| 牌号简介 About |
|---|
| 最佳大电流引弧性能。玻璃/PTFE填充。根据ISO 1043-1的化学缩写：LCP固有阻燃塞拉尼斯已在FDA建立了Vectra® MT1335的药物主文件（DMF 8468）和设备主文件（MAF 315）。这些是为了帮助我们的客户最终使用FDA的申请。Vectra® MT1335已经过测试，并符合美国药典第六类。 Vectra® MT1335 VF3001 (natural) is a glass/PTFE filled, tribologically-modified, easy flow LCP grade for injection molding. Vectra® MT1335 VF3001 (natural) is a special grade developed for medical industry applications and complies with: Food Contact Substance Notification (FCN) No. 742 of the Food and Drug Administration (FDA) and is listed in the Drug Master File (DMF 8464) and the Device Master File (MAF 315) the corresponding EU and national registry regulatory requirements biocompatibility in tests corresponding to USP 23 Class VI/ISO 10993 low residual monomers no animal products Best High Current Arc Ignition (HAI) performance Chemical abbreviation according to ISO 1043-1 : LCP Inherently flame retardant |
产品描述 Product Description
性能特点： 防火阻燃等级V-0; 阻燃; Flame Characteristics,V-0
填料：PTFE
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.62 | g/cm³ | ISO 1183 |
|
收缩率 Shrinkage rate |
ISO 294-4 | ||
|
TD TD |
0.40 | % | ISO 294-4 |
|
MD MD |
0.10 | % | ISO 294-4 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
23℃ 23℃ |
26 | kJ/m² | ISO 179/1eA |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
|
23℃ 23℃ |
38 | kJ/m² | ISO 179/1eU |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
|
23℃ 23℃ |
kJ/m² | ISO 180/1U | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
8.0 MPa，未退火 8.0 MPa, unannealed |
℃ | ISO 75-2/C | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
B50 B50 |
℃ | ISO 306 | |
|
熔融温度 Melting temperature 2 |
℃ | ISO 11357-3 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
TD TD |
1/℃ | ISO 11359-2 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
|
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
|
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
|
相对电容率 Relative permittivity |
IEC 60250 | ||
|
100 Hz 100 Hz |
IEC 60250 | ||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
耗散因数 Dissipation factor |
IEC 60250 | ||
|
100 Hz 100 Hz |
IEC 60250 | ||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
耐电弧性 Arc resistance |
sec | 内部方法 | |
|
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
MPa | ISO 527-2/1A/1 | |
|
拉伸强度 tensile strength |
|||
|
断裂 fracture |
MPa | ISO 527-2/1A/5 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ISO 527-2/1A/5 | |
|
弯曲模量 Bending modulus |
|||
|
23℃ 23℃ |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
|||
|
23℃ 23℃ |
MPa | ISO 178 | |
|
压缩模量 Compression modulus |
MPa | ISO 604 | |
|
压缩强度 compressive strength |
|||
|
1% 应变 1% strain |
MPa | ISO 604 | |
|
洛氏硬度 Rockwell hardness |
|||
|
M 级 M-level |
ISO 2039-2 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 10°C/min |
|
【新闻资讯】查看全部 
上新了！抚顺石化开发高熔体强度聚丙烯
2021-03-11 搜料网资讯： 近日，抚顺石化研究院加大了新产品开发力度，开展了一系列聚烯烃产品性能分析试验，为优化加工方案，提高产品质量提供依据。 高熔体强度聚丙烯属于高端聚丙烯产品 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |