牌号简介 About |
---|
它是热塑性弹性体(TPE)系列中的一种硬质、可着色、通用型热塑性硫化弹性体 (TPV)。这种材料同时具有良好的物理性质和耐化学性,适用于广泛的领域。这 一牌号的山都平 TPV 是剪切速率依赖型产品,可在常规热塑性注塑成型、挤出成 型、吹塑成型、热成型或真空成型设备上加工。这是一种聚烯烃基材料,可在生产 过程中进行回收利用。 A hard, colorable, versatile thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material combines good physical properties and chemical resistance for use in a wide range of applications. This grade of Santoprene TPV is shear-dependent and can be processed on conventional thermoplastics equipment for injection molding, extrusion, blow molding, thermoforming or vacuum forming. It is polyolefin based and recyclable within the manufacturing stream. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.948 | g/cm³ | ASTM D792 |
密度 Density |
0.950 | g/cm³ | ISO 1183 |
Detergent Resistance Detergent Resistance |
f4 | UL 2157 | |
Detergent Resistance Detergent Resistance |
f3 | UL 749 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
TD,断裂,23℃ TD, fracture, 23 ℃ |
20.7 | MPa | ISO 37 |
TD,断裂,23℃ TD, fracture, 23 ℃ |
MPa | ASTM D412 | |
TD,100% 应变,23℃ TD, 100% strain, 23 ℃ |
MPa | ISO 37 | |
TD,100% 应变,23℃ TD, 100% strain, 23 ℃ |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
|||
TD,断裂,23℃ TD, fracture, 23 ℃ |
% | ASTM D412 | |
TD,断裂,23℃ TD, fracture, 23 ℃ |
% | ISO 37 | |
撕裂强度 tear strength |
|||
TD,23℃ TD,23℃ |
kN/m | ASTM D624 | |
TD,23℃ TD,23℃ |
kN/m | ISO 34-1 | |
压缩形变 Compression deformation |
ASTM D395B | ||
70℃,22 hr 70℃,22 hr |
% | ASTM D395B | |
125℃,70 hr 125℃,70 hr |
% | ASTM D395B | |
压缩形变 Compression deformation |
ISO 815 | ||
70℃,22 hr 70℃,22 hr |
% | ISO 815 | |
125℃,70 hr 125℃,70 hr |
% | ISO 815 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,15 秒,23℃ Shore D, 15 seconds, 23 ℃ |
ISO 868 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
脆化温度 Embrittlement temperature |
℃ | ISO 812 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
|||
150℃,168 hr 150℃,168 hr |
% | ASTM D573 | |
150℃,168 hr 150℃,168 hr |
% | ISO 188 | |
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air |
|||
150℃,168 hr 150℃,168 hr |
% | ASTM D573 | |
Change in Tensile Strain at Break in Air(150℃,168 hr) Change in Tensile Strain at Break in Air(150℃,168 hr) |
% | ISO 188 | |
Change in Durometer Hardness in Air(邵氏 D,150℃,168 hr) Change in Durometer Hardness in Air (Shore D, 150 ℃, 168 hr) |
ASTM D573 | ||
空气中邵氏硬度的变化率 The rate of change of Shore hardness in air |
|||
邵氏 D,150℃,168 hr Shore D, 150 ℃, 168 hr |
ISO 188 | ||
拉伸强度的变化率 The rate of change in tensile strength |
ASTM D471 | ||
23℃,168 hr,in Acetic Acid 23℃,168 hr,in Acetic Acid |
% | ASTM D471 | |
23℃,168 hr,in Cyclohexane 23℃,168 hr,in Cyclohexane |
% | ASTM D471 | |
23℃,168 hr,in Detergent(Tide),2.5% 23℃,168 hr,in Detergent(Tide),2.5% |
% | ASTM D471 | |
23℃,168 hr,in Ethanol,95% 23℃,168 hr,in Ethanol,95% |
% | ASTM D471 | |
23℃,168 hr,in Hydrochloric Acid,10% 23℃,168 hr,in Hydrochloric Acid,10% |
% | ASTM D471 | |
23℃,168 hr,in Isopropyl Alcohol 23℃,168 hr,in Isopropyl Alcohol |
% | ASTM D471 | |
23℃,168 hr,in Methylethylketone 23℃,168 hr,in Methylethylketone |
% | ASTM D471 | |
23℃,168 hr,in Sodium Chloride,15% 23℃,168 hr,in Sodium Chloride,15% |
% | ASTM D471 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ASTM D471 | |
23℃,168 hr,in Sulfuric Acid,98% 23℃,168 hr,in Sulfuric Acid,98% |
% | ASTM D471 | |
23℃,168 hr,in Trichloroethylene 23℃,168 hr,in Trichloroethylene |
% | ASTM D471 | |
100℃,168 hr,in Deionized Water 100℃,168 hr,in Deionized Water |
% | ASTM D471 | |
100℃,168 hr,in IRM 903 Oil 100℃,168 hr,in IRM 903 Oil |
% | ASTM D471 | |
125℃,70 hr,in IRM 903 Oil 125℃,70 hr,in IRM 903 Oil |
% | ASTM D471 | |
125℃,168 hr,in IRM 903 Oil 125℃,168 hr,in IRM 903 Oil |
% | ASTM D471 | |
拉伸强度的变化率 The rate of change in tensile strength |
ISO 1817 | ||
23℃,168 hr,in Acetic Acid 23℃,168 hr,in Acetic Acid |
% | ISO 1817 | |
23℃,168 hr,in Cyclohexane 23℃,168 hr,in Cyclohexane |
% | ISO 1817 | |
23℃,168 hr,in Detergent(Tide),2.5% 23℃,168 hr,in Detergent(Tide),2.5% |
% | ISO 1817 | |
23℃,168 hr,in Ethanol,95% 23℃,168 hr,in Ethanol,95% |
% | ISO 1817 | |
23℃,168 hr,in Hydrochloric Acid,10% 23℃,168 hr,in Hydrochloric Acid,10% |
% | ISO 1817 | |
23℃,168 hr,in Isopropyl Alcohol 23℃,168 hr,in Isopropyl Alcohol |
% | ISO 1817 | |
23℃,168 hr,in Methylethylketone 23℃,168 hr,in Methylethylketone |
% | ISO 1817 | |
23℃,168 hr,in Sodium Chloride,15% 23℃,168 hr,in Sodium Chloride,15% |
% | ISO 1817 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ISO 1817 | |
23℃,168 hr,in Sulfuric Acid,98% 23℃,168 hr,in Sulfuric Acid,98% |
% | ISO 1817 | |
23℃,168 hr,in Trichloroethylene 23℃,168 hr,in Trichloroethylene |
% | ISO 1817 | |
100℃,168 hr,in Deionized Water 100℃,168 hr,in Deionized Water |
% | ISO 1817 | |
100℃,168 hr,in IRM 903 Oil 100℃,168 hr,in IRM 903 Oil |
% | ISO 1817 | |
125℃,70 hr,in IRM 903 Oil 125℃,70 hr,in IRM 903 Oil |
% | ISO 1817 | |
125℃,168 hr,in IRM 903 Oil 125℃,168 hr,in IRM 903 Oil |
% | ISO 1817 | |
极限伸长率的变化率 Change rate of ultimate elongation |
ASTM D471 | ||
23℃,168 hr,in Cyclohexane 23℃,168 hr,in Cyclohexane |
% | ASTM D471 | |
23℃,168 hr,in Detergent(Tide),2.5% 23℃,168 hr,in Detergent(Tide),2.5% |
% | ASTM D471 | |
23℃,168 hr,in Ethanol,95% 23℃,168 hr,in Ethanol,95% |
% | ASTM D471 | |
23℃,168 hr,in Hydrochloric Acid,10% 23℃,168 hr,in Hydrochloric Acid,10% |
% | ASTM D471 | |
23℃,168 hr,in Isopropyl Alcohol 23℃,168 hr,in Isopropyl Alcohol |
% | ASTM D471 | |
23℃,168 hr,in Methylethylketone 23℃,168 hr,in Methylethylketone |
