| 牌号简介 About |
|---|
| TUFLIN™ HS-7028 NT 7线性低密度聚乙烯树脂是一种乙烯-己烯共聚物，线性低密度（LLDPE）树脂，设计具有良好的强度和加工性能。本产品推荐用于一般用途的包装应用，从厚规格、重型袋子到高速薄型应用，己烯线性低密度树脂，一般用途树脂，高强度。本产品中的添加剂限制仅用于食品接触应用的薄膜形式。符合：美国FDA 21 CFR 177.1520（c）3.1a（有限制）欧洲委员会第10/2011号条例（欧盟）有关完整细节，请参考条例。 TUFLIN™ HS-7028 NT 7 Linear Low Density Polyethylene Resin is an ethylene-hexene copolymer, linear low density (LLDPE) resin designed for good strength and processability. This product is recommended for general purpose packaging applications from thick gauge, heavy duty bags to high speed thin gauge applications Hexene Linear Low Density Resin General Purpose Resin Excellent Strength An additive present in this product limits use only in film form for food contact applications. Complies with: U.S. FDA 21 CFR 177.1520 (c) 3.1a (with Restrictions) European Commission Regulation (EU) No 10/2011 Consult the regulations for complete details. |
产品描述 Product Description
加工条件：吹塑薄膜
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.918 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
1.0 | g/10min | ASTM D1238 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
25 | µm | 内部方法 |
|
膜刺穿强度 Membrane puncture strength |
4.52 | J | 内部方法 |
|
膜刺穿力 Membrane puncture force |
48.9 | N | 内部方法 |
|
膜耐刺穿性 Membrane puncture resistance |
J/cm³ | 内部方法 | |
|
膜强度 Membrane strength |
ASTM D882 | ||
|
MD MD |
J/cm³ | ASTM D882 | |
|
TD TD |
J/cm³ | ASTM D882 | |
|
割线模量 Secant modulus |
ASTM D882 | ||
|
1% 正割，MD 1% secant, MD |
MPa | ASTM D882 | |
|
2% 正割，MD 2% secant, MD |
MPa | ASTM D882 | |
|
1% 正割，TD 1% secant, TD |
MPa | ASTM D882 | |
|
2% 正割，TD 2% secant, TD |
MPa | ASTM D882 | |
|
拉伸强度 tensile strength |
ASTM D882 | ||
|
MD，屈服 MD, yield |
MPa | ASTM D882 | |
|
TD，屈服 TD, yield |
MPa | ASTM D882 | |
|
MD，断裂 MD, fracture |
MPa | ASTM D882 | |
|
TD，断裂 TD, fracture |
MPa | ASTM D882 | |
|
拉伸应变 Tensile strain |
ASTM D882 | ||
|
MD，断裂 MD, fracture |
% | ASTM D882 | |
|
TD，断裂 TD, fracture |
% | ASTM D882 | |
|
落锤冲击 Drop hammer impact |
g | ASTM D1709-A | |
|
埃尔曼多夫抗撕强度 Elmandorf tear strength 2 |
ASTM D1922 | ||
|
MD MD |
g | ASTM D1922 | |
|
TD TD |
g | ASTM D1922 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
|
熔融温度 Melting temperature |
|||
|
DSC DSC |
℃ | 内部方法 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
45° 45° |
ASTM D2457 | ||
|
雾度 Haze |
% | ASTM D1003 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 方法 B |
|
【新闻资讯】查看全部 
塑料耐候测试
2017-06-21 老化与服务生活研究 多面体实验室认识到，天气条件或化学试剂对塑料，聚合物和弹性计的使用寿命的影响与这些材料的基本物理性质一样重要。多面体可以根据ASTM G 154进行加速风化 |
|