牌号简介 About |
---|
FRIANYL® A3 GF25 V0P2是一种聚酰胺66(尼龙66)化合物,25%玻璃纤维增强,阻燃,红色磷和低磷酸盐释放,UL认证的V0。该化合物用于注塑成型。FRIANYL® A3 GF25 V0P2主要为电气和电子工业设计。它也适用于汽车或工业和消费者应用。 FRIANYL® A3 GF25 V0P2 is a Polyamide 66 (Nylon 66) compound, 25% glass fiber reinforced, flame retardant with red phosphorous and low phosphate release, UL listed V0. This compound is intended for injection molding. FRIANYL® A3 GF25 V0P2 is primarily designed for the Electrical and Electronic industry. It is also suitable for Automotive or Industrial & Consumer applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.34 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD:23℃ TD:23℃ |
0.70 | % | ISO 294-4 |
MD:23℃ MD:23℃ |
0.50 | % | ISO 294-4 |
吸水率 Water absorption rate |
ISO 62 | ||
23℃,24hr 23℃,24hr |
0.80 | % | ISO 62 |
饱和,23℃ Saturation, 23 ℃ |
5.5 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-A | |
23℃ 23℃ |
kJ/m² | ISO 180-A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
连续使用温度 Continuous use temperature 3 |
℃ | IEC 60216 | |
球压测试 Ball pressure test |
IEC 60695-10-2 | ||
125℃ 125℃ |
IEC 60695-10-2 | ||
165℃ 165℃ |
IEC 60695-10-2 | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity 4 |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
2 mm 2 mm |
kV/mm | IEC 60243-1 | |
相比漏电起痕指数 Compared to the leakage tracing index |
|||
3.20 mm,解决方案 A 3.20 mm, solution A |
V | IEC 60112 | |
针焰测试 Needle flame test |
IEC 60695-11-5 | ||
1.00 mm 1.00 mm |
IEC 60695-11-5 | ||
2.00 mm 2.00 mm |
IEC 60695-11-5 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.80 mm,本色,黑色 0.80 mm, natural color, black |
UL 94 | ||
1.60 mm,本色,黑色 1.60 mm, natural color, black |
UL 94 | ||
3.20 mm,本色,黑色 3.20 mm, natural color, black |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
IEC 60695-2-12 | ||
0.80 mm 0.80 mm |
℃ | IEC 60695-2-12 | |
3.2 mm 3.2 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
0.8 mm 0.8 mm |
℃ | IEC 60695-2-13 | |
3.2 mm 3.2 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 20000 hr |
3 23°C |
【新闻资讯】查看全部
抖M!这些塑料机械等你来攻
2018-02-02 随着中国石油化学工业的发展,中国塑料机械工业逐步形成了一个独立的工业部门,并初具规模。目前,我国已经成为全球最大的塑料生产和消费之地,且行业增长势态犹在。该行业情况表明,塑料加工工业仍将是中国塑料机械制造工业高速发展的源动力。 抖M!这些塑料机械等你来攻 现阶段的塑料机械产业紧跟材料科学、电子信息、云计算、大数据和人工智能等学科,将各类最新科技成果运用到本行业,按照客 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |