| 牌号简介 About |
|---|
| Lotr_ne Q2018系列是采用丁烯（C4）共聚单体在气相反应器中生产的线性低密度聚乙烯树脂。它们是为吹塑薄膜应用而设计的，可以纯形式使用，也可以与其他聚乙烯树脂（例如，用于单挤出或共挤出工艺的低密度聚乙烯或高密度聚乙烯和MPE树脂）混合，以改变薄膜性能。Lotr_ne Q2018系列适用于消费者、工业、食品或卫生包装领域的许多应用，如冷冻膜、面包袋、购物者和袋子，以及层压膜和多层包装膜。 Lotrène® Q2018 Series are Linear Low Density Polyethylene resins produced in a gas phase reactor using butene (C4) co-monomer. They are designed for blown film applications and can be used in pure form as well as blended with other PE resins, such as LDPE or HDPE and mPE resins for mono extrusion or co-extrusion process to modify film properties. Lotrène® Q2018 Series are suited for many applications in the field of consumer, industrial, food or hygiene packaging such as freezer film, bread bags, shoppers and bags as well as lamination film and multilayer packaging film. |
产品描述 Product Description
用途：薄膜;多层薄膜;包装;工业应用;袋子;食品包装;层压板;消费品应用领域;薄壁包装;混合;
加工条件：共挤薄膜
性能特点： 抗结块性; 热稳定性好; 高光滑性; 丁烯共聚单体; Smoothness,High anti-blocking,Butylene copolymer,Heat Stabilized
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.918 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
2.0 | g/10min | ASTM D1238 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
割线模量 Secant modulus |
ASTM D882 | ||
|
1% 正割，MD：40 µm，吹塑薄膜 1% secant, MD: 40 µ m, blow molded film |
215 | MPa | ASTM D882 |
|
1% 正割，TD：40 µm，吹塑薄膜 1% secant, TD: 40 µ m, blow molded film |
245 | MPa | ASTM D882 |
|
拉伸强度 tensile strength |
ASTM D882 | ||
|
MD，屈服，40 µm，吹塑薄膜 MD, yield, 40 µ m, blow molded film |
11.0 | MPa | ASTM D882 |
|
TD，屈服，40 µm，吹塑薄膜 TD, yield, 40 µ m, blow molded film |
MPa | ASTM D882 | |
|
MD，断裂，40 µm，吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
MPa | ASTM D882 | |
|
TD，断裂，40 µm，吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
MPa | ASTM D882 | |
|
拉伸应变 Tensile strain |
ASTM D882 | ||
|
MD，断裂，40 µm，吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
% | ASTM D882 | |
|
TD，断裂，40 µm，吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
% | ASTM D882 | |
|
落锤冲击 Drop hammer impact 2 |
|||
|
40 µm，吹塑薄膜 40 µ m, blow molded film 2 |
g | ASTM D1709 | |
|
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
|
MD：40 µm，吹塑薄膜 MD: 40 µ m, blow molded film |
g | ASTM D1922 | |
|
TD：40 µm，吹塑薄膜 TD: 40 µ m, blow molded film |
g | ASTM D1922 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
|
结晶峰温度 Crystallization peak temperature |
|||
|
DSC DSC |
℃ | 内部方法 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
45°，40.0 µm，吹塑薄膜 45 °, 40.0 µ m, blow molded film |
ASTM D2457 | ||
|
雾度 Haze |
|||
|
40 µm，吹塑薄膜 40 µ m, blow molded film |
% | ASTM D1003 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 F50 |
|
【新闻资讯】查看全部 
中国石油“辛烯等α-烯烃合成成套技术工业试验”项目如期中交！
2021-09-01 搜料网资讯： 8月30日， 中国石油辛烯等-烯烃合成 成套技术工业试验项目 如期中交啦！ 这个项目是中国石油重大工业现场试验项目，也是国家重点研发计划高性能润滑油生产关键技术 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付