% | ASTM D471 | |
23℃,168 hr,in Sodium Chloride,15% 23℃,168 hr,in Sodium Chloride,15% |
% | ASTM D471 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ASTM D471 | |
23℃,168 hr,in Sulfuric Acid,98% 23℃,168 hr,in Sulfuric Acid,98% |
% | ASTM D471 | |
23℃,168 hr,in Trichloroethylene 23℃,168 hr,in Trichloroethylene |
% | ASTM D471 | |
100℃,168 hr,in Deionized Water 100℃,168 hr,in Deionized Water |
% | ASTM D471 | |
100℃,168 hr,in IRM 903 Oil 100℃,168 hr,in IRM 903 Oil |
% | ASTM D471 | |
125℃,70 hr,in IRM 903 Oil 125℃,70 hr,in IRM 903 Oil |
% | ASTM D471 | |
125℃,168 hr,in IRM 903 Oil 125℃,168 hr,in IRM 903 Oil |
% | ASTM D471 | |
断裂时拉伸应力变化 Changes in tensile stress during fracture |
ISO 1817 | ||
23℃,168 hr,in Cyclohexane 23℃,168 hr,in Cyclohexane |
% | ISO 1817 | |
23℃,168 hr,in Detergent(Tide),2.5% 23℃,168 hr,in Detergent(Tide),2.5% |
% | ISO 1817 | |
23℃,168 hr,in Ethanol,95% 23℃,168 hr,in Ethanol,95% |
% | ISO 1817 | |
23℃,168 hr,in Hydrochloric Acid,10% 23℃,168 hr,in Hydrochloric Acid,10% |
% | ISO 1817 | |
23℃,168 hr,in Isopropyl Alcohol 23℃,168 hr,in Isopropyl Alcohol |
% | ISO 1817 | |
23℃,168 hr,in Methylethylketone 23℃,168 hr,in Methylethylketone |
% | ISO 1817 | |
23℃,168 hr,in Sodium Chloride,15% 23℃,168 hr,in Sodium Chloride,15% |
% | ISO 1817 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ISO 1817 | |
23℃,168 hr,in Sulfuric Acid,98% 23℃,168 hr,in Sulfuric Acid,98% |
% | ISO 1817 | |
23℃,168 hr,in Trichloroethylene 23℃,168 hr,in Trichloroethylene |
% | ISO 1817 | |
100℃,168 hr,in Deionized Water 100℃,168 hr,in Deionized Water |
% | ISO 1817 | |
100℃,168 hr,in IRM 903 Oil 100℃,168 hr,in IRM 903 Oil |
% | ISO 1817 | |
125℃,70 hr,in IRM 903 Oil 125℃,70 hr,in IRM 903 Oil |
% | ISO 1817 | |
125℃,168 hr,in IRM 903 Oil 125℃,168 hr,in IRM 903 Oil |
% | ISO 1817 | |
邵氏硬度的变化率 The rate of change in Shore hardness |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在乙酸中 Shore A, 23 ℃, 168 hr, in acetic acid |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在环己烷中 Shore A, 23 ℃, 168 hr, in cyclohexane |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在洗涤剂(汰渍)中,2.5% Shaw A, 23 ℃, 168 hr, in detergent (Tide), 2.5% |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在乙醇中,95% Shore A, 23 ℃, 168 hr, in ethanol, 95% |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在盐酸中,10% Shore A, 23 ℃, 168 hr, in hydrochloric acid, 10% |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在异丙醇中 Shore A, 23 ℃, 168 hr, in isopropanol |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在甲基乙基酮中 Shore A, 23 ℃, 168 hr, in methyl ethyl ketone |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在氯化钠中,15% Shore A, 23 ℃, 168 hr, in sodium chloride, 15% |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在氢氧化钠中,50% Shore A, 23 ℃, 168 hr, in sodium hydroxide, 50% |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在硫酸中,98% Shore A, 23 ℃, 168 hr, in sulfuric acid, 98% |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在三氯乙烯中 Shore A, 23 ℃, 168 hr, in trichloroethylene |
ASTM D471 | ||
邵氏 A,100℃,168 hr,在去离子水中 Shore A, 100 ℃, 168 hr, in deionized water |
ASTM D471 | ||
邵氏 A,100℃,168 hr,在IRM 903油中 Shaw A, 100 ℃, 168 hr, in IRM 903 oil |
ASTM D471 | ||
邵氏 A,125℃,168 hr,在IRM 903油中 Shaw A, 125 ℃, 168 hr, in IRM 903 oil |
ASTM D471 | ||
邵氏硬度的变化率 The rate of change in Shore hardness |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在乙酸中 Shore A, 23 ℃, 168 hr, in acetic acid |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在环己烷中 Shore A, 23 ℃, 168 hr, in cyclohexane |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在洗涤剂(汰渍)中,2.5% Shaw A, 23 ℃, 168 hr, in detergent (Tide), 2.5% |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在乙醇中,95% Shore A, 23 ℃, 168 hr, in ethanol, 95% |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在盐酸中,10% Shore A, 23 ℃, 168 hr, in hydrochloric acid, 10% |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在异丙醇中 Shore A, 23 ℃, 168 hr, in isopropanol |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在甲基乙基酮中 Shore A, 23 ℃, 168 hr, in methyl ethyl ketone |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在氯化钠中,15% Shore A, 23 ℃, 168 hr, in sodium chloride, 15% |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在氢氧化钠中,50% Shore A, 23 ℃, 168 hr, in sodium hydroxide, 50% |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在硫酸中,98% Shore A, 23 ℃, 168 hr, in sulfuric acid, 98% |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在三氯乙烯中 Shore A, 23 ℃, 168 hr, in trichloroethylene |
ISO 1817 | ||
邵氏 A,100℃,168 hr,在去离子水中 Shore A, 100 ℃, 168 hr, in deionized water |
ISO 1817 | ||
邵氏 A,100℃,168 hr,在IRM 903油中 Shaw A, 100 ℃, 168 hr, in IRM 903 oil |
ISO 1817 | ||
邵氏 A,125℃,168 hr,在IRM 903油中 Shaw A, 125 ℃, 168 hr, in IRM 903 oil |
ISO 1817 | ||
质量变化率 Quality change rate |
ASTM D471 | ||
23℃,168 hr,in Acetic Acid 23℃,168 hr,in Acetic Acid |
% | ASTM D471 | |
23℃,168 hr,in Cyclohexane 23℃,168 hr,in Cyclohexane |
% | ASTM D471 | |
23℃,168 hr,in Ethanol,95% 23℃,168 hr,in Ethanol,95% |
% | ASTM D471 | |
23℃,168 hr,in Hydrochloric Acid,10% 23℃,168 hr,in Hydrochloric Acid,10% |
% | ASTM D471 | |
23℃,168 hr,in Isopropyl Alcohol 23℃,168 hr,in Isopropyl Alcohol |
% | ASTM D471 | |
23℃,168 hr,in Methylethylketone 23℃,168 hr,in Methylethylketone |
% | ASTM D471 | |
23℃,168 hr,in Sodium Chloride,15% 23℃,168 hr,in Sodium Chloride,15% |
% | ASTM D471 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ASTM D471 | |
23℃,168 hr,in Sulfuric Acid,98% 23℃,168 hr,in Sulfuric Acid,98% |
% | ASTM D471 | |
23℃,168 hr,in Trichloroethylene 23℃,168 hr,in Trichloroethylene |
% | ASTM D471 | |
100℃,168 hr,in Deionized Water 100℃,168 hr,in Deionized Water |
% | ASTM D471 | |
100℃,168 hr,in IRM 903 Oil 100℃,168 hr,in IRM 903 Oil |
% | ASTM D471 | |
125℃,168 hr,in IRM 903 Oil 125℃,168 hr,in IRM 903 Oil |
% | ASTM D471 | |
质量变化率 Quality change rate |
ISO 1817 | ||
23.0℃,168 hr,in Methylethylketone 23.0℃,168 hr,in Methylethylketone |
% | ISO 1817 | |
23.0℃,168 hr,in Isopropyl Alcohol 23.0℃,168 hr,in Isopropyl Alcohol |
% | ISO 1817 | |
23.0℃,168 hr,in Cyclohexane 23.0℃,168 hr,in Cyclohexane |
% | ISO 1817 | |
23.0℃,168 hr,in Trichloroethylene 23.0℃,168 hr,in Trichloroethylene |
% | ISO 1817 | |
23.0℃,168 hr,in Ethanol,95% 23.0℃,168 hr,in Ethanol,95% |
% | ISO 1817 | |
23.0℃,168 hr,in Sodium Hydroxide,50% 23.0℃,168 hr,in Sodium Hydroxide,50% |
% | ISO 1817 | |
23.0℃,168 hr,in Sodium Chloride,15% 23.0℃,168 hr,in Sodium Chloride,15% |
% | ISO 1817 | |
23.0℃,168 hr,in Hydrochloric Acid,10% 23.0℃,168 hr,in Hydrochloric Acid,10% |
% | ISO 1817 | |
23.0℃,168 hr,in Sulfuric Acid,98% 23.0℃,168 hr,in Sulfuric Acid,98% |
% | ISO 1817 | |
23.0℃,168 hr,in Acetic Acid 23.0℃,168 hr,in Acetic Acid |
% | ISO 1817 | |
100℃,168 hr,in Deionized Water 100℃,168 hr,in Deionized Water |
% | ISO 1817 | |
100℃,168 hr,in IRM 903 Oil 100℃,168 hr,in IRM 903 Oil |
% | ISO 1817 | |
125℃,168 hr,in IRM 903 Oil 125℃,168 hr,in IRM 903 Oil |
% | ISO 1817 | |
体积变化 Volume change |
|||
125℃,70 hr,在IRM 903油中 125 ℃, 70 hr, in IRM 903 oil |
% | ASTM D471 | |
125℃,70 hr,在IRM 903油中 125 ℃, 70 hr, in IRM 903 oil |
% | ISO 1817 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电强度 Dielectric strength |
|||
23 ℃,2 mm 23 ℃,2 mm |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
23 ℃,1.98 mm 23 ℃,1.98 mm |
ASTM D150 | ||
23 ℃,1.98 mm 23 ℃,1.98 mm |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
高压电弧抗点燃指数(HVAR)(PLC) High voltage arc ignition resistance index (HVAR) (PLC) |
UL 746 | ||
高电压电弧起痕速率 High voltage arc marking rate |
|||
HVTR HVTR |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
1.0 mm 1.0 mm |
UL 746 | ||
1.5 mm 1.5 mm |
UL 746 | ||
3.0 mm 3.0 mm |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.00 mm 1.00 mm |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
3 B 方法,直角形试样(割口) |
4 类型 1 |
5 类型 A |
【新闻资讯】查看全部
我国废塑料加工行业已堕入困境?
2015-11-25 近年来,塑料加工行业迅速发展,塑料制品已经深入到社会的每个角落,极大的方便了人们的生活。但是同时废塑料造成的“白色污染”问题也日渐突出,对环境造成了严重的污染与破坏。而废塑料的回收是解决该问题最有效的方法,不仅可以减少环境污染、而且可以变废为宝,实现资源高效和循环利用。而目前,是否已经研制出多种废塑料回收技术? 目前,我国废塑料回收行业陷入窘境,在技术上废塑料再生企业技术设备,工艺水平都比较低下,严重阻碍了该行业的快速发展。废旧网小编认为,科技是第一生产力,想要与时俱进,不 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |