牌号简介 About |
---|
亲和力*pl 1840g聚烯烃塑性体(pop)是通过InSite*技术生产的。它是一种乙烯-α-烯烃树脂,旨在提供低温密封性、良好的耐穿刺性、光学和感官性能的吹塑薄膜。它还与其他聚烯烃具有良好的兼容性,允许有效的混合和共挤。优异的低温密封性和韧性,适用于液体和干燥食品袋应用中的密封剂:铸膜符合:加拿大HPFP无异议欧盟,编号10/2011美国FDA FCN 424美国FDA-DMF有关完整细节,请参考法规。 AFFINITY* PL 1840G Polyolefin Plastomer (POP) is produced via INSITE* Technology. It is an ethylene alpha-olefin resin designed to provide blown film with low temperature sealability, good puncture resistance, optics and organoleptic properties. It also has excellent compatibility with other polyolefins, allowing efficient blending and coextrusion. Outstanding low temperature sealability and toughness Suitable as a sealant in liquid & dry food pouch applications Applications: Blown Film Complies with: Canadian HPFP No Objection EU, No 10/2011 U.S. FDA FCN 424 U.S. FDA-DMF Consult the regulations for complete details. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.909 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.0 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
51 | µm | |
膜刺穿强度 Membrane puncture strength |
|||
51 µm 51 µm |
9.16 | J | 内部方法 |
膜刺穿力 Membrane puncture force |
|||
51 µm 51 µm |
93.0 | N | 内部方法 |
膜耐刺穿性 Membrane puncture resistance |
|||
51 µm 51 µm |
J/cm³ | 内部方法 | |
割线模量 Secant modulus |
ASTM D882 | ||
2% 正割,MD:51 µm 2% secant, MD: 51 µ m |
MPa | ASTM D882 | |
2% 正割,TD:51 µm 2% secant, TD: 51 µ m |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,51 µm MD, yield, 51 µ m |
MPa | ASTM D882 | |
TD,屈服,51 µm TD, yield, 51 µ m |
MPa | ASTM D882 | |
MD,断裂,51 µm MD, fracture, 51 µ m |
MPa | ASTM D882 | |
TD,断裂,51 µm TD, fracture, 51 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,51 µm MD, fracture, 51 µ m |
% | ASTM D882 | |
TD,断裂,51 µm TD, fracture, 51 µ m |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
51 µm 51 µm |
g | ASTM D1709-B | |
埃尔曼多夫抗撕强度 Elmandorf tear strength 2 |
ASTM D1922 | ||
MD:51 µm MD:51 µm |
g | ASTM D1922 | |
TD:51 µm TD:51 µm |
g | ASTM D1922 | |
始封温度 Initial sealing temperature 3 |
|||
51 µm 51 µm 3 |
℃ | 内部方法 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
20°,50.8 µm 20°,50.8 µm |
ASTM D2457 | ||
透明度 transparency |
|||
50.8 µm 50.8 µm |
ASTM D1746 | ||
雾度 Haze |
|||
50.8 µm 50.8 µm |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 改性过的矩形测件。 |
3 实现 2 磅/英寸 (8.8 N/25.4 mm) 热封强度的温度。 热封强度,Topwave HT 测试仪 0.5 S 保压,40 psi 压力,拉动速度 10 英寸/分(250 mm/秒)。 |
【新闻资讯】查看全部
磷肥:保障有力 价格坚挺
2022-02-25 整体来看,今年春耕磷肥供应充足。目前磷肥行业开工率较春节前大幅提升,加之国家实施保供稳价政策,磷肥供应完全可以保障春耕需求。 中国磷复肥工业协会信息部主任王莹分析认 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |