EMERGE™ PC/ABS 7700 NA高级树脂是一种不含氯或溴添加剂的阻燃PC/ABS混合物。它具有优越的可加工性,适用于注塑成型应用。这一等级具有良好的美学,是紫外线稳定,可定制颜色。主要特点:符合RoHS的应用:电气外壳消费电子信息技术设备 EMERGE™ PC/ABS 7700 NA Advanced Resin is an ignition-resistant PC/ABS blend that contains no chlorine or bromine additives. It has superior processability for injection molding applications. This grade has excellent aesthetics, is UV stabilized and is available in custom colors. Main Characteristics: RoHS Compliant Applications: Electrical housings Consumer Electronics Information technology equipment |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
-- -- |
1.17 | g/cm³ | ASTM D792 |
-- -- |
1.18 | g/cm³ | ISO 1183/B |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,3.80kg 230℃,3.80kg |
11 | g/10min | ASTM D1238 |
240℃,5.0kg 240℃,5.0kg |
20 | g/10min | ASTM D1238 |
260℃,2.16kg 260℃,2.16kg |
13 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD MD |
% | ASTM D955 | |
MD MD |
% | ISO 294-4 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃,注塑成型 -30 ℃, injection molding |
kJ/m² | ISO 179/1eA | |
23℃,注塑成型 23 ℃, injection molding |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-18℃,3.2mm,注塑成型 -18 ℃, 3.2mm, injection molding |
J/m | ASTM D256 | |
-7℃ -7℃ |
J/m | ASTM D256 | |
23℃,3.2mm,注塑成型 23 ℃, 3.2mm, injection molding |
J/m | ASTM D256 | |
-30℃,注塑成型 -30 ℃, injection molding |
kJ/m² | ISO 180-A | |
23℃,注塑成型 23 ℃, injection molding |
kJ/m² | ISO 180-A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ASTM D1525 3 , ISO 306/A120 3 | |
B50 B50 |
℃ | ISO 306 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
ASTM D696 | ||
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM D696 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM D696 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
IEC 60243-1 | ||
1.6 mm,在油中 1.6 mm in oil |
kV/mm | IEC 60243-1 | |
3.2 mm,在油中 3.2 mm in oil |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level 4 |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
2.00 mm 2.00 mm |
UL 94 | ||
2.50 mm 2.50 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index 4 |
IEC 60695-2-12 | ||
1.5 mm 1.5 mm |
℃ | IEC 60695-2-12 | |
2.0 mm 2.0 mm |
℃ | IEC 60695-2-12 | |
2.5 mm 2.5 mm |
℃ | IEC 60695-2-12 | |
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
极限氧指数 Extreme oxygen index 4 |
% | ASTM D2863 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级,3.20 mm R-grade, 3.20 mm |
ASTM D785 | ||
拉伸模量 Tensile modulus |
|||
3.20 mm,注塑成型 3.20 mm, injection molded |
MPa | ASTM D638 | |
4 mm,注塑成型 4 mm, injection molded |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding |
MPa | ASTM D638 | |
屈服,4 mm,注塑成型 Yield, 4 mm, injection molding |
MPa | ISO 527-2/50 | |
断裂,3.20 mm,注塑成型 Fracture, 3.20 mm, injection molded |
MPa | ASTM D638 | |
断裂,4 mm,注塑成型 Fracture, 4 mm, injection molded |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding |
% | ASTM D638 | |
屈服,4 mm,注塑成型 Yield, 4 mm, injection molding |
% | ISO 527-2/50 | |
断裂,3.20 mm,注塑成型 Fracture, 3.20 mm, injection molded |
% | ASTM D638 | |
断裂,4 mm,注塑成型 Fracture, 4 mm, injection molded |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus |
|||
3.20 mm,注塑成型 3.20 mm, injection molded |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
3.20 mm,注塑成型 3.20 mm, injection molded |
MPa | ASTM D790 |
备注 |
---|
3 标准 B (120°C/h), 压 力1 (10N) |
4 This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
【新闻资讯】查看全部
顺酐市场弱势难改 或将维持僵持局面
2015-11-26 上周顺酐略有下跌,目前整体僵持运行为主。本文小编将依据手中现有资料对顺酐本周的走势作出分析及预测。 上周走势总结 近期顺酐的走势以稳为主,上周稳中小跌。上周周初顺酐均价为6387.5元/吨(均含税),截至周末为6375元/吨,跌幅-0.2%。顺酐市场主要受下游开工率低的影响,导致供需面的失衡。且长久以来,顺酐市场需求一直处于清淡状态,产能过剩日益突出,这也是导致顺酐僵持运行的主要原因,另外,目前顺酐市场正处于淡季,因此可谓是雪上加霜,导致稳中小跌。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |