heat stabilized. Enhanced level of mold release. FDA food contact compliant in limited colors. Effective January 15th, 2007 this grade will no longer be supported with biocompatibility information and should not be used for medical applications which require biocompatibility. Alternative grade HP1R. |
产品描述 Product Description
用途：电气/电子应用领域;粘合剂;粘合;
性能特点： 导电; 快速固化; 防火阻燃等级V-2; 电磁屏蔽; 导热; Conductive,EMI,Thermal conductivity,Fast Cure,V-2
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.20 | g/cm³ | ASTM D792 |
|
特定体积 Specific volume |
0.830 | cm³/g | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
300℃，1.20kg 300℃，1.20kg |
25 | g/10min | ASTM D1238 |
|
熔体体积流动速率 Melt Volume Rate |
|||
|
300℃，1.2 kg 300℃，1.2 kg |
23.0 | cm³/10min | ISO 1133 |
|
收缩率 Shrinkage rate |
|||
|
MD：3.2 mm MD：3.2 mm |
0.50 to 0.70 | % | 内部方法 |
|
吸水率 Water absorption rate |
ASTM D570 | ||
|
24hr 24hr |
% | ASTM D570 | |
|
平衡，23℃ Equilibrium, 23 ℃ |
% | ASTM D570 | |
|
平衡，100℃ Equilibrium, 100 ℃ |
% | ASTM D570 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength 7 |
ISO 179/1eA | ||
|
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
|
23℃ 23℃ |
J/m | ASTM D4812 | |
|
Natural，Tints Natural，Tints |
J/m | ASTM D256 | |
|
23℃ 23℃ |
J/m | ASTM D256 | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 8 |
ISO 180/1A | ||
|
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
|
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
|
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
|
23℃，Energy at Peak Load 23℃，Energy at Peak Load |
J | ASTM D3763 | |
|
落锤冲击 Drop hammer impact |
|||
|
23℃ 23℃ |
J | ASTM D3029 | |
|
拉伸冲击强度 Tensile impact strength 9 |
kJ/m² | ASTM D1822 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
ASTM D648 | ||
|
1.8 MPa，未退火，100 mm跨距 1.8 MPa, unannealed, 100 mm span 10 |
℃ | ISO 75-2/Ae | |
|
0.45 MPa，未退火，6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
|
0.45 MPa，未退火，100 mm跨距 0.45 MPa, unannealed, 100 mm span 10 |
℃ | ISO 75-2/Be | |
|
1.8 MPa，未退火，3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
|
1.8 MPa，未退火，6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
A50 A50 |
℃ | ISO 306/A50 | |
|
B50 B50 |
℃ | ISO 306 | |
|
B120 B120 |
℃ | ISO 306/B120 | |
|
球压测试 Ball pressure test |
|||
|
125℃ 125℃ |
IEC 60695-10-2 | ||
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD：23~80℃ MD：23~80℃ |
1/℃ | ISO 11359-2 | |
|
MD：-40~95℃ MD：-40~95℃ |
1/℃ | ASTM E831 | |
|
比热 specific heat |
J/kg/℃ | ASTM C351 | |
|
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM C177 | |
|
导热系数 Thermal conductivity coefficient |
W/m/K | ISO 8302 | |
|
相对温度指数 Relative temperature index |
|||
|
电气性能 Electrical performance |
℃ | UL 746 | |
|
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
|
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
|
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
|
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
|
介电强度 Dielectric strength |
IEC 60243-1 | ||
|
3.2 mm，在空气中 3.2 mm in air |
kV/mm | ASTM D149 | |
|
0.8 mm，在油中 0.8 mm in oil |
kV/mm | IEC 60243-1 | |
|
1.6 mm，在油中 1.6 mm in oil |
kV/mm | IEC 60243-1 | |
|
3.2 mm，在油中 3.2 mm in oil |
kV/mm | IEC 60243-1 | |
|
介电常数 Dielectric constant |
ASTM D150 | ||
|
50 Hz 50 Hz |
ASTM D150 | ||
|
60 Hz 60 Hz |
ASTM D150 | ||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
相对电容率 Relative permittivity |
IEC 60250 | ||
|
50 Hz 50 Hz |
IEC 60250 | ||
|
60 Hz 60 Hz |
IEC 60250 | ||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
耗散因数 Dissipation factor |
ASTM D150 | ||
|
50 Hz 50 Hz |
ASTM D150 | ||
|
60 Hz 60 Hz |
ASTM D150 | ||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
耗散因数 Dissipation factor |
IEC 60250 | ||
|
50 Hz 50 Hz |
IEC 60250 | ||
|
60 Hz 60 Hz |
IEC 60250 | ||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
|
高电弧燃烧指数（HAI） High Arc Burning Index (HAI) |
UL 746 | ||
|
高电压电弧起痕速率 High voltage arc marking rate |
|||
|
HVTR HVTR |
UL 746 | ||
|
热丝引燃 Hot wire ignition |
|||
|
HWI HWI |
UL 746 | ||
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
1.10 mm 1.10 mm |
UL 94 | ||
|
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
折射率 Refractive index |
ASTM D542 | ||
|
透光率 Transmittance |
|||
|
2540 µm 2540 µm |
% | ASTM D1003 | |
|
雾度 Haze |
|||
|
2540 µm 2540 µm |
% | ASTM D1003 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
|
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
|
拉伸强度 tensile strength 3 |
|||
|
断裂 fracture |
MPa | ISO 527-2/50 | |
|
断裂 fracture 3 |
MPa | ASTM D638 | |
|
屈服 yield |
MPa | ISO 527-2/50 | |
|
屈服 yield 3 |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain 3 |
|||
|
断裂 fracture |
% | ISO 527-2/50 | |
|
断裂 fracture 4 |
% | ASTM D638 | |
|
屈服 yield |
% | ISO 527-2/50 | |
|
屈服 yield 3 |
% | ASTM D638 | |
|
弯曲模量 Bending modulus 5 |
MPa | ISO 178 | |
|
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
|
弯曲强度 bending strength 5 , 6 |
MPa | ISO 178 | |
|
弯曲强度 bending strength 4 |
|||
|
屈服，50 mm跨度 Yield, 50 mm span 4 |
MPa | ASTM D790 | |
|
泰伯耐磨性 Taber abraser |
|||
|
1000 周期，1000 g，CS-17 转轮 1000 cycles, 1000 g, CS-17 wheels |
mg | ASTM D1044 | |
|
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
|
M 级 M-level |
ASTM D785 | ||
|
R 级 R-level |
ASTM D785 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 3 Below Tg |
| 4 Above Tg |
| 5 Part B |
| 6 Part A |
| 7 1.0 rpm |
|
【新闻资讯】查看全部 
节能塑料机械注塑机是企业可持续开展将来
2017-09-22 世界能源危机越来越紧迫,不知道你是否已经考虑过这个问题。你仍不使用节能塑料机械注塑机吗?你浪费大量的能量,一年浪费的能量等于你买新机器。能源危机,未来,我们的后代将使用什么样的能量。 严重的能源真正各行各业必须增加“节能环保”的意识,政府也计划对新能源产业的发展。政府大力促进和支持新能源产业,使即将到来的节能产业发展得到有力支持,潜在的中间的巨大的发展空间。注塑机行业制造商推出各种各样的新节能注塑机,和引进节能改革旧的机器。 < |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |