牌号简介 About |
---|
热传导矿物填充PA6-FR复合材料 Thermally conductive mineral filled PA6 FR compounding |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.69 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
ASTM D955 | ||
MD:24 hrs MD:24 hrs |
0.54 | % | ASTM D955 |
TD:24 hrs TD:24 hrs |
0.57 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.060 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
-- -- 2 |
13700 | MPa | ASTM D638 |
-- -- |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture 3 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
断裂 fracture 3 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/5 | |
弯曲模量 Bending modulus |
|||
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
-- -- 5 |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
-- -- 5 , 6 |
MPa | ISO 178 | |
断裂,50 mm跨度 Fracture, 50 mm span 4 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
23℃ 23℃ 7 |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
J/m | ASTM D4812 | |
23℃ 23℃ 7 |
kJ/m² | ISO 180/1U | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,64 mm跨距 0.45 MPa, unannealed, 64 mm span 8 |
℃ | ISO 75-2/Bf | |
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 8 |
℃ | ISO 75-2/Af | |
线性热膨胀系数 Linear coefficient of thermal expansion |
ASTM E831 | ||
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM E831 | |
MD:40~120℃ MD:40~120℃ |
1/℃ | ASTM E831 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
TD:40~120℃ TD:40~120℃ |
1/℃ | ASTM E831 | |
导热系数 Thermal conductivity coefficient |
|||
-- -- 9 |
W/m/K | ASTM E1461 | |
-- -- 10 |
W/m/K | ASTM E1461 | |
-- -- 11 |
W/m/K | ISO 22007-2 | |
-- -- 12 |
W/m/K | ISO 22007-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
介电强度 Dielectric strength |
|||
1 mm,在油中 1 mm in oil |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
1.10 GHz 1.10 GHz |
ASTM ES7-83 | ||
耗散因数 Dissipation factor |
|||
1.1 GHz 1.1 GHz |
ASTM ES7-83 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
0.80 mm 0.80 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
|||
1.0-3.0 mm 1.0-3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
1 mm 1 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.20 in/min |
3 类型 1, 0.20 in/min |
4 0.051 in/min |
5 0.079 in/min |
6 Break |
7 80*10*4 |
8 80*10*4 mm |
9 through-plane, 10*10*3mm sample |
10 in-plane, ø25*0.4mm disc |
11 through-plane, 60*60*3mm plaque |
12 in-plane, 60*60*3mm plaque |
【新闻资讯】查看全部
福布斯:由近期游戏驿站股价看石油行业泡沫
2021-02-10 搜料网资讯: 据福布斯2月1日报道,对于石油交易商来说, 围绕近期游戏驿站公司(GME)股价飙升的争论耳熟能详,对查尔斯 狄 更斯(Charles Dickens)的粉丝而言也是如此,他在《尼古 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |